Interdigital Photodetector with stabilized α-phase CsPbI3 using polyethylene oxide

Published online by Cambridge University Press:  23 June 2020

Haider Salman ,
Amir Shariffar ,
Tanveer A. Siddique  and
M. O. Manasreh
Haider Salman
Affiliation:
Department of Electrical Engineering, University of Arkansas, Fayetteville, AR, 72701, USA
Amir Shariffar
Affiliation:
Department of Electrical Engineering, University of Arkansas, Fayetteville, AR, 72701, USA
Tanveer A. Siddique
Affiliation:
Department of Electrical Engineering, University of Arkansas, Fayetteville, AR, 72701, USA
M. O. Manasreh
Affiliation:
Department of Electrical Engineering, University of Arkansas, Fayetteville, AR, 72701, USA
Get access

Abstract

Inorganic perovskite photodetector with chromium interdigitated electrodes is investigated. The active material is a solution processed CsPbI3 synthesized by one step deposition. The α-phase of this material is unstable at room temperature and it converts to the δ-phase at temperatures below 320°C. The stabilization of the α-phase was conducted in nitrogen environment by adding 5% weight ratio of polyethylene oxide to the equimolar mixture of PbI2 and CsI in dimethyl sulfoxide. The absorbance spectrum of the CsPbI3 with polyethylene oxide showed the emergence of a second peak at ∼ 690 nm related to the α-phase in addition to the peak at 420 nm of the δ phase. The peak in the visible range was also observed in the μ-photoluminescence spectrum at 690 nm. The interdigital structure was prepared by photolithography method to deposit 80 nm of chromium interdigitated electrodes on glass substrate with 10 μm channel width. The detector's on/off ratio and the detectivity were calculated from the current voltage curve under 100 mW/cm2 to be 9.64×103 and 9.2×109 Jones respectively.

Type
Articles
Information
MRS Advances , Volume 5 , Issue 50: Energy, Storage and Conversion , 2020 , pp. 2537 - 2543
Check for updates
Copyright
Copyright © Materials Research Society 2020

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Hsiao, Y. C., Wu, T., Li, M., Liu, Q., Qin, W., and Hu, B., J. Mater. Chem. A, 3, 15372 (2015)10.1039/C5TA01376CCrossRefGoogle Scholar
Wang, H., and Kim, D., Chem. Soc. Rev. 46, 5204 (2017)10.1039/C6CS00896HCrossRefGoogle Scholar
Li, Z., Yang, M., Park, J., Wei, S., Berry, J., and Zhu, K., Chem. Mater. 28, 284 (2016)10.1021/acs.chemmater.5b04107CrossRefGoogle Scholar
Pandey, N., Kumar, A., and Chakrabarti, S., RSC Adv. 9, 29556 (2019)10.1039/C9RA05685HCrossRefGoogle Scholar
Li, Z., Xu, J., Zhou, S., Zhang, B., Liu, X., Dai, S., and Yao, J., ACS Appl. Mater. Interfaces, 10, 38183 (2018)10.1021/acsami.8b11474CrossRefGoogle Scholar
Luo, P., Xia, W., Zhou, S., Sun, L., Cheng, J., Xu, C., and Lu, Y. J. Phys. Chem. Lett. 7, 3603 (2016)10.1021/acs.jpclett.6b01576CrossRefGoogle Scholar
Eperon, G., Paterno, G., Sutton, R., Zampetti, A., Haghighirad, A., Cacialli, F., and Snaith, H., J. Mater. Chem. A 3, 19688 (2015).10.1039/C5TA06398ACrossRefGoogle Scholar
Tai, Q., Tang, K., and Yan, Feng Energy Environ. Sci. 12 2375 (2019)10.1039/C9EE01479ACrossRefGoogle Scholar
Jeong, B., Han, H., Choi, Y., Cho, S., Kim, E., Lee, S., Kim, J., Park, C., Kim, D., and Park, C., Adv. Funct. Mater. 28, 1706401 (2018)10.1002/adfm.201706401CrossRefGoogle Scholar
Choi, H., Jeong, J., Kim, H., Kim, S., Walker, B., Kim, G., and Kim, J., Nano Energy, 7, 80 (2014)10.1016/j.nanoen.2014.04.017CrossRefGoogle Scholar