Luminescence of Be-doped GaN layers grown by molecular beam epitaxy on Si (111).

Abstract

Low temperature photoluminescence spectra of Be-doped layers grown on Si (111) by molecular beam epitaxy have been analyzed. Emissions at 3.466 eV and 3.384 eV, and a broad band centered at 2.4-2.5 eV are observed. Their evolution with temperature and excitation power, and time resolved PL measurements ascribe an excitonic character for the luminescence at 3.466 eV, whereas the emission at 3.384 eV is associated with a donor-acceptor pair transition. This recombination involves residual donors and Be-related acceptors, which are located around 90meV above the valence band, confirming Be as the shallowest acceptor reported in GaN. The intensity of the band at 2.4-2.5 eV increases with the Be content. This emission involves a band of deep acceptors generated by Be complex defects, as suggested by the parameter g = 2.008 ± 0.003 obtained by photoluminescence-detected electron paramagnetic resonance.

This article was received on Friday, June 19, 1998 and accepted on Thursday, September 10, 1998.

1. Introduction

Controllable doping is a key issue for the fabrication of ultraviolet and blue emitters based on GaN alloys. Si and Ge have been successfully used for n-type doping [1]. P-type doping remains a challenge because of the high n-type residual background present in GaN, and the large ionization energy of acceptors (Mg, Zn, Cd) [2]. P-type GaN has been achieved by Mg doping of metalorganic chemical vapor deposition (MOCVD) [3] and molecular beam epitaxy (MBE) [4] layers. However, the large ionization energy of Mg (250 meV) [5] implies a low activation of the acceptor at room temperature. Hence, the search for shallower acceptors is still a matter of great importance.

Be should be a shallower acceptor in GaN than Mg [6] [7] due to its large electronegativity and the absence of d-electrons [8]. Theoretical calculations suggest that Be behaves as a rather shallow acceptor in GaN [9], with a thermal ionization energy of 60 meV [10]. Nevertheless, experimental evidences point to the introduction of deep levels by Be doping in GaN. Several authors have reported a Be-related deep emission detected by photoluminescence (PL) in Be-doped [11] [12] and Be-implanted GaN [5], probably associated with the formation of complex defects. Salvador et al. [13] observed a broad band centered at 390-420 nm, which is interpreted as a donor-acceptor emission involving Be acceptors, with an ionization energy of 250 meV.

In this work, the optical properties of GaN:Be layers will be analyzed in order to determine the shallow acceptor level and study the generation of deep levels.

2. Experimental

Be-doped wurtzite GaN layers were grown on Si (111) substrates by MBE in a MECA-2000 chamber [14]. Nitrogen was supplied by an Oxford Applied Research RF plasma source, and high-purity ( ≥ 7N) standard solid sources were used for Ga and Be. Samples consist of an AlN buffer layer (500 Å) and a 0.5-1 μm thick GaN:Be layer grown at 840 °C and 750 °C respectively. The Be doping level was controlled varying the Be cell temperature (T_Be) in the range of 700-910°C. Secondary ion mass spectroscopy (SIMS) measurements showed Be concentration increasing over two orders of magnitude in the T_Be range of 700 − 870°C (Figure 1). The scale of Be concentration is arbitrary, because no SIMS calibration was available for Be in GaN.

Figure 1. Arrhenius plot of the Be concentration measured by SIMS as a function of the Be cell temperature. The scale of Be concentration is arbitrary, because no SIMS calibration was available for Be in GaN.

PL experiments were carried out in a He closed-cycle cryostat at temperatures between 4 and 300 K. The 334 nm line of an Ar⁺ laser was used for continuous wave (cw) excitation. Sample luminescence was dispersed by a THR-1000 Jobin-Yvon monochromator and detected by a GaAs photomultiplier. Time resolved PL measurements were performed at 10 K using a frequency doubled Ti-Sapphire laser with 200 fs pulses (peak power ∼ 0.2 MW/cm² ) pumped by a mode-locked Ar⁺ laser, with a system time resolution of 100 ps.

PL detected electron paramagnetic resonance (PL-EPR) measurements were performed at 1.5 K, with a microwave frequency of 72 GHz (V-band), for higher resolution. The optical excitation was performed with a halogen lamp followed by a monochromator, and the magnetic resonance was measured as a change of the PL intensity detected by a photomultiplier, with amplitude modulation of the microwaves and lock-in techniques.

3. Results

A typical low temperature PL spectrum of a Be-doped GaN layer is shown in Figure 2. A narrow emission attributed to free excitons recombination is observed at 3.466 eV. In addition, new peaks at lower energies are present, related to transitions involving Be shallow acceptors [15], as described below. A broad band centered at 2.4-2.5 eV is also observed as previously reported [5] [11] [12], with its emission shape modulated by a Fabry-Perot interference pattern. The integrated PL intensity of the band increases with Be doping level, whereas this emission is not detected in undoped samples. Hence, a relationship between this band and deep levels generated by Be will be established.

