Shear localization of nanoscale W in metallic glass composites

Published online by Cambridge University Press:  01 February 2006

Min Ha Lee  and
Daniel J. Sordelet
Min Ha Lee
Affiliation:
Materials and Engineering Physics Program, Ames Laboratory, Iowa State University, Ames, Iowa 50011
Daniel J. Sordelet*
Affiliation:
Materials and Engineering Physics Program, Ames Laboratory, Iowa State University, Ames, Iowa 50011
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

High-density tungsten/metallic glass composites were fabricated by warm extrusion of two different powders. The first powder was a physical blend of −45 μm tungsten and Hf-based metallic glass powders and produced a relatively coarse distribution of tungsten particles within a continuous metallic glass matrix. The second powder was synthesized by mechanical milling the −45 μm tungsten and Hf-based metallic glass powders into composite particles composed of 20–500-nm layers of tungsten and metallic glass. The amorphous structure of the starting glass powders did not change during milling. Some macroscopic plasticity during compression testing was observed due to the formation of multiple shear bands at the interface between the coarse tungsten particles and the metallic glass matrix in the composite produced from blended powders. In contrast, shear localization without a decrease in strength occurred uniformly throughout the nano-grained tungsten and metallic glass phases in the sample obtained from extruded composite powders.

Keywords

CompositeGlassNanoscale
Type
Articles
Information
Journal of Materials Research , Volume 21 , Issue 2 , February 2006 , pp. 492 - 499
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Inoue, A.: Stabilization of metallic supercooled liquid and bulk amorphous alloys. Acta Mater. 48, 279 (2000).CrossRefGoogle Scholar
2.He, G., Eckert, J. and Loser, W.: Stability, phase transformation and deformation behavior of Ti-base metallic glass and composites. Acta Mater. 51, 1621 (2003).CrossRefGoogle Scholar
3.Steif, P.S., Spaepen, F. and Hutchinson, J.W.: Strain localization in amorphous metals. Acta Metall. 30, 447 (1982).CrossRefGoogle Scholar
4.Ramesh, K.T. and Coates, R.S.: Microstructural influences on the viscoplastic response of tungsten heavy alloys. Metall. Mater. Trans. A23, 2625 (1992).CrossRefGoogle Scholar
5.Bruck, H.A., Christman, T., Rosakis, A.J. and Johnson, W.L.: Quasi-static constitutive behavior of Zr41.25Ti13.75Ni10Cu12.5Be22.5 bulk amorphous alloy. Scripta Mater. 30, 429 (1994).CrossRefGoogle Scholar
6.Conner, R.D., Dandliker, R.B., Scruggs, V. and Johnson, W.L.: Dynamic deformation behavior of tungsten-fiber/metallic-glass matrix composites. Int. J. Impct. Eng. 24, 435 (2000).CrossRefGoogle Scholar
7.Choi-Yim, H., Conner, R.D., Szuecs, F. and Johnson, W.L.: Quasistatic and dynamic deformation of tungsten reinforced Zr57Nb5Al10Cu15.4Ni12.6 bulk metallic glass matrix composites. Scripta Mater. 45, 1039 (2001).CrossRefGoogle Scholar
8.Wei, Q., Ramesh, K.T., Ma, E., Kesckes, L.J., Dowing, R.J., Kazykhanov, V.U. and Valiev, R.Z.: Plastic flow localization in bulk tungsten with ultrafine microstructure. Appl. Phys. Lett. 86, 101907 (2005).CrossRefGoogle Scholar
9.Choi-Yim, H., Busch, R., Koster, U. and Johnson, W.L.: Synthesis and characterization of particulate reinforced Zr57Nb5Al10Cu15.4Ni12.6 bulk metallic glass composites. Acta Mater. 47, 2455 (1999).CrossRefGoogle Scholar
