Hydrolytic Degradation of Actuators Based on Copolymer Networks From Oligo(ε-caprolactone) Dimethacrylate and n-Butyl Acrylate

Published online by Cambridge University Press:  08 April 2019

M. Balk ,
M. Behl  and
A. Lendlein
M. Balk
Affiliation:
Institute of Biomaterial Science, Helmholtz-Zentrum Geesthacht, Teltow, Germany
M. Behl
Affiliation:
Institute of Biomaterial Science, Helmholtz-Zentrum Geesthacht, Teltow, Germany
A. Lendlein*
Affiliation:
Institute of Biomaterial Science, Helmholtz-Zentrum Geesthacht, Teltow, Germany Institute of Chemistry, University of Potsdam, Potsdam, Germany
*
*Correspondence to: Prof. Andreas Lendlein Institute of Biomaterial Science, Helmholtz-Zentrum Geesthacht, Kantstr. 55, 14513, Teltow, Germany Email: [email protected] Phone: +49 (0)3328 352-235
Get access

Abstract

Shape-memory polymer actuators often contain crystallizable polyester segments. Here, the influence of accelerated hydrolytic degradation on the actuation performance in copolymer networks based on oligo(ε-caprolactone) dimethacrylate (OCL) and n-butyl acrylate is studied. The semi-crystalline OCL was utilized as crosslinker with molecular weights of 2.3 and 15.2 kg∙mol−1 (ratio: 1:1 wt%) and n-butyl acrylate (25 wt% relative to OCL content) acted as softening agent creating the polymer main chain segments within the network architecture. The copolymer networks were programmed by 50% elongation and were degraded by means of alkaline hydrolysis utilizing sodium hydroxide solution (pH = 13). Experiments were performed in the range of the broad melting range of the actuators at 40 °C. The degradation of test specimen was monitored by the sample mass, which was reduced by 25 wt% within 105 d. As degradation products, fragments of OCL with molecular masses ranging from 400 to 50.000 g·mol-1 could be detected by NMR spectroscopy and GPC measurements. The cleavage of ester groups included in OCL segments resulted in a decrease of the melting temperature (Tm) related to the actuator domains (amorphous at the temperature of degradation) and simultaneously, the Tm associated to the skeleton domain was increased (semi-crystalline at the temperature of degradation).

The alkaline hydrolysis decreased the polymer chain orientation of OCL domains until a random alignment of crystalline domains was obtained. This result was confirmed by cyclic thermomechanical actuation tests. The performance of directed movements decreased almost linearly as function of degradation time resulting in the loss of functionality when the orientation of polymer chains disappeared. Here, actuators were able to provide reversible movements until 91 d when the accelerated bulk degradation procedure using alkaline hydrolysis (pH = 13) was applied. Accordingly, a lifetime of more than one year can be guaranteed under physiological conditions (pH = 7.4) when, e.g., artificial muscles for biomimetic robots as potential application for these kind of shape-memory polymer actuators will be addressed.

