Tribological and corrosion properties of Al–12Si produced by selective laser melting

Published online by Cambridge University Press:  08 July 2014

K.G. Prashanth*
Affiliation:
IFW Dresden, Institut für Komplexe Materialien, Dresden D-01171, Germany
B. Debalina
Affiliation:
Department of Metallurgical and Materials Engineering, Indian Institute of Technology Madras, Chennai 600036, India
Z. Wang
Affiliation:
IFW Dresden, Institut für Komplexe Materialien, Dresden D-01171, Germany
P.F. Gostin
Affiliation:
IFW Dresden, Institut für Komplexe Materialien, Dresden D-01171, Germany
A. Gebert
Affiliation:
IFW Dresden, Institut für Komplexe Materialien, Dresden D-01171, Germany
M. Calin
Affiliation:
IFW Dresden, Institut für Komplexe Materialien, Dresden D-01171, Germany
U. Kühn
Affiliation:
IFW Dresden, Institut für Komplexe Materialien, Dresden D-01171, Germany
M. Kamaraj
Affiliation:
Department of Metallurgical and Materials Engineering, Indian Institute of Technology Madras, Chennai 600036, India
S. Scudino
Affiliation:
IFW Dresden, Institut für Komplexe Materialien, Dresden D-01171, Germany
J. Eckert
Affiliation:
IFW Dresden, Institut für Komplexe Materialien, Dresden D-01171, Germany; and TU Dresden, Institut für Werkstoffwissenschaft, Dresden D-01062, Germany
*
a)Address all correspondence to this author. e-mail: [email protected], [email protected]
Get access

Abstract

The effect of annealing on the tribological and corrosion properties of Al–12Si samples produced by selective laser melting (SLM) is evaluated via sliding and fretting wear tests and weight loss experiments and compared to the corresponding material processed by conventional casting. Sliding wear shows that the as-prepared SLM material has the least wear rate compared to the cast and heat-treated SLM samples with abrasive wear as the major wear mechanism along with oxidation. Similar trend has also been observed for the fretting wear experiments, where the as-prepared SLM sample displays the minimum wear loss. On the other hand, the acidic corrosion behavior of the as-prepared SLM material as well as of the cast samples is similar and the corrosion rate is accelerated by increasing the heat treatment temperature. This behavior is due to the microstructural changes induced by the heat treatment, where the continuous network of Si characterizing the as-prepared SLM sample transforms to isolated Si particles in the heat-treated SLM specimens. This shows that both the wear and corrosion behaviors are strongly associated with the change in microstructure of the SLM samples due to the heat-treatment process, where the size of the hard Si particles increases, and their density decreases with increasing annealing temperature.

