Raman spectroscopy studies on the thermal stability of TiN, CrN, TiAlN coatings and nanolayered TiN/CrN, TiAlN/CrN multilayer coatings

Published online by Cambridge University Press:  01 November 2004

Harish C. Barshilia  and
K.S. Rajam
Harish C. Barshilia*
Affiliation:
Surface Engineering Division, National Aerospace Laboratories, Bangalore 560 017, India
K.S. Rajam
Affiliation:
Surface Engineering Division, National Aerospace Laboratories, Bangalore 560 017, India
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

About 1.5-μm-thick single-layer TiN, CrN, TiAlN coatings and nanolayered TiN/CrN, TiAlN/CrN multilayer coatings were deposited on silicon (111) substrates using a reactive direct current magnetron sputtering process. Structural characterization of the coatings was done using x-ray diffraction (XRD) and micro-Raman spectroscopy. All the coatings exhibited NaCl B1 structure in the XRD data. Raman spectroscopy data of as-deposited coatings exhibited two broad bands centered at 230–250 and 540–630 cm-1. These bands have been assigned to acoustical and optical phonon modes, respectively. Thermal stability of the coatings was studied by heating the coatings in air in a resistive furnace for 30 min in the temperature range 400–900 °C. Structural changes as a result of heating were characterized using Raman spectroscopy and XRD. Raman data showed that TiN, CrN, TiN/CrN, TiAlN, and TiAlN/CrN coatings started to oxidize at 500, 600, 750, 800, and 900 °C, respectively. To isolate the oxidation-induced spectral changes as a result of heating of the coatings in air, samples were also annealed in vacuum at 800 °C under similar conditions. The Raman data of vacuum-annealed coatings showed no phase transformation, and intensity of the optical phonon mode increased and shifted to lower frequencies. The origin of these spectral changes is discussed in terms of defect structure of the coatings. Our results indicate that the thermal stability of nanolayered multilayer coatings is superior to the single-layer coatings.

