Thermal treatment effects on hard and soft films measured by nanoindentation test

Published online by Cambridge University Press:  31 January 2011

F.C. Tai ,
S.C. Lee ,
C. Wei ,
P.J. Wei  and
J.F. Lin
F.C. Tai*
Affiliation:
Department of Materials Science and Engineering, National Tsing Hua University, Hsinchu 300, Taiwan
S.C. Lee
Affiliation:
Department of Materials Science and Engineering, National Cheng-Kung University, Tainan 701, Taiwan
C. Wei
Affiliation:
Department of Mechanical Engineering, Tatung University, Taipei 104, Taiwan
P.J. Wei
Affiliation:
Department of Mechanical Engineering, National Cheng-Kung University, Tainan 701, Taiwan
J.F. Lin
Affiliation:
Department of Mechanical Engineering, National Cheng-Kung University, Tainan 701, Taiwan
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Nanoindentation measurements using the Berkovich diamond tip with a load up to 700 and 210 mN were performed on 1-μm hydrogenated diamond-like carbon (DLCH) films and 6-μm polyimide (PI) films under different thermal treatment. The average nanohardness and elastic modulus from nanoindentation measurements are 25.13 and 192.18 GPa for as-deposited DLCH film and 22.93 and 174.22 GPa for as-annealed DLCH film, respectively. The ID/IG ratio of Raman spectra is 1.72 for as-deposited DLCH film and 2.04 for as-annealed DLCH film. The average nanohardness and elastic modulus from nanoindentation measurements are 0.37 and 5.58 GPa for 300 as-cured PI film and 0.42 and 5.19 GPa for 400 as-cured PI film, respectively. The relative cured rate is 92.1% for 300 as-cured PI film and 100% for 400 as-cured PI film. Both the nanohardness and elastic modulus derived from nanoindentation test results can correlate well with the trend of Raman spectra and FTIR spectra for hard DLCH film and soft PI film under different thermal treatment effects.

Keywords

NanoindentationPolymerRaman spectroscopy
Type
Articles
Information
Journal of Materials Research , Volume 24 , Issue 3 , March 2009 , pp. 1069 - 1074
Copyright
Copyright © Materials Research Society 2009

