Suppression of SiC surface roughening during high-temperature annealing by atmospheric control using purified Ar gas

Published online by Cambridge University Press:  31 January 2011

Atsushi Ogura ,
Daisuke Kosemura  and
Shingo Kinoshita
Shingo Kinoshita
Affiliation:
School of Science and Technology, Meiji University, Tama-ku, Kawasaki 214-8571, Japan
Get access

Abstract

4H-silicon carbide (SiC) wafers were annealed at 1300 and 1600 °C for 30 min and 60 min in a conventional and purified Ar atmosphere. The surface roughness before and after annealing was evaluated by atomic force microscopy. The surface roughness before annealing was approximately 2.37 nm in root mean square. The roughness, after annealing for 30 min at 1300 and 1600 °C in a conventional Ar furnace, was increased to 4.53 and 14.9 nm, respectively. The roughness, after annealing for 60 min, was 5.01 and 19.1 nm, respectively. In this study, the G3 grade Ar gas (99.999%) was supplied in the conventional furnace tube. When the Ar gas was purified to an impurity concentration of less than 1 ppb, and it was supplied in the leak-tight furnace tube, the roughness after 30-min annealing improved 4.27 and 6.93 nm at 1300 and 1600 °C, respectively. The roughness after 60-min annealing was also reduced to 3.54 and 9.28 nm, respectively. We assume that a significant reduction of H2O concentration in the annealing atmosphere might play an important role in suppressing surface roughening of SiC during high-temperature annealing.

Type
Articles
Information
Journal of Materials Research , Volume 25 , Issue 4 , April 2010 , pp. 708 - 710
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Matsunami, H., Kimoto, T.Step-controlled epitaxial growth of SiC: High quality homoepitaxy. Mater. Sci. Eng., R 20, 125 (1997)Google Scholar
2.Matsunami, H.Current SiC technology for power electronic devices beyond Si. Microelectron. Eng. 83, 2 (2006)Google Scholar
3.Ohashi, H.Possibility of power electronics paradigm shift with wide band gap semiconductors. Mater. Sci. Forum 457, 21 (2004)Google Scholar
4.Sankin, I., Merrett, J.N., Draper, W.A., Casady, J.R.B., Casady, J.B.A review of SiC power switch: Achievements, difficulties and perspectives. Mater. Sci. Forum 457, 1249 (2004)CrossRefGoogle Scholar
5.Nakashima, S., Mitani, T., Senzaki, J., Okumura, H., Yamamoto, T.Deep ultraviolet Raman scattering characterization of ion-implanted SiC crystals. J. Appl. Phys. 97, 123507 (2005)CrossRefGoogle Scholar
6.Matsuura, H., Sugiyama, K., Nishikawa, K., Nagata, T., Fukunaga, N.Occupation probability for acceptor in Al-implanted p-type 4H–SiC. J. Appl. Phys. 94, 2234 (2003)Google Scholar
7.Kimoto, T., Takemura, O., Matsunami, H., Nakata, T., Inoue, M.Al+ and B+ implantations into 6H-SiC epilayers and application to pn junction diodes. J. Electron. Mater. 27, 358 (1998)Google Scholar
8.Negoro, Y., Katsumoto, K., Kimoto, T., Matsunami, H.Electronic behaviors of high-dose phosphorus-ion implanted 4H–SiC (0001). J. Appl. Phys. 96, 224 (2004)CrossRefGoogle Scholar
9.Saddow, S.E., Williams, J., Isaacs-Smith, T., Copper, M.A. Jr., Mazzola, M.S., Hsieh, A.J., Casaby, B.High-temperature implant activation in 4H and 6H-SiC in a silane ambient to reduce step bunching. Mater. Sci. Forum 338, 901 (2000)Google Scholar
10.Shibagaki, M., Kurematsu, Y., Watanabe, F., Haga, S., Miura, K., Suzuki, T., Satoh, M.Development of the novel electron bombardment anneal system (EBAS) for SiC post ion implantation anneal. Mater. Sci. Forum 483, 609 (2005)CrossRefGoogle Scholar
11.SIMOX edited by M.J. Anc (The Institution of Electrical Engineers, London 2004)Google Scholar
12.Johnson, B., Tan, Y., Anderson, P., Seraphin, S., Anc, M.J.The effect of surface capping during annealing on the microstructure of ultrathin SIMOX materials. J. Electrochem. Soc. 148, G63 (2001)Google Scholar
13.White, A.E., Short, K.T., Batstone, J.L., Jacobson, D.C., Poate, J.M., West, K.W.Mechanism of buried oxide formation by ion implantation. Appl. Phys. Lett. 50, 19 (1987)CrossRefGoogle Scholar
14.Thompson, K., Larson, D.J., Kelly, T.F.Mechanism of Si field evaporation. Microsc. Microanal. 11, 888 (2005)Google Scholar