Figure 2. Typical low temperature PL spectrum of a Be-doped GaN layer.

3.1 The 3.466 eV line

The peak at 3.466 eV (15 meV full width half maximum, FWHM) observed in all samples is attributed to free excitons recombination (FXA), as deduced from the temperature evolution (4-300 K) shown in Figure 3, and time resolved PL spectra shown below. The effect of lattice vibrations on bandgap energy of semiconductors has been studied by Fan [16], who propose the following temperature dependence:

(1)

where E(0), θ_E, and κ are respectively the transition energy at 0 K, the Einstein temperature and a constant. The values obtained for these parameters with the best fit are: E(0) = 3.4658 ± 0.0001 eV, 0.171 ± 0.007 eV and θ_E = 447 ± 9 K. Calle et al. observed the FXA recombination at 3.479 eV in relaxed samples grown on Si (111) [17]. However, in the samples analyzed in this work, the energy position of FXA is affected by biaxial tensile strain due to thermal expansion mismatch between GaN and Si [18]. From x-ray diffraction measurements performed in these layers, a lattice parameter c = 5.1844 Å has been obtained, in agreement with the results by Chichibu et al. [18].

Figure 3. Temperature evolution of the transition energy of the near bandgap emissions. The best fit to the FXA variation and the fitting parameters are shown.

3.2 The 3.384 eV band

At lower energies than the FXA, Be-doped samples present a new emission (30 meV, FWHM) centered at 3.384 ± 0.001 eV, together with other recombinations at 3.292 and 3.202 eV. The energy spacing between these emissions (92 meV) reveals that the lower energy transitions are respectively the first and second LO phonon replicas of the luminescence at 3.384 eV. This recombination and its LO phonon replicas have been also recently observed on GaN layers grown by MBE on sapphire substrates [15].

The variation of the energy position of the emissions with excitation power and temperature has been analyzed to identify the origin of the emission at 3.384 eV. Figure 4 shows the evolution of this transition with increasing temperature in the range 4-60 K. A blueshift of ∼ 4 meV is observed. This variation in the energy position corresponds to a rate of ~ k, the Boltzmann constant, consistent with that expected for a donor-acceptor pair recombination (DAP). This dependence with temperature is due to the enhancement of more closely spaced pairs by a higher thermal ionization rate for the donors [19]. The evolution of the energy of the transition at 3.292 eV with increasing temperature is parallel to that described for the DAP band (Figure 3), supporting the identification of this emission as a first order LO phonon replica (DAP-LO).

Figure 4. Variation of PL spectra with increasing temperature under P = 1mW.

The evolution of the transition at 3.384 eV with increasing excitation power is depicted in Figure 5. The emission shifts 15 meV to higher energies when increasing the incident excitation power for almost three orders of magnitude (0.02-10 mW), what is consistent with the saturation of distant pairs under increasing excitation expected for a DAP recombination. On the contrary, the emission at 3.466 eV does not shift with excitation power, confirming its excitonic origin (FXA), as previously established.

Figure 5. Evolution of PL spectra with increasing excitation power at T = 4K.

PL intensity decay measurements also support that the peak at 3.384 eV is a DAP transition. Figure 6 shows a comparison between the luminescence decays of the 3.466 eV emission (FXA) and that of the 3.384 eV peak (DAP). The excitonic emission shows a very fast and exponential decay, with a time constant limited by the system resolution (∼100 ps). Conversely, the decay of the DAP luminescence is slow and strongly non exponential, with a life time of 0.2 μs in the region between 200 ns and 500 ns.

Figure 6. Low temperature PL decays of FXA and DAP emissions.

Time resolved PL spectra are shown in Figure 7, recorded in several 10 ns periods from the beginning of the decay. The DAP emission and its first LO phonon replica shift to a lower energy (longer wavelength) with time. This red-shift is explained considering the exponential decrease of the transition probability with increasing distance between donor and acceptor. Thus, the recombination of close pairs (higher energy transitions) dominates the emission for short times (0-10 ns). On the contrary, the recombination of distant pairs (lower energy) becomes dominant at longer times (250-260 ns).

Figure 7. Time resolved PL spectra recorded in 10 ns periods between 0 and 260 ns at 10K.

All the above results are consistent with the identification of the peak at 3.384 eV with a DAP transition, with the acceptor probably related to substitutional Be. The energy of a DAP transition is given by:

(2)

The donor is likely the residual donor reported on our samples [17], with an ionization energy E_D = 35 meV. The bandgap energy is reduced to E_g ≈ 3.492 eV because of the biaxial tensile strain [18], as was established for the FXA recombination. The coulombic interaction energy can be estimated as E_coul ≈ 15 meV [19]. Hence, an ionization energy E_A ∼ 90 meV is derived for the Be-acceptor. This result is in agreement with recent theoretical calculations, predicting that Be is a shallow acceptor in GaN [9], with a thermal ionization energy of 60 meV [10], and it is very close to the 85 meV calculated by Pödör for the hydrogenic acceptor in GaN [7]. This conclusion is also supported by the recent work by Dewsnip et al. [15] where a DAP character related to substitutional Be is attributed to the 3.384 eV recombination, finding an optical ionization energy between 90-100 meV for the Be acceptor.