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Maier, G.: Low-dielectric constant polymers for microelectronics. Prog. Polym. Sci. 26, 3 (2001).CrossRefGoogle Scholar
2.Ferrari, A.C. and Robertson, J.: Interpretation of Raman spectra of disordered and amorphous carbon. Phys. Rev. B.: Condens. Matter 61, 14095 (2000).CrossRefGoogle Scholar
3.Pharr, G.M., Callahan, D.L., McAdams, S.D., Tsui, T.Y., Anders, S., Anders, A., Ager, J.W. III, Brown, I.G., Bhatia, C.S., Silva, S.R.P., and Robertson, J.: Hardness, elastic modulus, and structure of very hard carbon films produced by cathodic-arc deposition with substrate pulse biasing. Appl. Phys. Lett. 68, 779 (1996).CrossRefGoogle Scholar
4.Oliver, W.C. and Pharr, G.M.: An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564 (1992).CrossRefGoogle Scholar
5.Jian, S.R., Fang, T.H., and Chuu, D.S.: Nanoindentation investigation of amorphous hydrogenated carbon thin films deposited by ECR-MPCVD. J. Non-Cryst. Solids 333, 291 (2004).CrossRefGoogle Scholar
6.Ziebert, C., Rinke, M., Stuber, M., Ulrich, S., and Holleck, H.: Interfaces and temperature stability of stepwise graded DLC films studied by nanoindentation and Raman spectroscopy. Surf. Coat. Technol. 200, 1127 (2005).CrossRefGoogle Scholar
7.Amagai, M.: The effect of polyimide surface chemistry and morphology on critical stress intensity factor. Microelectron. Reliab. 40, 2077 (2000).CrossRefGoogle Scholar
8.Nishino, T., Kotera, M., Inayoshi, N., Miki, N., and Nakamae, K.: Residual stress and microstructures of aromatic polyimide with different imidization processes. polym. 41, 6913 (2000).CrossRefGoogle Scholar
9.Lee, S.C., Tai, F.C., Wei, C.H., and Yu, J.I.: ATR-FTIR and nanoindentation measurements of PMDA-ODA polyimide under different curing temperature. Mater. Trans. 48, 1554 (2007).CrossRefGoogle Scholar
10.Tai, F.C., Lee, S.C., and Wei, C.H.: Correlation between ID/IG ratio from visible Raman spectra and sp2/sp3 ratio from XPS spectra of annealed hydrogenated DLC film. Mater. Trans. 47, 1847 (2006).CrossRefGoogle Scholar
11.Chiu, M.C., Hsieh, W.P., Ho, W.Y., Wang, D.Y., and Shieu, F.S.: Thermal stability of Cr-doped diamond-like carbons synthesized by cathodic arc evaporation. Thin Solid Films 476, 258 (2005).CrossRefGoogle Scholar
12.Tallant, D.R., Parmeter, J.E., Siegal, M.P., and Simpson, R.L.: The thermal stability of diamond-like carbon. Diamond Relat. Mater. 4, 191 (1995).CrossRefGoogle Scholar
13.Ma, F., Chen, Q., Cai, X., Li, G., and Ma, H.: DLC film fabricated by a composite technique of unbalanced magnetron sputtering and PIII. Mater. Trans. 43, 1398 (2002).CrossRefGoogle Scholar
14.Sung, S.L., Guo, X.J., Huang, K.P., Chen, F.R., and Shih, H.C.: The strengthening mechanism of DLC film on silicon by MPECVD. Thin Solid Films 315, 345 (1998).CrossRefGoogle Scholar
15.Sheeja, D., Tay, B.K., Yu, L., and Lau, S.P.: Low stress thick diamond-like carbon films prepared by filtered arc deposition for tribological applications. Surf. Coat. Technol. 154, 289 (2002).CrossRefGoogle Scholar
16.Zhang, Q., Yoon, S.F., Ahn, J., Rusli, X., Yang, H., Gan, B., Yang, C., Watt, F., Teo, E.J., and Osipowice, T.: Structural modification of polymeric amorphous hydrogenated carbon films induced by high energetic He+ irradiation and thermal annealing. Diamond Relat. Mater. 9, 1758 (2000).CrossRefGoogle Scholar
17.Oral, B., Hauert, R., Muller, U., and Ernst, K.H.: Structural changes in doped a-C:H films during annealing. Diamond Relat. Mater. 4, 482 (1995).CrossRefGoogle Scholar
18.Tang, Z., Zhang, Z.J., Narumi, K., Xu, Y., Naramoto, H., Nagai, S., and Miyashita, K.: Effect of mass-selected ion species on structure and properties of diamond-like carbon film. J. Appl. Phys. 89, 1959 (2001).CrossRefGoogle Scholar
19.Tuinstra, F. and Koenig, J.L.: Raman spectrum of graphite. J. Chem. Phys. 53, 1126 (1970).CrossRefGoogle Scholar
20.Schwan, J., Ulrich, S., Batori, V., Ehrhardt, H., and Silva, S.R.P.: Raman spectroscopy on amorphous carbon films. J. Appl. Phys. 80, 440 (1996).CrossRefGoogle Scholar
21.Martimez, E., Andujar, J.L., Polo, M.C., Esteve, J., Robertson, J., and Milne, W.I.: Study of the mechanical properties of tetrahedral amorphous carbon films by nanoindentation. Diamond Relat. Mater. 10, 145 (2001).CrossRefGoogle Scholar
22.Nay, R.J., Warren, O.L., Yang, D., and Wyrobek, T.J.: Mechanical characterization of low-k dielectric materials using nanoindentation. Microelectron. Erte. 75, 103 (2004).CrossRefGoogle Scholar
23.Fujikane, M., Nagao, S., Liu, X.W., Chrobak, D., Lehto, A., Yamanaka, S., and Nowak, R.: Evaluation of carbon-doped low-k multilayer structure by nanoindentation. J. Alloys Cornnd. 448, 293 (2008).CrossRefGoogle Scholar
24.Shen, L., Phang, I.Y., and Liu, T.: Nanoindentation studies on polymorphism of nylon 6. Polym. Test. 25, 249 (2006).CrossRefGoogle Scholar