Multiferroic properties of Dy modified BiFeO3 thin films in comparison with Tb modified BiFeO3 thin films

Published online by Cambridge University Press:  31 January 2011

V.R. Palkar ,
R. Anisha ,
R. Pinto  and
S. Bhattacharya
V.R. Palkar*
Affiliation:
Tata Institute of Fundamental Research, Mumbai 400005, India
R. Anisha
Affiliation:
Indian Institute of Technology Bombay, Mumbai 400076, India
R. Pinto
Affiliation:
Indian Institute of Technology Bombay, Mumbai 400076, India
S. Bhattacharya
Affiliation:
Tata Institute of Fundamental Research, Mumbai 400005, India
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Coexistence of ferroelectric and ferromagnetic order parameters was observed at room temperature in Bi0.6Dy0.3La0.1FeO3 thin films grown on Pt/TiO2/SiO2/Si substrates using a pulsed laser deposition technique similar to that for Bi0.6Tb0.3La0.1FeO3. The coexistence of ferroelectric and magnetic domains in specific spatial area of the thin film was also confirmed by scanning probe imaging. As expected, the magnetization values obtained for Bi0.6Dy0.3La0.1FeO3 bulk and thin films were higher than those of Bi0.6Tb0.3La0.1FeO3 bulk and polycrystalline thin films because the magnetic moment of Dy is higher than that of Tb. However, preferentially oriented thin films of Bi0.6Tb0.3La0.1FeO3 exhibit much higher magnetization values. It is speculated that structural alignment caused by stress developed during deposition of these films could be responsible for enhancement in magnetization.

Keywords

FerroelectricityFerromagneticFilm
Type
Articles
Information
Journal of Materials Research , Volume 22 , Issue 8 , August 2007 , pp. 2068 - 2073
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Fiebig, M.: Revival of the magnetoelectric effect. J. Phys. D: Appl. Phys. 38, R123 2005CrossRefGoogle Scholar
2Hill, N.A.: Why are there so few magnetic ferroelectrics? J. Phys. Chem. B 104, 6694 2000CrossRefGoogle Scholar
3Spaldin, N.A.Fiebig, M.: The renaissance of magnetoelectric multiferroics. Science 309, 391 2005CrossRefGoogle ScholarPubMed
4Wang, J., Neaton, J.B., Zheng, H., Nagarajan, V., Ogale, S.B., Liu, B., Viehland, D., Vaithyanathan, V., Schlom, D.G., Waghmare, U.V., Spaldin, N.A., Rabe, K.M., Wuttig, M.Ramesh, R.: Epitaxial BiFeO3 multiferroic thin film heterostructures. Science 299, 1719 2003CrossRefGoogle ScholarPubMed
5Bai, F., Wang, J., Wutting, M., Lee, J., Wang, N., Pyatakov, A.P., Zvezdin, A.K., Cross, L.C.Viehland, D.: Distribution of spin cycloid in (111) c-oriented BiFeO3 thin films by epitaxial constraint: Enhanced polarization and release of latent magnetization. Appl. Phys. Lett. 86, 032511 2005CrossRefGoogle Scholar
6Mathe, V.L., Patankar, K.K., Patil, R.N.Lokhande, C.D.: Synthesis and dielectric properties of Bi1−xNdxFeO3. J. Magn. Magn. Mater. 270, 380 2004CrossRefGoogle Scholar
7Lee, D., Kim, M.G., Ryu, S.Jang, H.M.: Epitaxially grown La modified BiFeO3 magnetoferroelectric thin films. Appl. Phys. Lett. 86, 222903 2005CrossRefGoogle Scholar
8Jiang, Q.Qiu, J.H.: The thickness dependence of ferroelectric and magnetic properties in epitaxial BiFeO3 thin films. J. Appl. Phys. 99, 103901 2006CrossRefGoogle Scholar
9Singh, S.K., Sato, K., Maruyama, K.Ishiwara, H.: Cr-doping effects toelectrical properties of BiFeO3 thin films formed by chemical solution deposition. Jpn. J. Appl. Phys. 45, L1087 2006CrossRefGoogle Scholar
10Wang, Y.Nan, C.: Enhanced ferroelectricity in Ti-doped multiferroic BiFeO3 thin films. Appl. Phys. Lett. 89, 052903 2006CrossRefGoogle Scholar
11Palkar, V.R., Kundaliya, D., Malik, S.K.Bhattacharya, S.: Magnetoelectricity at room temperature in Bi0.9−xTbxLa0.1FeO3 system. Phys. Rev. B 69, 212102 2004CrossRefGoogle Scholar
12Palkar, V.R., Kumara, K. GaneshMalik, S.K.: Observation of room temperature magnetoelectric coupling in pulsed laser deposited Bi0.6Tb0.3La0.1FeO3 thin films. Appl. Phys. Lett. 84, 2856 2004CrossRefGoogle Scholar
13Palkar, V.R., Kundaliya, D.C.Malik, S.K.: Process for manufacture of novel compound exhibiting magnetoelectric coupling and high dielectric constant at room temperature, Indian Patent Application No. 409/MUM/2003 (24 April 2003),Google Scholar
14Palkar, V.R., Purandare, S.C., Pai, S.P., Chattopadhyay, S., Apte, P.R., Pinto, R.Multani, M.S.: c-axis oriented ferroelectric thin films of PbTiO3 on Si by pulsed laser ablation. Appl. Phys. Lett. 68, 1582 1996CrossRefGoogle Scholar
15Yun, K.Y., Noda, M., Okuyama, M., Saeki, H., Tabata, H.Saito, K.: Structural and multiferroic properties of BiFeO3 thin films at room temperature. J. Appl. Phys. 96, 3399 2004CrossRefGoogle Scholar
16Palkar, V.R., John, J.Pinto, R.: Observation of saturated polarization and dielectric anomaly in magnetoelectric BiFeO3 thin films. Appl. Phys. Lett. 80, 1628 2002CrossRefGoogle Scholar