10.Hays, C.C., Kim, C.P. and Johnson, W.L.: Improved mechanical behavior of bulk metallic glasses containing in situ formed ductile phase dendrite dispersions. Mater. Sci. Eng. A 304–306, 650 (2001).CrossRefGoogle Scholar
11.Pekarskaya, E., Kim, C.P. and Johnson, W.L.: In situ transmission electron microscopy studies of shear bands in a bulk metallic glass based composite. J. Mater. Res. 16, 2513 (2001).CrossRefGoogle Scholar
12.Lee, M.H., Bae, D.H., Kim, D.H. and Sordelet, D.J.: Synthesis of Ni-based bulk metallic glass matrix composites containing ductile brass phase by warm extrusion of gas atomized powders. J. Mater. Res. 18, 2513 (2003).CrossRefGoogle Scholar
13.Leonhard, A., Xing, L.Q., Heilmaier, M., Gebert, A., Eckert, J. and Schultz, L.: Effect on crystalline precipitations on the mechanical behavior of bulk glass forming Zr-based alloys. Nanostruct. Mater. 10, 805 (1998).CrossRefGoogle Scholar
14.Venkataraman, S., Rozhkova, E., Eckert, J., Schultz, L. and Sordelet, D.J.: Thermal stability and crystallization kinectics of Cu-reinforced Cu47Ti33Zr11Ni8Si1 metallic glass composite powders synthesized by ball milling: The effect of particulate reinforcement. Intermetallics 13, 833 (2005).CrossRefGoogle Scholar
15.Kecskes, L.J., Edwards, B.T., and Woodman, R.H.: Hafnium-based bulk metallic glasses for kinetic energy penetrators, in Proceedings of the 24th Army Science Conference (Assistant Secretary of the Army, Washington, DC, 2004).Google Scholar
16.Bae, D.H., Lee, M.H., Kim, D.H. and Sordelet, D.J.: Plasticity in Ni59Zr20Ti16Si2Sn3 metallic glass matrix composites containing brass fiber synthesized by warm extrusion of powders. Appl. Phys. Lett. 83, 2312 (2003).CrossRefGoogle Scholar
17.Li, H., Subhash, G., Kecskes, L.J. and Dowing, R.J.: Mechanical behavior of tungsten preform reinforced bulk metallic glass composites. Mater. Sci. Eng. A 403, 134 (2005).CrossRefGoogle Scholar
18.Sun, Y.F., Guan, S.K., Wei, B.C., Wang, Y.R. and Shek, C.H.: Brittleness of Zr-based bulk metallic glass matrix composites containing ductile dendritic phase. Mater. Sci. Eng. A 406, 57 (2005).CrossRefGoogle Scholar
19.Ishijima, Y., Kurishita, H., Arakawa, H., Hasegawa, M., Hiraoka, Y., Takida, T. and Takebe, K.: Microstructure and bend ductility of W–0.3 mass% TiC alloys fabricated by advanced powder-metallurgucal processing. Mater. Trans. 46, 568 (2005).CrossRefGoogle Scholar
20.Sordelet, D.J., Rozhkova, E., Besser, M.F. and Kramer, M.J.: Consolidation of gas atomized Cu47Ti34Zr11Ni8 amorphous powders. J. Non-Cryst. Solids 315, 137 (2003).CrossRefGoogle Scholar
21.Jiao, T., Kecskes, L.J., Hufnagel, T.C. and Ramesh, K.T.: Deformation and failure of Zr57Nb5Al10Cu15.4Ni12.6/W particle composites under quasi-static and dynamic compression. Metall. Mater. Trans. 35A, 3439 (2004).CrossRefGoogle Scholar
22.Bae, D.H., Lee, M.H. and Kim, D.H.: Deformation behavior of Ni-based metallic glass matrix composites reinforced by brass short-fibers synthesized by warm extrusion of powders. Mater. Sci. Forum 449–452, 937 (2004).CrossRefGoogle Scholar
23.Becher, P.F.: Microstructural design of toughened ceramics. J. Am. Ceram. Soc. 74, 255 (1991).CrossRefGoogle Scholar
24.Biner, S.B.: Stress state and growth behavior of bridged cracks at creep regime. Eng. Frac. Mech. 69, 923 (2002).CrossRefGoogle Scholar