Boundary Lubrication of Materials

Published online by Cambridge University Press:  29 November 2013

Stephen M. Hsu
Get access

Extract

Lubrication may be defined as any method used to achieve control of friction and wear of interacting surfaces in relative motion under load. Gases, liquids, and solids have been used successfully as lubricants. To prevent surface contact, liquids and gases provide a film under hydrodynamic pressure to support the load.

When the load is high and/or the speed is low, the hydrodynamic or hydrostatic pressure may not be sufficient and the surfaces come into close contact. The amount and the extent of the surface contact depends on many factors: surface roughness, fluid film pressure, normal load, hardness of the materials, etc. When the surfaces come into close contact, many of the asperities undergo elastic deformation. The condition is generally referred to as elasto-hydrodynamic lubrication (EHL). EHL theories are well-developed. They describe and predict the surface temperatures, fluid film thickness, and hydrodynamic pressures. Contact pressure increases beyond the EHL conditions causes asperities to deform plastically and thinning of the fluid film. When the average fluid film thickness falls below the average surface roughness, the interaction between the contacting surfaces becomes the dominant factor in supporting the load.

This condition is referred to as the boundary lubrication (BL) regime. Theories for BL are not well-developed and the detailed processes are not understood. The classical view of boundary lubrication postulates the formation of a surface chemical film which is easily sheared and protects the surface.

Type
Materials Tribology
Information
MRS Bulletin , Volume 16 , Issue 10 , October 1991 , pp. 54 - 58
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Rowe, C.N., ASLE Trans. 9 (1966) p. 110.CrossRefGoogle Scholar
2.Rowe, C.N., ASLE Trans. 13 (1970) p. 179.CrossRefGoogle Scholar
3.Groszek, A.J., ASLE Trans. 5 (1962) p. 105.CrossRefGoogle Scholar
4.Klaus, E.E. and Bieber, H.E., ASLE Trans. 8 (1965) p. 12.CrossRefGoogle Scholar
5.Hsu, S.M. and Klaus, E.E., ASLE Trans. 22 (1979) p. 135.CrossRefGoogle Scholar
6.Hsu, S.M., Klaus, E.E., and Cheng, H.S., Wear 128 (1988) p. 307.CrossRefGoogle Scholar
7.Furey, M.J., ASLE Trans. 7 (1964) p. 133.CrossRefGoogle Scholar
8.Hsu, S.M. and Klaus, E.E., ASLE Trans. 21 (3) (1978) p. 201.CrossRefGoogle Scholar
9.Gates, R.S., Jewett, K.L. and Hsu, S.M., Tribology Trans. 32 (4) (1989) p. 423.CrossRefGoogle Scholar
10.Godfrey, D., ASLE Trans. 8 (1965) p. 1.CrossRefGoogle Scholar
11.Gates, R.S. and Hsu, S.M., Tribology Trans. 34 (3) (1991) p. 417.CrossRefGoogle Scholar
12.Hsu, S.M., in Engineered Materials for Advanced Friction and Wear Applications, edited by Smidt, F.A. and Blau, P.J. (ASM International, Metals Park, Ohio, 1988) p. 135.Google Scholar
13.Klaus, E.E., et al., DOE Conf. 870762, 1987, p. 65.Google Scholar
14.Klaus, E.E., Phillips, J., Lin, S.C., Wu, N.L. and Duda, J.L., Tribology Trans. 33 (1) (1990) p. 25.CrossRefGoogle Scholar