Keywords

actuationshape memorycrystallization
Type
Articles
Information
MRS Advances , Volume 4 , Issue 21: Biomaterials and Soft Materials , 2019 , pp. 1193 - 1205
Copyright
Copyright © Materials Research Society 2019 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Majidi, C.: Soft Robotics: A Perspective—Current Trends and Prospects for the Future. Soft Robotics 1, 5 (2013).CrossRefGoogle Scholar
Miriyev, A., Stack, K.and Lipson, H.: Soft material for soft actuators. Nature Communications 8, 596 (2017).CrossRefGoogle ScholarPubMed
Hines, L., Petersen, K., Lum, G.Z.and Sitti, M.: Soft Actuators for Small-Scale Robotics. Advanced Materials 29, 1603483 (2017).CrossRefGoogle ScholarPubMed
Shintake, J., Cacucciolo, V., Floreano, D.and Shea, H.: Soft Robotic Grippers. Advanced Materials 30, 1707035 (2018).CrossRefGoogle Scholar
Ohm, C., Brehmer, M.and Zentel, R.: Liquid Crystalline Elastomers as Actuators and Sensors. Advanced Materials 22, 3366 (2010).CrossRefGoogle ScholarPubMed
Yuan, C., Roach, D.J., Dunn, C.K., Mu, Q., Kuang, X., Yakacki, C.M., Wang, T.J., Yu, K.and Qi, H.J.: 3D printed reversible shape changing soft actuators assisted by liquid crystal elastomers. Soft Matter 13, 5558 (2017).CrossRefGoogle ScholarPubMed
Pei, Z., Yang, Y., Chen, Q., Terentjev, E.M., Wei, Y.and Ji, Y.: Mouldable liquid-crystalline elastomer actuators with exchangeable covalent bonds. Nature Materials 13, 36 (2013).CrossRefGoogle ScholarPubMed
Lendlein, A.: Fabrication of reprogrammable shape-memory polymer actuators for robotics. Science Robotics 3 (2018).CrossRefGoogle Scholar
Behl, M., Kratz, K., Noechel, U., Sauter, T.and Lendlein, A.: Temperature-memory polymer actuators. Proceedings of the National Academy of Sciences 110, 12555 (2013).CrossRefGoogle ScholarPubMed
Farhan, M., Rudolph, T., Nöchel, U., Kratz, K.and Lendlein, A.: Extractable Free Polymer Chains Enhance Actuation Performance of Crystallizable Poly(ε-caprolactone) Networks and Enable Self-Healing. Polymers 10, 255 (2018).CrossRefGoogle ScholarPubMed
Yan, W., Rudolph, T., Noechel, U., Gould, O., Behl, M., Kratz, K.and Lendlein, A.: Reversible Actuation of Thermoplastic Multiblock Copolymers with Overlapping Thermal Transitions of Crystalline and Glassy Domains. Macromolecules 51, 4624 (2018).CrossRefGoogle Scholar
Biswas, A., Aswal, V.K., Sastry, P.U., Rana, D.and Maiti, P.: Reversible Bidirectional Shape Memory Effect in Polyurethanes through Molecular Flipping. Macromolecules 49, 4889 (2016).CrossRefGoogle Scholar
Behl, M., Kratz, K., Zotzmann, J., Nöchel, U.and Lendlein, A.: Reversible Bidirectional Shape-Memory Polymers. Advanced Materials 25, 4466 (2013).CrossRefGoogle ScholarPubMed
Ge, F., Lu, X., Xiang, J., Tong, X.and Zhao, Y.: An Optical Actuator Based on Gold-Nanoparticle-Containing Temperature-Memory Semicrystalline Polymers. Angewandte Chemie International Edition 56, 6126 (2017).CrossRefGoogle ScholarPubMed
Wang, L., Razzaq, M.Y., Rudolph, T., Heuchel, M., Nöchel, U., Mansfeld, U., Jiang, Y., Gould, O.E.C., Behl, M., Kratz, K.and Lendlein, A.: Reprogrammable, magnetically controlled polymeric nanocomposite actuators. Materials Horizons 5, 861 (2018).CrossRefGoogle Scholar
Saatchi, M., Behl, M., Nöchel, U.and Lendlein, A.: Copolymer Networks From Oligo(ε-caprolactone) and n-Butyl Acrylate Enable a Reversible Bidirectional Shape-Memory Effect at Human Body Temperature. Macromolecular Rapid Communications 36, 880 (2015).CrossRefGoogle ScholarPubMed
Kelch, S., Steuer, S., Schmidt, A.M.and Lendlein, A.: Shape-Memory Polymer Networks from Oligo[(ε-hydroxycaproate)-co-glycolate]dimethacrylates and Butyl Acrylate with Adjustable Hydrolytic Degradation Rate. Biomacromolecules 8, 1018 (2007).CrossRefGoogle ScholarPubMed
Kumar, U.N., Kratz, K., Wagermaier, W., Behl, M.and Lendlein, A.: Non-contact actuation of triple-shape effect in multiphase polymer network nanocomposites in alternating magnetic field. J. Mater. Chem. 20, 3404 (2010).CrossRefGoogle Scholar