3.3 The 2.4-2.5 band

The low temperature spectrum of a Be-doped layer presents also a broad band centered at 2.4-2.5 eV (Figure 2). Figure 8 shows this emission for different samples with increasing T_Be, i.e., Be concentration. A clear relation between the intensity of this band and the Be concentration is observed, suggesting that this band is associated with complex defects involving Be.

Figure 8. Intensity variation of the 2.4-2.5 eV band at low temperature with increasing Be concentration.

Figure 9 shows the variation of the band position with excitation power. The center of the interferencial pattern envelope of the band shifts about 400 meV to higher energies when increasing the power three orders of magnitude (0.01-10 mW). This blue-shift is much higher than that corresponding to a DAP transition between discrete levels (see Figure 5 for 3.384 eV DAP). This fact points to a transition involving a broad band of deep levels related to Be.

Figure 9. Low temperature evolution of the 2.4-2.5 eV band with increasing excitation power.

The evolution of this luminescence with increasing temperature is shown in Figure 10. The center of the emission envelope is red-shifted ∼ 300 meV for a temperature range of 4-290 K. This shift to lower energies is higher than that observed in Figure 3 for the free exciton recombination, FXA. This behavior also suggests the presence of a band of deep states whose occupation level changes with temperature, rather than a single DAP recombination.

Figure 10. Evolution of the 2.4-2.5 eV band with temperature under P = 1mW.

Time resolved PL has also been performed in this spectral region at low temperature (10 K). The time evolution of the intensity at 2.25 eV is shown in Figure 11. The decay is extremely slow and clearly non exponential, with a lifetime of 10 μs for the range 4-10 μs. This result provides additional support for the interpretation of this broad band as produced by deep levels with different lifetimes, making the decay strongly non exponential.

Figure 11. Low temperature PL decay of the emission at 2.25 eV.

PL-EPR measurements have been carried out in order to obtain more information about the levels involved in this transition. The PL-EPR spectrum shown in Figure 12 was measured via the 2.4-2.5 band. In first order perturbation theory, the deviation of the g factor from the free electron value, g_e = 2.0023, is given by the expression:

(3)

where λ is the spin-orbit interaction constant, E is the energy of the perturbed state and E₀ is the energy of the fundamental state, without perturbation effects. A donor-like resonance with a half width ∼ 7 mT was observed at 2.637 T (Figure 12), with an anisotropic g factor, g_|| = 1.955 ± 0.001 and g_⊥ = 1.949 ± 0.001 (|| and ⊥ indicate magnetic field B being parallel or perpendicular to the c-axis of the layers respectively). These results are in agreement with those obtained for the residual donor in undoped MOVPE layers grown on sapphire [20] [21]. On the low field side of this resonance, there is another peak, with a half width ∼ 15 mT and g_|| = 1.956 ± 0.001 and g_⊥ = 1.957 ± 0.001 (inset in Figure 12), likely related to a second shallow donor also involved in the 2.4-2.5 eV luminescence. The resonance at lower magnetic field (2.57 T), with g = 2.008 ± 0.003, is assigned to an acceptor-like defect. This resonance does not present any anisotropy, as expected for a deep acceptor.

Figure 12. PL-EPR spectrum of a Be-doped GaN layer, measured via the 2.4-2.5 eV band. Inset : high resolution spectrum, showing shallow donors resonances.

All the experimental evidences described above suggest a model for the broad emission at 2.4-2.5 eV, that consists of a recombination between shallow residual donors, and a band of deep acceptors at 0.9−1 eV above the valence band.

4. Conclusions

PL spectra of Be-doped GaN samples are presented, and emissions at 3.466, 3.384 eV and a broad band at 2.4-2.5 eV have been studied. The transition at 3.466 eV is identified as a FXA recombination, as deduced from PL evolution with temperature and time resolved PL. The luminescence at 3.384 eV has been analyzed under cw excitation. PL measurements show blue-shifts with increasing temperature and excitation power. Time resolve PL experiments reveal a non exponential and slow decay, and a red-shift of the transition energy with time. These experimental evidences indicate a donor-acceptor origin, involving Be acceptors with an ionization energy as low as 90 meV. Hence, Be is confirmed as the shallowest acceptor reported in GaN. Finally, PL evolution with temperature, excitation power and time, together with PL-EPR measurements allow to associate the luminescence at 2.4-2.5 eV with a transition between shallow donors and a band of deep acceptors related to complex defects.