Synthesis and characterization of NbCr2 Laves phase produced by spark plasma sintering

Published online by Cambridge University Press:  12 February 2016

K.W. Li ,
S.M. Li ,
K. Gao  and
D.Q. Gong
K.W. Li*
Affiliation:
College of Material Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024, China
S.M. Li
Affiliation:
State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an 710072, China
K. Gao
Affiliation:
School of Mechatronics Engineering, Zhengzhou Institute of Aeronautical Industry Management, Zhengzhou, Henan 450000, China
D.Q. Gong
Affiliation:
College of Material Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024, China
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

The NbCr2 Laves phase was fabricated by spark plasma sintering (SPS) using spherical Nb and Cr powders. The experimental results revealed that increasing the sintering temperature to 1773 K can result in the formation of NbCr2 Laves phase as major phase, but it always appeared with trace amounts of Nb and Cr solid solutions. Based on the theoretical calculations, the residual of Nb and Cr solid solutions was attributed to the inhomogeneous distribution of temperature increase from the particle-contacting surface to the center of particle when pulsed current passed through. Moreover, the hardness and fracture toughness of the SPS-processed NbCr2 attained 14.05 ± 0.67 GPa and 8.9 MPa·m1/2, which were 1.6 and 7.4 times of the as-cast NbCr2 Laves phase (1.2 MPa·m1/2). The formation of ductile Nb and Cr solid solutions and fine grains were considered to be the reason for the remarkable enhancements in mechanical properties.

Keywords

Laves phasespark plasma sinteringmechanical properties
Type
Articles
Information
Journal of Materials Research , Volume 31 , Issue 3 , 15 February 2016 , pp. 380 - 387
Copyright
Copyright © Materials Research Society 2016 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

