Strength and ductility performance of corroded steel bars in concrete exposed to 2D chloride ingress

Published online by Cambridge University Press:  11 August 2020

Mike Otieno Open the ORCID record for Mike Otieno [Opens in a new window]  and
Ze Zakka
Mike Otieno*
Affiliation:
School of Civil and Environmental Engineering, University of the Witwatersrand, Johannesburg
Ze Zakka
Affiliation:
School of Civil and Environmental Engineering, University of the Witwatersrand, Johannesburg
*
Corresponding author: Mike Otieno ([email protected])
Get access

Abstract

This paper presents the residual tensile strength test results of corroded high yield steel bars. Single steel bars were embedded at a cover depth of 20 mm in 150 × 150 × 625 mm long cracked concrete beam specimens made with 70/30 PC/FA and 50/50 PC/SL binders with a constant w/b ratio of 0.40. The steel bars were placed in the cross-section centre and near the orthogonal edge of the beams, and selected beam faces epoxy-coated in order to simulate, respectively, 1D and 2D chloride ingress. The beams were subjected to 2-week wetting (with 5% NaCl) and 2-week air-drying cycles in the laboratory for 110 weeks after which the corroded steel bars were extracted, assessed for corrosion morphology, and tested in tension for ultimate strength, fracture strength and ductility performance. The steel bars in concretes exposed to 1D chloride ingress had isolated corrosion pits while both general and isolated corrosion pits were observed in specimens exposed to 2D chloride ingress. The residual ultimate and fracture tensile strengths, and ductility of corroded steel reinforcing bars in concretes exposed to 2D chloride ingress are lower than those for steel bars in concretes exposed to 1D chloride ingress.

Type
Articles
Information
MRS Advances , Volume 5 , Issue 54-55: Nanoscale and Quantum Materials , 2020 , pp. 2817 - 2825
Check for updates
Copyright
Copyright © Materials Research Society 2020

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Andrade, C. & Alonso, C. (2001) On-site measurements of corrosion rate of reinforcements. Construction and Building Materials, Vol. 15(2-3), pp. 141-145.Google Scholar
Yoon, S., Wang, K., Weiss, W. J. & Shah, S. P. (2000) Interaction between loading, corrosion, and serviceability of reinforced concrete ACI Materials Journal, Vol. 97(6), pp. 637-644.Google Scholar
Ortega, N. F. & Robles, S. I. (2016) Assessment of residual life of concrete structures affected by reinforcement corrosion. HBRC Journal, Vol. 12(2), pp. 114-122.Google Scholar
Cao, C. & Cheung, M. M. S. (2014) Non-uniform rust expansion for chloride-induced pitting corrosion in RC structures. Construction and Building Materials, Vol. 51, pp. 75-81.CrossRefGoogle Scholar
Tan, R., Hendriks, M. A. N. & Kanstad, T. (2017) Evaluation of current crack width calculation methods according to Eurocode 2 and fib Model Code 2010. Proceedings of the fib Symposium: High-Tech Concrete: where Technology and Engineering Meet, 29-30 August, 2017, Oslo, Norway, pp. 1610-1618.Google Scholar
Kang, B. & Shim, H. (2011) Two dimensional chloride ion diffusion in reinforced concrete structures for railway. International Journal of Railway, Vol. 4(4), pp. 86-92.Google Scholar
Zhang, Y., Sun, W., Chen, S. & Guo, F. (2011) Two- and three-dimensional chloride ingress into fly ash concrete. Journal of Wuhan University of Technology - Materials Science Edition, Vol. 26(5), pp. 978-982.CrossRefGoogle Scholar
Zhang, Y., Sun, W., Liu, Z. & Chen, S. (2011) One and two dimensional chloride ion diffusion of fly ash concrete under flexural stress. Journal of Zhejiang University - SCIENCE A, Vol. 12(9), pp. 692-701.CrossRefGoogle Scholar
Bijen, J. (1996) Benefits of slag and fly ash. Construction and Building Materials, Vol. 10(5), pp. 309-314.Google Scholar
SANS-920 (2011) Steel bars for concrete reinforcement (Edition 2.3). South African Standard Code of practice, ISBN 978-0-626-25730-9.Google Scholar
Malumbela, G. (2010) Measurable parameters for performance of corroded and repaired RC beams under load. PhD Thesis, Department of civil engineering, University of Cape Town.Google Scholar
Otieno, M., Beushausen, H. & Alexander, M. (2016) Chloride-induced corrosion of steel in cracked concrete – Part I: Experimental studies under accelerated and natural marine environments. Cement and Concrete Research, Vol. 79, pp. 373-385.CrossRefGoogle Scholar
Otieno, M., Golden, G., Beushausen, H. & Alexander, M. G. (2019) Acceleration of steel corrosion in concrete by cyclic wetting and drying: effect of drying duration and concrete quality. Materials and Structures, Vol. 52(2), pp. 1-14.CrossRefGoogle Scholar
Scott, A. N. & Alexander, M. G. (2007) The influence of binder type, cracking and cover on corrosion rates of steel in chloride-contaminated concrete. Magazine of Concrete Research, Vol. 59(7), pp. 495-505.Google Scholar
SANS-6892-1 (2010) Metallic materials - tensile testing, Part 1: Method of test at room temperature. South African Standard Code of practice, ISBN 978-0-626-33263-1.Google Scholar
Val, D. V. & Trapper, P.A. (2006) Probabilistic evaluation of time to corrosion initiation in RC elements exposed to chlorides: 2-D modelling. Proceedings of the 3rd International Conference on Bridge Maintenance, Safety and Management - Bridge Maintenance, Safety, Management, Life-Cycle Performance and Cost, 16-19 July, 2006, Porto, Portugal, pp. 527-528.CrossRefGoogle Scholar
Val, D. V. & Trapper, P. A. (2008) Probabilistic evaluation of initiation time of chloride-induced corrosion. Reliability Engineering and System Safety, Vol. 93(3), pp. 364-372.CrossRefGoogle Scholar