New configuration of a [001] superdislocation formed during high-temperature creep in the γ′ phase of a single-crystal superalloy TMS-138

Published online by Cambridge University Press:  01 March 2006

J.X. Zhang ,
H. Harada  and
Y. Koizumi
J.X. Zhang*
Affiliation:
National Institute for Materials Science, Tsukuba, Ibaraki 305-0047, Japan
H. Harada
Affiliation:
National Institute for Materials Science, Tsukuba, Ibaraki 305-0047, Japan
Y. Koizumi
Affiliation:
National Institute for Materials Science, Tsukuba, Ibaraki 305-0047, Japan
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

A new configuration of a superdislocation in the γ′ phase of a fourth-generation single-crystal TMS-138 superalloy was found after creep rupture in a [001] tensile test at 1150 °C and 137 MPa. The segments of the superdislocation lie in four directions, i.e., [110], [110], [100], and [010], strictly on a (001) plane with a Burgers vector b = [001]. This superdislocation is pure edge in character and does not dissociate into superpartials. Microstructural evidence shows that this kind of superdislocation is formed by combination of two interfacial dislocations with different Burgers vectors, i.e., 1/2[011] + 1/2[011] → [001].

Keywords

AlloyDislocationsTransmission electron microscopy (TEM)
Type
Articles
Information
Journal of Materials Research , Volume 21 , Issue 3 , March 2006 , pp. 647 - 654
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Nabarro, F.R.N., de Villiers, H.L.: The Physics of Creep (Taylor and Francies, London, UK, 1995), p. 187.Google Scholar
2.Kear, B.H., Hornbecker, M.F.: Deformation structure in polycrystalline Ni3Al. Trans. Am. Soc. Metals 59, 155 (1966).Google Scholar
3.Staton-Bevan, A.E., Rawlings, R.D.: Dislocation structures in deformed single-crystal Ni3(Al,Ti). Philos. Mag. 32, 787 (1975).CrossRefGoogle Scholar
4.Sun, Y.Q., Hazzledine, P.M. Geometry of dislocation glide in L12 γ′ phase: TEM observations, in Dislocations in Solids, Vol. 10, edited by Nabarro, F.R.N. and Duesbery, M.S. (Elsevier Science, Amsterdam, The Netherlands, 1996), p. 29.Google Scholar
5.Sun, Y.Q., Hazzledine, P.M.: A TEM weak-beam study of dislocations in γ′ in a deformed Ni-based superalloy. Philos. Mag. A 58, 603 (1988).CrossRefGoogle Scholar
6.Pollock, T.M., Argon, A.S.: Creep resistance of CMSX-3 nickel base superalloy single crystals. Acta Metal. Mater. 40, 1 (1992).CrossRefGoogle Scholar
7.Louchet, F., Ignat, M.: TEM analysis of square-shaped dislocation configurations in the γ′ phase of a Ni-based superalloy. Acta Metal. 34, 1681 (1986).CrossRefGoogle Scholar
8.Bonnet, R., Ati, A.: Observation of interactions of γ/γ′ interfacial dislocations in the two-phase superalloy. Acta Metall. 37, 2153 (1989).CrossRefGoogle Scholar
9.Eggeler, G., Dlouhy, A.: On the formation of 〈010〉-dislocations in the γ′-phase of superalloy single crystals during high temperature low stress creep. Acta Mater. 45, 4251 (1997).CrossRefGoogle Scholar
10.Srinivasan, R., Eggeler, G.F., Mills, M.J.: γ′-cutting as rate-controlling recovery process during high-temperature and low-stress creep of superalloy single crystals. Acta Mater. 48, 4867 (2000).CrossRefGoogle Scholar
11.Srinivasan, R., Nathal, M.V., Daw, M.S., Eggeler, G.F., Mills, M.J. Mechanisms of shearing of γ′ precipitates during high temperature / low stress creep of superalloy single crystals, in Structural Intermetallics 2001, edited by Hemker, K.J., Dimiduk, D.M., Clemens, H., Darolia, R., Inui, H., Larsen, J.M., Sikka, V.K., Thomas, M., and Whittenberger, J.D. (The Minerals, Metals & Materials Society, Warrendale, PA, 2001), p. 423.Google Scholar
12.Koizumi, Y., Zhang, J.X., Kobayashi, T., Yokokawa, T., Harada, H., Aoki, Y., Arai, M.: Development of next generation Ni-base single crystal superalloys containing ruthenium. J. Japan Inst. Metals. 67, 468 (2003).CrossRefGoogle Scholar
13.Edington, J.W.: Practical Electron Microscopy in Materials Science. (N.V. Philips’ Gloeilampenfabrieken, Eindhoven, 1976), p. 87.Google Scholar
14.Hirth, J.P., Lothe, J.: Theory of Dislocations, 2nd ed. (Krieger Publishing Company, Malabar, FL, 1992).Google Scholar
15.Williams, D.B., Carter, C.B.: Transmission Electron Microscopy (Plenum Press, New York, 1996), p. 405.CrossRefGoogle Scholar
16.Foreman, A.J.F.: Dislocation energies in anisotropic crystals. Acta Metall. 3, 322 (1955).CrossRefGoogle Scholar
17.Hazzledine, P.M., Yoo, M.H., Sun, Y.Q.: The geometry of glide in Ni3Al at temperatures above the flow stress peak. Acta Metall. 37, 3235 (1989).CrossRefGoogle Scholar
18.Veyssiere, P., Douin, J.: Dislocations with 〈100〉 Burgers vectors in Ni3Al. Philos. Mag. A 51((2)), L1 (1985).CrossRefGoogle Scholar