Stress-assisted-electrochemical corrosion of Cu-based bulk metallic glass

Published online by Cambridge University Press:  31 January 2011

Ding Li ,
Mimi Yang ,
Fuqian Yang  and
Peter K. Liaw
Ding Li
Affiliation:
Materials Program, Department of Chemical and Materials Engineering, University of Kentucky, Lexington, Kentucky 40506
Mimi Yang
Affiliation:
MSTC Program, Paul Laurence Dunbar High School, Lexington, Kentucky 40513
Fuqian Yang*
Affiliation:
Materials Program, Department of Chemical and Materials Engineering, University of Kentucky, Lexington, Kentucky 40506
Peter K. Liaw
Affiliation:
Department of Materials Science and Engineering, University of Tennessee, Knoxville, Tennessee 37994
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Using the microindentation test, the stress-assisted-electrochemical corrosion of Cu46.25Zr45.25Al7.5Er1 bulk metallic glass (BMG) was studied in a 10 wt% NaCl electrolyte. The microindentation was performed in an indentation load range of 500 to 4000 mN to create shear bands over the deformation zone. Electric current of various densities was passed through the indented BMGs to evaluate the effect of shear bands and localized deformation on the electrochemical corrosion of the BMGs. Surface pits always initiated from the shear-banding zone and the contact edges between the indenter and the BMGs, and the size of the corroded zone grew with the increase in the polarization time, the indentation load, and the current density. Wormlike amorphous whiskers were formed over the corroded zone, and the density of the wormlike whiskers increased with the current density and polarization time.

Keywords

AmorphousNanoindentation
Type
Articles
Information
Journal of Materials Research , Volume 25 , Issue 3 , March 2010 , pp. 592 - 597
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Schroeder, V., Ritchie, R.O.Stress-corrosion fatigue-crack growth in a Zr-based bulk amorphous metal. Acta Mater. 54, 1785 (2006)CrossRefGoogle Scholar
2.Pampillo, C.A.Flow and fracture in amorphous alloys. J. Mater. Sci. 10, 1194 (1975)Google Scholar
3.Sandenbergh, R.F., Latanision, R.M.The stress-corrosion cracking of a glassy Fe32Ni36Cr14P12B6 alloy. Corrosion 41, 369 (1985)Google Scholar
4.Kawashima, A., Hashimoto, K., Masumoto, T.Stress-corrosion cracking of amorphous iron base alloys. Corros. Sci. 16, 935 (1976)Google Scholar
5.Jiang, W.H., Jiang, F., Green, B.A., Liu, F.X., Liaw, P.K., Choo, H., Qiu, K.Q.Electrochemical corrosion behavior of a Zr-based bulk-metallic glass. Appl. Phys. (Berl.) 91, 041904 (2007)Google Scholar
6.Li, X. D., Bhushan, B.Micro/nanomechanical and tribological studies of bulk and thin film materials used in magnetic recording heads Thin Solid Films 398, 313 (2001)CrossRefGoogle Scholar
7.Yang, F.Q., Jiang, C.B., Du, W.W., Zhang, Z.Q., Li, S.X., Mao, S.X.Nanomechanical characterization on ZnS nanobelts. Nanotechnology 16, 1073 (2005)CrossRefGoogle Scholar
8.Yang, F.Q., Geng, K., Liaw, P.K., Fan, G.J., Choo, H.Deformation in a Zr57Ti5Cu20Ni8Al10 bulk metallic glass during nanoindentation. Acta Mater. 55, 321 (2007)CrossRefGoogle Scholar
9.Yang, F.Q., Li, D., Yang, M.M.L., Li, R., Jiang, W.H., Wang, G.Y., Zhang, T., Liaw, P.K.Localized deformation of a Cu46.25Zr45.25Al7.5Er1 bulk metallic glass. J. Phys. D: Appl. Phys. 42, 065401 (2009)CrossRefGoogle Scholar
10.Li, D., Yang, M.M.L., Muralidhar, P., Wu, C., Yang, F.Q.Local surface damage and material dissolution in 45S5 bioactive glass: Effect of the contact deformation. J. Non-Cryst. Solids 355, 874 (2009)Google Scholar
11.Li, D., Yang, F.Q., Nychka, J.Indentation-induced residual stresses in 45S5 bioglass and the stress effect on the material dissolution. Eng. Fract. Mech. 75, 4898 (2008)Google Scholar
12.Jana, S., Ramamurty, U., Chattopadhyay, K., Kawamura, Y.Subsurface deformation during Vickers indentation of bulk metallic glasses. Mater. Sci. Eng., A 375–377, 1191 (2004)Google Scholar
13.Johnson, K.L.Contact Mechanics (Cambridge University Press, Cambridge 1987)Google Scholar
14.Marsh, D.M.Plastic flow in glass. Proc. R. Soc. London, Ser. A 279, 420 (1964)Google Scholar
15.Yang, F.Q., Peng, L.L., Okazaki, K.J.Micro-indentation of aluminum processed by equal channel angular extrusion. Metall. Mater. Trans. A 35, 3323 (2004)CrossRefGoogle Scholar
16.Kramer, D., Huang, H., Kriese, M., Robach, J., Nelson, J., Wright, A., Bahr, D., Gerberich, W.W.Yield strength predictions from the plastic zone around nanocontacts. Acta Mater. 47, 333 (1998)Google Scholar