Type
Articles
Copyright
Copyright © Materials Research Society 2014 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Davis, J.R.: Aluminum and Aluminum Alloys (ASM International, OH, 1993).Google Scholar
Srivastava, V.C., Mandal, R.K., and Ojha, S.N.: Microstructure and mechanical properties of Al–Si alloys produced by spray forming process. Mater. Sci. Eng., A 304306, 555 (2001).CrossRefGoogle Scholar
Zhou, J., Duszczyk, J., and Korevaar, B.M.: Microstructural features and final mechanical properties of the iron-modified Al-20Si-3Cu-1 Mg alloy product processed from atomized powder. J. Mater. Sci. 26, 3041 (1991).Google Scholar
Grosselle, F., Timelli, G., and Bonollo, F.: Doe applied to microstructural and mechanical properties of Al-Si-Cu-Mg casting alloys for automotive applications. Mater. Sci. Eng., A 527, 3536 (2010).Google Scholar
Kasprzak, W., Amirkhiz, B.S., and Niewczas, M.: Structure and properties of cast Al-Si based alloy with Zr-V-Ti additions and its evaluation of high temperature performance. J. Alloys Compd. 595, 67 (2014).Google Scholar
Middleton, C.J., Timmins, R., and Townsend, R.D.: The integrity of materials in high temperature components; performance and life assessment. Int. J. Pres. Ves. Pip. 66, 33 (1996).CrossRefGoogle Scholar
Krätschmer, D., Roos, E., Schuler, X., and Herter, K-H.: Proof of fatigue strength of nuclear components part II: Numerical fatigue analysis for transient stratification loading considering environmental effects. Int. J. Pres. Ves. Pip. 92, 1 (2012).Google Scholar
Ejiofor, J.U. and Reddy, R.G.: Developments in the processing and properties of particulate Al-Si composites. JOM 49, 31 (1997).Google Scholar
Chen, M., Meng-Burany, X., Perry, T.A., and Alpas, A.T.: Micromechanisms and mechanics of ultra-mild wear in Al-Si alloys. Acta Mater. 56, 5605 (2008).CrossRefGoogle Scholar
Khruschov, M.M.: Principles of abrasive wear. Wear 28, 69 (1974).Google Scholar
Jeong, D.H., Erb, U., Aust, K.T., and Palumbo, G.: The relationship between hardness and abrasive wear resistance of electrodeposited nanocrystalline Ni-P coatings. Scr. Mater. 48, 1067 (2003).CrossRefGoogle Scholar
Moore, M.A.: The relationship between the abrasive wear resistance, hardness and microstructure of ferritic materials. Wear 28, 59 (1974).Google Scholar
Jeong, D.H., Gonzalez, F., Palumbo, G., Aust, K.T., and Erb, U.: The effect of grain size on the wear properties of electrodeposited nanocrystalline nickel coatings. Scr. Mater. 44, 493 (2001).Google Scholar
Makarov, A.V., Pozdejeva, N.A., Savrai, R.A., Yurovskikh, A.S., and Malygina, I.Y.: Improvement of wear resistance of quenched structural steel by nanostructuring frictional treatment. J. Frict. Wear 33, 433 (2012).CrossRefGoogle Scholar
Clarke, J. and Sarkar, A.D.: Wear characteristics of as-cast binary aluminum silicon alloys. Wear 54, 7 (1979).Google Scholar
Pramila Bai, B.N. and Biswas, S.K.: Mechanism of wear in dry sliding of a hypoeutectic aluminum alloy. Lubr. Eng. 43, 57 (1987).Google Scholar
Mohammed Jasim, K. and Dwarakadasa, E.S.: Effect of sliding speed on adhesive wear of binary Al-Si alloys. J. Mater. Sci. Lett. 12, 650 (1993).Google Scholar
Elmadagli, M., Perry, T., and Alpas, A.T.: A parametric study of the relationship between microstructure and wear resistance of Al–Si alloys. Wear 262, 79 (2007).Google Scholar
Lashgari, H.R., Zangeneh, S., Shahmir, H., Saghafi, M., and Emamy, M.: Heat treatment effect on the microstructure, tensile properties and dry sliding wear behavior of A356–10%B4C cast composites. Mater. Des. 31, 4414 (2010).Google Scholar
Jia, K. and Fischer, T.E.: Sliding wear of conventional and nanostructured cemented carbides. Wear 203, 310 (1997).Google Scholar
Jin, H.W., Park, C.G., and Kim, M.C.: Microstructure and surface wear resistance in rapidly quenched Fe-Cr-B alloy spray coatings. Curr. Appl. Phys. 1, 473 (2001).CrossRefGoogle Scholar
Bourell, D., Wohlert, M., Harlan, N., Das, S., and Beaman, J.: Powder densification maps in selective laser sintering. Adv. Eng. Mater. 4, 663 (2002).Google Scholar
Li, J.P., Wilson, C., Wijn, J.R., Van Blitterswijk, C.A., and De Groot, K.: Fabrication of porous Ti6Al4V with designed structure by rapid prototyping technology. Key Eng. Mater. 330, 1293 (2007).Google Scholar
Pauly, S., Löber, L., Petters, R., Stoica, M., Scudino, S., Kühn, U., and Eckert, J.: Processing metallic glasses by selective laser melting. Mater. Today 16, 37 (2013).Google Scholar
