Optimizing the manganese and silicon content for hot dipgalvanizing of 3rd generation advanced high strength steels⋆

Published online by Cambridge University Press:  14 February 2014

J. Staudte ,
J. M. Mataigne ,
F. Del Frate ,
D. Loison  and
S. Cremel
Get access

Abstract

The influence of variable Manganese content (2.4−4.6 wt%), while keeping constant Silicon(1.5 wt%) and Chromium (0.3 wt%) levels, and variable oxidation potential of the annealingatmosphere on hot dip galvanizability was investigated. Surface oxides prior to hot dipgalvanizing were analyzed and coating quality assessed. The increasing oxidation potentialof the annealing atmosphere led to a transition from external to internal selectiveoxidation of Mn, Si and Cr; their enrichment at the surface could be reduced and themetallic iron at the surface was increased. Hot dip galvanizability could thus be obtainedup to 2.9%Mn. With increasing Mn content, the surface was covered by a rising amount ofMn-oxides. By exceeding a critical amount of Manganese, reactivity in the Zinc bath wasdeteriorated. This amount was found to be between 2.9 and 3.8 wt% for Si content of 1.5wt%.

Keywords

AHSSManganese-Silicon ratiointernal and external selective oxidationincreased dew point annealing
Type
Research Article
Information
Metallurgical Research & Technology , Volume 111 , Issue 1 , 2014 , pp. 17 - 23
Copyright
© EDP Sciences 2014

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

P. Drillet, Z. Zermout, D. Bouleau, J.-M. Mataigne, S. Claessens, Selective Oxidation of high Si, Mn and Al steel grade during Recrystallization, Annealing, and Steel/Zn reactivity; Proceedings of 6th international conference on Zinc and Zinc alloy coated steel, GALVATECH’04, Chicago, 2004, pp. 1123-1134
Bellhouse, E.M., McDermid Selective, J.R., Metall. Mater. Trans. A 43 (2012) 2426-2441
Kim, M.S., Kwak, J.H., Kim, J.S., Liu, Y.H., Gao, N., Tang, N.-Y., Metall. Mater. Trans. A 40 (2009) 1903-1910
Gong, Y.F., Kim, H.S., De Cooman, B.C., ISIJ Int. 48 (2008) 1745-1751
Gong, Y.F., Kim, H.S., De Cooman, B.C., ISIJ Int. 49 (2009) 557-563
Huin, D., Flauder, P., Leblond, J.B., Oxid. Met. 64 (2005) 131-167
Suzuki, Y., Yamashita, T., Sugimoto, Y., Fujita, S., Yamaguchi, S., ISIJ Int. 49 (2009) 564-573
J. Staudte, J.-M. Mataigne, D. Loison, F. Del Frate, Galvanizability of high Mn grade versus mixed Mn-Al and Mn-Si grades, Proceedings of 8th international conference on Zinc and Zinc alloy coated steel, GALVATECH2011, Genova, 2011