Collimated Sputtering of Titanium and Titanium Nitride Films

Published online by Cambridge University Press:  29 November 2013

James G. Ryan ,
Stephen B. Brodsky ,
Tomio Katata ,
Makoto Honda ,
Naohiro Shoda  and
Hideaki Aochi
Get access

Extract

Collimated sputtering is a physical vapor deposition (PVD) method where a collimator is inserted between a conventional “full-face-erosion” sputtering target and a substrate (Figure 1). The collimator is a plate of hexagonal cells that acts as a filter to remove obliquely incident atoms before they arrive at the substrate. Only material with a nearly normal incidence trajectory may pass through the collimator and deposit on the substrate. Collimated sputtering was initially evaluated for conductor-level depositions in order to improve the filling of recessed features. Although the method has been successfully used to fill damascene structures, depositing thick conductor films is inefficient because most of the sputtered material is captured by the collimator, causing the collimator to clog quickly, necessitating frequent replacement.

A more common use of collimated sputtering is associated with the deposition of thin “liner” films. For example, thin, collimated aluminum alloy films have been used as underlayers for aluminum reflow processes. Also, collimated Ti/TiN films are used as contact/adhesion layers for chemically vapor-deposited (CVD) W metallization. Collimation provides better bottom and sidewall coverage for small, high aspect-ratio features than conventionally sputtered films do.

Coliimated sputtered films often exhibit unique properties because the angle of incidence of depositing atoms is controlled. Collimated AlMg alloys have superior electromigration resistance compared to noncollimated AlMg films. Collimated TiN films appear to exhibit denser grain structures when compared to films deposited with higher amounts of obliquely incident flux (Figure 2).

Type
Metallization for Integrated Circuit Manufacturing
Information
MRS Bulletin , Volume 20 , Issue 11 , November 1995 , pp. 42 - 45
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Sakata, M., Shimamura, H., Kobayashi, S., Kawahito, T., Kamei, T., and Abe, K., U.S. Patent 4,724,060.Google Scholar
2.Rossnagel, S.M., Mikalsen, D., Kinoshita, H., Cuomo, J.J., J. Vac. Sci. Technol. A 9 (2) (1991) p. 261.CrossRefGoogle Scholar
3.Vollmer, B., Licata, T., Restaino, D., and Ryan, J.G., Thin Solid Films 247 (1994) p. 104.CrossRefGoogle Scholar
4.Roehl, S., Camilletti, L., Cote, W., Cote, D., Eckstein, E., Froehner, K.H., Lee, P.I., Restaino, D., Roeska, G., Vynorius, V., Wolff, S., and Vollmer, B., in Proc. 9th Int. VLSI Multilevel Interconnection Conf., edited by Wade, T.E. (VMIC, Tampa, 1992) p. 22.Google Scholar
5.Joshi, R.V., Cuomo, J.J., Dalal, H.M., and Hsu, L.L., U.S. Patent 5,300,813.Google Scholar
6.Kaanta, C.W., Bombardier, S.G., Cote, W.J., Hill, W.R., Kerszykowski, G., Lands, H.S., Poindexter, D.J., Pollard, C.W., Ross, G.H., Ryan, J.G., Wolff, S., and Cronin, J.E., in Proc. 8th Int. VLSI Multilevel Interconnection Conference, edited by Wade, T.E. (IEEE, Piscataway, 1991) p. 144.Google Scholar
7.Licata, T., Okazaki, M., Ronay, M., Nguyen, S., Aochi, H., Landers, W., Filippi, R., Restaino, D., Knorr, D., and Ryan, J.G., in Proc. 12th Int. VLSI Multilevel Interconnection Conference, edited by Wade, T.E. (VMIC, Tampa, 1995) p. 596.Google Scholar
8.Biberger, M., Rumer, M., Tkach, G., and Ouellet, L., in Proc. Mater. Soc. (Chicago, 1994) p. 379.Google Scholar
9.Joshi, R.V. and Brodsky, S., in Proc. 9th VLSI Multilevel Interconnection Conf., edited by Wade, T.E. (VMIC, Tampa, 1992) p. 310.Google Scholar
10.Oshaki, A., Maekawa, K., Fujisawa, M., Yamaguchi, S., Itoh, Y., Fujinaga, M., and Kotani, H., in Proc. 2nd Int. Symposium on ISSP (Tokyo, 1993).Google Scholar
11.Licata, T.J., Sullivan, T.D., Bass, R.S., Ryan, J.G., and Knorr, D.B., in Materials Reliability in Microelectronics III, edited by Rodbell, K., Filter, B., Frost, H., and Ho, P. (Mater. Res. Soc. Symp. Proc. 309, Pittsburgh, 1993) p. 87.Google Scholar
12.Strippe, D., Licata, T., Bass, R., and Ryan, J. G., presented at the 1991 International Conference on Metallurgical Coatings and Thin Films, San Diego, 1991 (unpublished).Google Scholar
13.Licata, T., Strippe, D., McDevitt, T., Lasky, Jerome B. and Ryan, J.G., presented at the 39th National AVS Symposium and Topical Conferences, Seattle, 1992 (unpublished).Google Scholar
14.Bronner, G., Aochi, H., Gall, M., Gambino, J., Gernhardt, S., Hammerl, E., Ho, H., Iba, J., Ishiuchi, H., Jaso, M., Kleinhenz, R., Mii, T., Narita, M., Nesbit, L., Neumueller, W., Nitayama, A., Ohiwa, T., Parke, S., Ryan, J., Sato, T., Takato, H., and Yoshikawa, S., in 1995 Symposium on VLSI Technology Digest of Technical Papers (The Japan Society of Applied Physics and The IEEE Electron Devices Society, Kyoto, 1995) p. 15.CrossRefGoogle Scholar