Keywords

CoatingPhysical vapor deposition (PVD)Raman spectroscopy
Type
Articles
Information
Journal of Materials Research , Volume 19 , Issue 11 , November 2004 , pp. 3196 - 3205
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Munz, W.D.: Titanium aluminium nitride films: A new alternative to TiN coatings. J. Vac. Sci. Technol. A 4, 2717 (1986).Google Scholar
2Barshilia, H.C. and Rajam, K.S.: Characterization of Cu/Ni multilayer coatings by nanoindentation and atomic force microscopy. Surf. Coat. Technol. 155, 195 (2002).CrossRefGoogle Scholar
3Barshilia, H.C. and Rajam, K.S.: Deposition of TiN/CrN hard superlattices by reactive DC magnetron sputtering. Bull. Mater. Sci. 26, 233 (2003).CrossRefGoogle Scholar
4Barshilia, H.C., Jain, A. and Rajam, K.S.: Structure, hardness and thermal stability of nanolayered TiN/CrN multilayer coatings. Vacuum 72/73, 241 (2004).Google Scholar
5Barshilia, H.C. and Rajam, K.S.: Structure and properties of reactive DC magnetron sputtered TiN/NbN hard superlattices. Surf. Coat. Technol. 183, 174 (2004).CrossRefGoogle Scholar
6Barshilia, H.C., Prakash, M.S., Poojari, A. and Rajam, K.S.: Corrosion behavior of nanolayered TiN/NbN multilayer coatings prepared by reactive DC magnetron sputtering process. Thin Solid Films 460, 133 (2004).CrossRefGoogle Scholar
7Panjan, P., Navinsek, B., Cvelbar, A., Zalar, A. and Milosev, I.: Oxidation of TiN, ZrN, TiZrN, CrN, TiCrN and TiN/CrN multilayer hard coatings reactively sputtered at low temperature. Thin Solid Films 281–282, 298 (1996).CrossRefGoogle Scholar
8Ichimura, H. and Kawana, A.: High-temperature oxidation of ion-plated TiN and TiAlN films. J. Mater. Res. 8, 1093 (1993).Google Scholar
9Franck, M., Celis, J-P. and Roos, J.R.: Microprobe Raman spectroscopy of TiN coatings oxidized by solar beam heat treatment. J. Mater. Res. 10, 119 (1995).CrossRefGoogle Scholar
10Mayrhofer, P.H., Willmann, H. and Mitterer, C.: Oxidation kinetics of sputtered Cr-N coatings. Surf. Coat. Technol. 146–147, 222 (2001).Google Scholar
11Tu, Jui-Neng, Duh, Jenq-Gong and Tsai, Shu-Yueh.: Morphology, mechanical properties, and oxidation behavior of reactively sputtered Cr-N films. Surf. Coat. Technol. 133–134, 181 (2000).Google Scholar
12Ichimura, H. and Kawana, A.: High temperature oxidation of ion-plated CrN films. J. Mater. Res. 9, 151 (1994).CrossRefGoogle Scholar
13McIntyre, D., Greene, J.E., Hakansson, G., Sundgren, J.E. and Munz, W.D.: Oxidation of metastable single-phase polycrystalline Ti0.5Al0.5N films: Kinetics and mechanisms. J. Appl. Phys. 67, 1542 (1990).CrossRefGoogle Scholar
14Panjan, P., Navinsek, B., Cvelbar, A., Zalar, A. and Vlcek, J.: High temperature oxidation of TiN/CrN multilayers reactively sputtered at low temperatures. Surf. Coat. Technol. 98, 1497 (1998).CrossRefGoogle Scholar
15Wadsworth, I., Smith, I.J., Donohue, L.A. and Munz, W.D.: Thermal stability and oxidation resistance of TiAlN/CrN multilayer coatings. Surf. Coat. Technol. 94–95, 315 (1997).CrossRefGoogle Scholar
16 H.C. Barshilia, M.S. Prakash, A. Jain, and K.S. Rajam: Structure, hardness and thermal stability of TiAlN coatings and nanolayered TiAlN/CrN multilayer coatings. Vacuum (in press).Google Scholar
17Spengler, W. and Kaiser, R.: First and second order Raman scattering in transition metal compounds. Solid State Commun. 18, 881 (1976).CrossRefGoogle Scholar
18Vancoille, E., Blanpain, B., Xingpu, Y., Celis, J.P. and Roos, J.R.: Tribo-oxidation of a TiN coating sliding against corundum. J. Mater. Res. 9, 992 (1994).CrossRefGoogle Scholar
19Muraki, N., Sergo, V., Pezzotti, G., Katagiri, G., Meriani, S. and Nishida, T.: Raman piezo-spectroscopic behavior of aluminum nitride. Appl. Spectro. 51, 1761 (1997).Google Scholar
20Chowdhury, R., Vispute, R.D., Jagannadham, K. and Narayan, J.: Characteristics of titanium nitride films grown by pulsed laser deposition. J. Mater. Res. 11, 1458 (1996).CrossRefGoogle Scholar
21Barata, A., Cunha, L. and Moura, C.: Characterization of chromium nitride films produced by PVD techniques. Thin Solid Films 398–399, 501 (2001).CrossRefGoogle Scholar
22Bernard, M., Deneuville, A., Thomas, O., Gergaud, P., Sandstrom, P. and Birch, J.: Raman spectra of TiN/AlN superlattices. Thin Solid Films 380, 252 (2000).CrossRefGoogle Scholar
23Parker, J.C. and Siegel, R.W.: Raman microprobe study of nanophase TiO2 and oxidation-induced spectral changes. J. Mater. Res. 5, 1246 (1990).CrossRefGoogle Scholar
24Misra, A., Bist, H.D., Navati, M.S., Thareja, R.K. and Narayan, J.: Thin film of aluminum oxide through pulsed laser deposition: A micro-Raman study. Mater. Sci. Eng. B 79, 49 (2001).CrossRefGoogle Scholar
25Spengler, W., Kaiser, R., Christensen, A.N. and Muller-Vogt, G.: Raman scattering, superconductivity and phonon density of states of stoichiometric and non-stoichiometric TiN. Phys. Rev. B 17, 1095 (1978).CrossRefGoogle Scholar
26Constable, C.P., Yarwood, J. and Munz, W.D.: Raman microscopic studies of PVD hard coatings. Surf. Coat. Technol. 116–119, 155 (1999).CrossRefGoogle Scholar
27Hultman, L.: Thermal stability of nitride thin films. Vacuum 57, 1 (2000).CrossRefGoogle Scholar
28Kosacki, I., Suzuki, T., Anderson, H.U. and Colomban, P.: Raman scattering and lattice defets in nanocrystalline CeO2 thin films. Solid State Ionics 149, 99 (2002).CrossRefGoogle Scholar
29Constable, C.P., Lewis, D.B., Yarwood, J. and Munz, W.D.: Raman microscopic studies of residual and applied stress in PVD hard ceramic coatings and correlation with x-ray diffraction (XRD) measurements. Surf. Coat. Technol. 184, 291 (2004).CrossRefGoogle Scholar
30Petrov, I., Hultman, L., Helmersson, U., Sundgren, J-E. and Greene, J.E.: Microstructure modification of TiN by ion bombardment during reactive sputter deposition. Thin Solid Films 169, 299 (1989).CrossRefGoogle Scholar
31Ljungcrantz, H., Hultman, L., Sundgren, J.E. and Karlsson, L.: Ion induced stress generation in arc-evaporated TiN films. J. Appl. Phys. 78, 832 (1995).Google Scholar
32Hultman, L., Helmersson, U., Barnett, S.A., Sundgren, J-E. and Greene, J.E.: Low-energy ion irradiation during film growth for reducing defect densities in epitaxial TiN (100) films deposited by reactive-magnetron sputtering. J. Appl. Phys. 61, 552 (1987).CrossRefGoogle Scholar
33Fujii, M., Hayashi, S. and Yamamoto, K.: Raman scattering from quantum dots of Ge embedded in SiO2 thin films. Appl. Phys. Lett. 57, 2692 (1990).CrossRefGoogle Scholar
34Tanaka, Y., Gur, T.M., Kelly, M., Hagstrom, S.B., Ikeda, T., Wakihira, K. and Satoh, H.: Properties of (Ti1-xAlx)N coatings for cutting tools prepared by the cathodic arc ion plating method. J. Vac. Sci. Technol. A 10, 1749 (1992).Google Scholar
35Andrievski, R.A., Anisimova, I.A., Anisimov, V.P., Makarov, V.P. and Popova, V.P.: Grain size and recrystallization of TiN, ZrN, NbN, and CrN alloyed and multilayer films. Thin Solid Films 261, 83 (1995).Google Scholar