Contributing Editor: Jürgen Eckert

References

REFERENCES

Xue, Y.L., Li, S.M., Zhong, H., and Fu, H.Z.: Characterization of fracture toughness and toughening mechanisms in Laves phase Cr2Nb based alloys. Mater. Sci. Eng., A 638, 340 (2015).Google Scholar
Zhong, W., Wang, W., Yang, X., Li, W., Yan, W., Sha, W., Wang, W., Shan, Y., and Yang, K.: Relationship between Laves phase and the impact brittleness of P92 steel reevaluated. Mater. Sci. Eng., A 639, 252 (2015).Google Scholar
Jia, L.N., Weng, J.F., Li, Z., Hong, Z., Su, L.F., and Zhang, H.: Room temperature mechanical properties and high temperature oxidation resistance of a high Cr containing Nb-Si based alloy. Mater. Sci. Eng., A 623, 32 (2015).CrossRefGoogle Scholar
Lu, S.Q., Zheng, H.Z., and Fu, M.W.: The fracture toughness of hot-pressed NbCr2 alloys doped by rare earth yttrium. Scr. Mater. 61, 205 (2009).CrossRefGoogle Scholar
Nie, X.W., Lu, S.Q., and Wang, K.L.: Effect of mechanical alloying on the structure and properties of NbCr2 Laves phase fabricated by hot pressing. Powder Technol. 184, 333 (2008).Google Scholar
Ohta, T., Nakagawa, Y., Kaneno, Y., Inoue, H., Takasugi, T., and Kim, W.Y.: Microstructures and mechanical properties of NbCr2 and ZrCr2 Laves phase alloys prepared by powder metallurgy. J. Mater. Sci. 38, 657 (2003).Google Scholar
Takeyama, M. and Liu, C.T.: Microstructure and mechanical properties of Laves-phase alloys based on Cr2Nb. Mater. Sci. Eng., A 132, 61 (1991).Google Scholar
Nie, X.W., Lu, S.Q., Wang, K.L., Chen, T.C., and Niu, C.L.: Fabrication and toughening of NbCr2 matrix composites alloyed with Ni obtained by powder metallurgy. Mater. Sci. Eng., A 502, 85 (2009).Google Scholar
Lu, S.Q., Zheng, H.Z., Deng, L.P., and Yao, J.: Effect of silicon on the fracture toughness and oxidation behavior of hot pressed NbCr2 alloys. Mater. Des. 51, 432 (2013).Google Scholar
Li, K.W., Li, S.M., Wang, X.B., Zhong, H., Xue, Y.L., and Fu, H.Z.: Microstructure and mechanical properties of Cr2Nb-based Laves phase alloys prepared by laser surface remelting. JOM 66, 1886 (2014).Google Scholar
Xiao, X., Lu, S.Q., Hu, P., Huang, M.G., Nie, X.W., and Fu, M.W.: The effect of hot pressing time on the microstructure and properties of Laves phase NbCr2 alloys. Mater. Sci. Eng., A 485, 80 (2008).Google Scholar
Ge, L., Subhash, G., Baney, R.H., and Tulenko, J.S.: Influence of processing parameters on thermal conductivity of uranium dioxide pellets prepared by spark plasma sintering. J. Eur. Ceram. Soc. 34, 1791 (2014).Google Scholar
Wang, C., Cheng, L., and Zhao, Z.: FEM analysis of the temperature and stress distribution in spark plasma sintering: Modelling and experimental validation. Comput. Mater. Sci. 49, 351 (2010).Google Scholar
Zhang, F., Ahmed, F., Holzhüter, G., and Burkel, E.: Growth of diamond from fullerene C60 by spark plasma sintering. J. Cryst. Growth 340, 1 (2012).Google Scholar
Anselmi-Tamburini, U., Kodera, Y., Gasch, M., Unuvar, C., Munir, Z.A., Ohyanagi, M., and Johnson, S.M.: Synthesis and characterization of dense ultra-high temperature thermal protection materials produced by field activation through spark plasma sintering (SPS): I. Hafnium diboride. J. Mater. Sci. 41, 3097 (2006).Google Scholar
Orrù, R., Licheri, R., Locci, A.M., Cincotti, A., and Cao, G.: Consolidation/synthesis of materials by electric current activated/assisted sintering. Mater. Sci. Eng., R 63, 127 (2009).Google Scholar
Karthiselva, N.S., Murty, B.S., and Bakshi, S.R.: Low temperature synthesis of dense and ultrafine grained zirconium diboride compacts by reactive spark plasma sintering. Scr. Mater. 110, 78 (2016).Google Scholar
Sun, Y., Haley, J., Kulkarni, K., Aindow, M., and Lavernia, E.J.: Influence of electric current on microstructure evolution in Ti/Al and Ti/TiAl3 during spark plasma sintering. J. Alloys Compd. 648, 1097 (2015).Google Scholar
Kumar, R., Chaubey, A.K., Bathula, S., Jha, B.B., and Dhar, A.: Synthesis and characterization of Al2O3-TiC nano-composite by spark plasma sintering. Int. J. Refract. Met. Hard Mater. 54, 304 (2016).Google Scholar
Bolarín-Miró, A.M., Sánchez-De Jesús, F., Cortés-Escobedo, C.A., Díaz-De la Torre, S., and Valenzuela, R.: Synthesis of M-type SrFe12O19 by mechanosynthesis assisted by spark plasma sintering. J. Alloys Compd. 643(Suppl 1), S226 (2015).Google Scholar
Liu, W., Fu, Y.M., and Sha, J.B.: Microstructure and mechanical properties of Nb–Si alloys fabricated by spark plasma sintering. Prog. Nat. Sci. 23, 55 (2013).Google Scholar
Couret, A., Molénat, G., Galy, J., and Thomas, M.: Microstructures and mechanical properties of TiAl alloys consolidated by spark plasma sintering. Intermetallics 16, 1134 (2008).Google Scholar
Chawake, N., Koundinya, N.T.B.N., Srivastav, A.K., and Kottada, R.S.: On correlation between densification kinetics during spark plasma sintering and compressive creep of B2 aluminides. Scr. Mater. 107, 63 (2015).Google Scholar
Shanmugasundaram, T., Guyon, J., Monchoux, J.P., Hazotte, A., and Bouzy, E.: On grain refinement of a γ-TiAl alloy using cryo-milling followed by spark plasma sintering. Intermetallics 66, 141 (2015).Google Scholar
Bu, J., Jönsson, P.G., and Zhao, Z.: Dense and translucent BaZrxCe0.8−xY0.2O3−δ (x = 0.5, 0.6, 0.7) proton conductors prepared by spark plasma sintering. Scr. Mater. 107, 145 (2015).Google Scholar
Li, X. and Bhushan, B.: A review of nanoindentation continuous stiffness measurement technique and its applications. Mater. Charact. 48, 11 (2002).Google Scholar
Anstis, G.R., Chantikul, P., Lawn, B.R., and Marshall, D.B.: A critical evaluation of indentation techniques for measuring fracture toughness: I, Direct crack measurements. J. Am. Ceram. Soc. 64, 533 (1981).CrossRefGoogle Scholar
Groza, J.R.: Consolidation of atomized NiAl powders by plasma activated sintering process. Scr. Metall. Mater. 30, 47 (1994).Google Scholar
Tsuchida, T., Furuichi, R., and Ishii, T.: Reactivity of η-, γ-, and α-Al2O3 for ZnAl2O4 formation. Z. Anorg. Allg. Chem. 415, 175 (1975).CrossRefGoogle Scholar
Schmetterer, C., Khvan, A., Jacob, A., Hallstedt, B., and Markus, T.: A new theoretical study of the Cr-Nb system. J. Phase Equilib. Diffus. 35, 434 (2014).Google Scholar
Liu, X., Song, X., and Zhang, J.: Neck formation and self-adjusting mechanism of neck growth of conducting powders in spark plasma sintering. J. Am. Ceram. Soc. 89, 494 (2006).Google Scholar
Suárez, M., Fernández, A., Menéndez, J.L., Torrecillas, R., Kessel, H.U., Hennicke, J., Kirchner, R., and Kessel, T.: Challenges and opportunities for spark plasma sintering: A key technology for a new generation of materials. In Sintering Applications, Ertuğ, Burcu, ed. (Intech, 2013). doi: 10.5772/53706.Google Scholar
Oliver, W.C. and Pharr, G.M.: An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564 (1992).Google Scholar
Tabor, D.: The Hardness of Metals (Oxford University Press, Oxford, 1951).Google Scholar
Chu, F., He, Y., Thoma, D.J., and Mitchell, T.E.: Elastic constants of the C15 laves phase compound NbCr2 . Scr. Metall. Mater. 33, 1295 (1995).Google Scholar
Lee, S., Liaw, P.K., Liu, C.T., and Chou, Y.T.: Cracking in Cr-Cr2Nb eutectic alloys due to thermal stresses. Mater. Sci. Eng., A 268, 184 (1999).Google Scholar