Delamination of pipeline steels: determination of an anisotropic cleavage criterion

Published online by Cambridge University Press:  10 February 2014

F. Tankoua ,
J. Crepin ,
P. Thibaux ,
M. Arafin ,
S. Cooreman  and
A.F. Gourgues
F. Tankoua*
Affiliation:
MINES ParisTech, Centre des Matériaux, UMR CNRS 7633, BP 87, 91003 Evry Cedex, France
J. Crepin
Affiliation:
MINES ParisTech, Centre des Matériaux, UMR CNRS 7633, BP 87, 91003 Evry Cedex, France
P. Thibaux
Affiliation:
ArcelorMittal R&D Gent, Pres. J.F. Kennedylaan 3, 9060 Zelzate, Belgium
M. Arafin
Affiliation:
ArcelorMittal R&D Gent, Pres. J.F. Kennedylaan 3, 9060 Zelzate, Belgium
S. Cooreman
Affiliation:
ArcelorMittal R&D Gent, Pres. J.F. Kennedylaan 3, 9060 Zelzate, Belgium
A.F. Gourgues
Affiliation:
MINES ParisTech, Centre des Matériaux, UMR CNRS 7633, BP 87, 91003 Evry Cedex, France
*
a Corresponding author: [email protected]
Get access

Abstract

Cleavage fracture anisotropy has been studied on a ferrite-bainite low alloy pipeline steel plate. Mechanical tests have been performed on smooth and notched bars taken along the three principal directions of the plate at temperatures between 20 °C and −196 °C, and analyzed by finite element calculations with an anisotropic plasticity model. The fracture mode of specimens tested along the normal direction differs from that of specimens taken along the two other directions, together with a lower critical cleavage stress. This difference seems to be related to microtexture anisotropy and might explain the sensitivity of this steel to delamination at low temperatures.

Keywords

Delamination fractureanisotropycleavagemicrotexturepipeline steelsDélaminageanisotropieclivagemicrotexturegazoducs
Type
Research Article
Information
Mechanics & Industry , Volume 15 , Issue 1 , 2014 , pp. 45 - 50
Copyright
© AFM, EDP Sciences 2013

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Bramfitt, B.L., Marder, A.R., A study of the delamination behavior of a very low-carbon steel, Metall. Mater. Trans. A 8 (1977) 1263−1273 CrossRefGoogle Scholar
Shin, Y.S., Hong, S.M., Bae, J.H., et al., Separation phenomenon occurring during the Charpy impact test of API X80 pipeline steels, Metall. Mater. Trans. A 40 (2009) 2333−2349 CrossRefGoogle Scholar
Inoue, T., Yin, F., Kimura, Y., et al., Delamination effect on impact properties of ultrafine-grained low carbon steel processed by warm caliber rolling, Metall. Mater. Trans. A 41 (2010) 341−355 CrossRefGoogle Scholar
T. Hara, Y. Shinohara, Y. Terada, et al., DWTT properties for high strength line pipe steels, Proceedings of the Eighteenth International Offshore and Polar Engineering Conference, 2008
T. Hara, Y. Shinohara, H. Asahi, Y. Terada, Effects of microstructure and texture on DWTT properties for high strength line pipe steels, Proceeding of IPC, International Pipeline Conference, 2006
T. Fujishiro, T. Hara, Effects of separation on ductile crack propagation behavior during drop weight tear test, Proceedings of Twenty-first International Offshore and Polar Engineering Conference, 2011
Yang, Z., Guo, W.L., Huo, C.Y., Wang, Y., Fracture appearance evaluation of high performance pipeline steel DWTT specimen with delamination cracks, Key Eng. Mater. 324-325 (2006) 59−62 CrossRefGoogle Scholar
Joo, M.S., Suh, D.-W., Bae, J.H., Bhadeshia, H.K.D.H., Role of delamination and crystallography on anisotropy of Charpy toughness in API-X80 steel, Mater. Sci. Eng. A 546 (2012) 314−322 CrossRefGoogle Scholar
Yan, W., Sha, W., Zhu, L., Wang, W., Shan, Y.-Y., Yang, K., Delamination fracture related to tempering in a high-strength low-alloy steel, Metall. Mater. Transa. A 41 (2010) 159−171 CrossRefGoogle Scholar
Mirzaev, D.A., Yakovleva, I.L., Tereshchenko, N.A., et al., Structural aspect of delamination crack formation during the HTMT of steels with a ferritic structure, The Physics of Metals and Metallography 106 (2008) 186−194 CrossRefGoogle Scholar
Yang, Z., Huo, C., Guo, W., The Charpy notch impact test of X70 pipeline steel with delamination cracks, Key Eng. Mater. 297−300 (2005) 2391−2396 CrossRefGoogle Scholar
Kalyanam, S., Beaudoin, A.J., Dodds, R.H. Jr., Barlat, F., Delamination cracking in advanced aluminium-lithium alloys-Experimental and computational studies, Eng. Fract. Mech. 76 (2009) 2174−2191 CrossRefGoogle Scholar
Baldi, G., Buzzichelli, G., Critical stress for delamination fracture in HSLA steels, Metal Science 12 (1978) 459−472 CrossRefGoogle Scholar
F. Tankoua, ArcelorMittal internal Ph.D. progress report, 2013
A. Andrieu, Mechanisms and multi-scale modeling of brittle fracture modifications induced by the thermal ageing of a pressurised water reactor steel, Ph.D. dissertation, École des Mines de Paris, France, 2013
Bron, F., Besson, J., A yield function for anisotropic materials, application to aluminium alloys, Int. J. Plast. 20 (2004) 937−963CrossRefGoogle Scholar