Prashanth, K.G., Scudino, S., Klauss, H., Surreddi, K.B., Löber, L., Wang, Z., Chaubey, A.K., Kühn, U., and Eckert, J.: Microstructure and mechanical properties of Al-12Si produced by selective laser melting: Effect of hear treatment. Mater. Sci. Eng., A 590, 153 (2014).CrossRefGoogle Scholar
Ma, P., Prashanth, K.G., Scudino, S., Lia, Y.D., Wang, H., Zou, C., Wei, Z., and Eckert, J.: Influence of annealing on mechanical properties of Al-20Si processed by selective laser melting. Metals 4, 28 (2014).Google Scholar
Prashanth, K.G., Damodaram, R., Scudino, S., Wang, Z., Prasad Rao, K., and Eckert, J.: Friction welding of Al-12Si parts produced by selective laser melting. Mater. Des. 57, 632 (2014).Google Scholar
Musa, A.Y., Mohamad, A.B., Khadum, A.A.H., and Chee, E.P.: Galvanic corrosion of aluminum alloy (Al2024) and copper in 1.0 M nitric acid. Int. J. Electrochem. Sci. 6, 5052 (2011).CrossRefGoogle Scholar
Song, G-L. and Liu, M.: Corrosion and electrochemical evaluation of an Al-Si-Cu aluminum alloy in ethanol solutions. Corros. Sci. 72, 73 (2013).Google Scholar
Holroyd, N.J.H., Scamans, G.M., Newman, R.C., and Vasudevan, A.K.: Chapter 14 – Corrosion and stress corrosion of aluminum-lithium alloys. In Aluminum-Lithium Alloys: Processing, Properties and Applications; 2014; pp. 457500.Google Scholar
Kending, M., Jeaniaquet, S., Addison, R., and Waldrop, J.: Role of hexavalent chromium in the inhibition of corrosion of aluminum alloys. Surf. Coat. Technol. 140, 58 (2001).Google Scholar
Prashanth, K.G., Kumar, S., Scudino, S., Murty, B.S., and Eckert, J.: Fabrication and response of Al70Y16Ni10Co4 glass reinforced metal matrix composites. Mater. Manuf. Process. 26, 1242 (2011).CrossRefGoogle Scholar
Archard, J.F.: Contact and rubbing of flat surface. J. Appl. Phys. 24, 981 (1953).Google Scholar
Elleuch, K. and Fouvry, S.: Wear analysis of A357 aluminium alloy under fretting. Wear 253, 662 (2002).Google Scholar
Raghukiran, N. and Kumar, R.: Processing and dry sliding wear performance of spray deposited hyper-eutectic aluminum–silicon alloys. J. Mater. Process. Technol. 213, 401 (2013).CrossRefGoogle Scholar
Suh, N.P.: The delamination theory of wear. Wear 25, 111 (1973).Google Scholar
Dwivedi, D.K.: Adhesive wear behavior of cast aluminium–silicon alloys: Overview. Mater. Des. 31, 2517 (2010).Google Scholar
Liu, Y., Asthana, R., and Rohatgi, P.A.: Map for wear mechanisms in aluminium alloys. J. Mater. Sci. 26, 99 (1991).CrossRefGoogle Scholar
Subramanian, C.: Some considerations towards the design of a wear resistant aluminium alloy. Wear 155, 193 (1992).Google Scholar
Zhang, J. and Alpas, A.T.: Transition between mild and severe wear in aluminium alloys. Acta Mater. 45, 513 (1997).Google Scholar
Zhu, M.H. and Zhou, Z.R.: On the mechanisms of various fretting wear modes. Tribol. Int. 44, 1378 (2011).Google Scholar
Blanchard, P., Colombie, C., Pellerin, V., Fayeulle, S., and Vincent, L.: Material effects in fretting wear: Application to iron, titanium and aluminum alloys. Metall. Trans. A 22A, 1535 (1991).CrossRefGoogle Scholar
Goto, H. and Uchijo, K.: Fretting wear of Al–Si alloy matrix composites. Wear 256, 630 (2004).CrossRefGoogle Scholar
Yoon, Y., Etsion, I., and Talke, F.E.: The evolution of fretting wear in a micro-spherical contact. Wear 270, 567 (2011).CrossRefGoogle Scholar
Timmermans, G. and Froyen, L.: Fretting wear behaviour of hypereutectic P/M Al–Si in oil environment. Wear 230, 105 (1999).Google Scholar
Kumar, S., Chakraborty, M., Subramanya Sarma, V., and Murty, B.S.: Tensile and wear behaviour of in situ Al–7Si/TiB2 particulate composites. Wear 265, 134 (2008).Google Scholar
Mandal, A., Chakraborty, M., and Murty, B.S.: Effect of TiB2 particles on sliding wear behaviour of Al–4Cu alloy. Wear 262, 160 (2007).Google Scholar
Thakur, S.K. and Dhindaw, B.K.: The influence of interfacial characteristics between SiCp and Mg/Al metal matrix on wear, coefficient of friction and microhardness. Wear 247, 191 (2001).Google Scholar
Srivastava, V.C., Rudrakshi, G.B., Uhlenwinkel, V., and Ojha, S.N.: Wear characteristics of spray formed Al–alloys and their composites. J. Mater. Sci. 44, 2288 (2009).Google Scholar
Prasad, B.K., Venkateswarlu, K., Modi, O.P., Jha, A.K., Das, S., Dasgupta, R., and Yegneswaran, A.H.: Sliding wear behavior of some Al–Si alloys: Role of shape and size of Si particles and test conditions. Metall. Mater. Trans. A 29A, 2747 (1998).Google Scholar
Torabian, H., Pathak, J.P., and Tiwari, S.N.: Wear characteristics of Al–Si alloys. Wear 172, 49 (1994).Google Scholar
Pourbaix, M.: Atlas of Electrochemical Equilibria in Aqueous Solutions (Pergamon Press, Brussels, 1996).Google Scholar