Microcantilever bending experiments in NiAl – Evaluation, size effects, and crack tip plasticity

Published online by Cambridge University Press:  26 September 2014

Johannes Ast ,
Thomas Przybilla ,
Verena Maier ,
Karsten Durst  and
Mathias Göken
Johannes Ast*
Affiliation:
Department of Material Science and Engineering, University of Erlangen-Nürnberg, Institute I, Erlangen 91058, Germany
Thomas Przybilla
Affiliation:
Department of Material Science and Engineering, University of Erlangen-Nürnberg, Institute VII, Erlangen 91058, Germany
Verena Maier
Affiliation:
Department of Materials Physics, University of Leoben, Leoben 8700, Austria; and Department of Material Science and Engineering, University of Erlangen-Nürnberg, Institute I, Erlangen 91058, Germany
Karsten Durst
Affiliation:
Department of Physical Metallurgy, Technical University of Darmstadt, Darmstadt 64287, Germany
Mathias Göken
Affiliation:
Department of Material Science and Engineering, University of Erlangen-Nürnberg, Institute I, Erlangen 91058, Germany
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

For a better understanding of the local fracture behavior of semi-brittle materials, we carried out bending experiments on notched microcantilevers of varying sizes in the micrometer range using NiAl single crystals. Smaller and larger beams were milled with a focused ion beam in the so-called “soft” <110> and “hard” <100> orientation and were tested in situ in a scanning electron microscope and ex situ with a nanoindenter, respectively. The measurements were evaluated using both linear-elastic fracture mechanics and elastic–plastic fracture mechanics. The results show that (i) the fracture toughness is in the same range as the macroscopically determined one which is around 3.5 MPa$\sqrt {\rm{m}}$ for the soft orientation and around 8.5 MPa$\sqrt {\rm{m}}$ for the hard orientation, that (ii) there is a strong influence of the anisotropic behavior of NiAl on the fracture toughness values, and that (iii) the J-integral technique is the most accurate quantification method.

Keywords

scanning electron microscopy (SEM)fractureion beam processing
Type
Articles
Information
Journal of Materials Research , Volume 29 , Issue 18 , 28 September 2014 , pp. 2129 - 2140
Copyright
Copyright © Materials Research Society 2014 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Uchic, M.D., Dimiduk, D.M., Florando, J.N., and Nix, W.D.: Sample dimensions influence strength and crystal plasticity. Science 305(5686), 986 (2004).CrossRefGoogle ScholarPubMed
Schaufler, J., Schmid, C., Durst, K., and Göken, M.: Determination of the interfacial strength and fracture toughness of a-C: H coatings by in-situ microcantilever bending. Thin Solid Films 522, 480 (2012).Google Scholar
Matoy, K., Detzel, T., Müller, M., Motz, C., and Dehm, G.: Interface fracture properties of thin films studied by using the micro-cantilever deflection technique. Surf. Coat. Technol. 204(6–7), 878 (2009).CrossRefGoogle Scholar
Kupka, D. and Lilleodden, E.T.: Mechanical testing of solid-solid interfaces at the microscale. Exp. Mech. 52(6), 649 (2012).Google Scholar
Wurster, S., Motz, C., and Pippan, R.: Characterization of the fracture toughness of micro-sized tungsten single crystal notched specimens. Philos. Mag. 92(14), 1803 (2012).CrossRefGoogle Scholar
Jaya B, N., Jayaram, V., and Biswas, S.K.: A new method for fracture toughness determination of graded (Pt,Ni)Al bond coats by microbeam bend tests. Philos. Mag. 92(25–27), 3326 (2012).CrossRefGoogle Scholar
Iqbal, F., Ast, J., Göken, M., and Durst, K.: In situ micro-cantilever tests to study fracture properties of NiAl single crystals. Acta Mater. 60(3), 1193 (2012).Google Scholar
Bergmann, G. and Vehoff, H.: Effect of environment on the brittle-to-ductile transition of pre-cracked NiAl single and polycrystals. Mater. Sci. Eng., A 192–193, 309 (1995).Google Scholar
Thome, F., Göken, M., and Vehoff, H.: Study of the fracture behavior in soft and hard oriented NiAl single crystals by AFM. Intermetallics 7(3), 491 (1999).CrossRefGoogle Scholar
Irwin, G.R.: Fracture (Springer Verlag, Berlin, Germany, 1958), pp. 551.Google Scholar
Demir, E., Roters, F., and Raabe, D.: Bending of single crystal microcantilever beams of cube orientation: Finite element model and experiments. J. Mech. Phys. Solids 58(10), 1599 (2010).CrossRefGoogle Scholar
E 399-490: Standard Test Method for Plane-Strain Fracture Toughness of Metallic Materials (ASTM International, West Conshohocken, PA, 1997).Google Scholar
E 1290-1302: Standard Test Method for Crack-Tip Opening Displacement (CTOD) Fracture Toughness Measurement (ASTM International, West Conshohocken, PA, 2002).Google Scholar
E 1820-1901: Standard Test Method for Measurement of Fracture Toughness (ASTM International, West Conshohocken, PA, 2001).Google Scholar
BS 5762: Methods for Crack Opening Displacement (COD) Testing (British Standards, London, UK, 1979).Google Scholar
Shih, C.F.: Relationships between the J-integral and the crack opening displacement for stationary and extending cracks. J. Mech. Phys. Solids 29(4), 305 (1981).CrossRefGoogle Scholar
Noebe, R.D., Bowman, R.R., and Nathal, M.V.: Physical and mechanical properties of the B2 compound NiAl. Int. Mater. Rev. 38(4), 193 (1993).CrossRefGoogle Scholar
Sih, G.C. and Liebowitz, H.: On the Griffith energy criterion for brittle fracture. Int. J. Solids Struct. 3(1), 1 (1967).Google Scholar
Chang, K-M., Darolia, R., and Lipsitt, H.A.: Cleavage fracture in B2 aluminides. Acta Metall. Mater. 40(10), 2727 (1992).Google Scholar
Durst, K., Backes, B., Franke, O., and Göken, M.: Indentation size effect in metallic materials: Modeling strength from pop-in to macroscopic hardness using geometrically necessary dislocations. Acta Mater. 54(9), 2547 (2006).Google Scholar
Tabor, D.: The Hardness of Metals (Oxford Univ. Press, Oxford, England, 1951), pp. 15.Google Scholar
Demir, E., Raabe, D., Zaafarani, N., and Zaefferer, S.: Investigation of the indentation size effect through the measurement of the geometrically necessary dislocations beneath small indents of different depths using EBSD tomography. Acta Mater. 57(2), 559 (2009).CrossRefGoogle Scholar
Miracle, D.B.: Overview No. 104: The physical and mechanical properties of NiAl. Acta Metall. Mater. 41(3), 649 (1993).Google Scholar
Göken, M., Vehoff, H., and Neumann, P.: Investigations of loaded crack tips in NiAl by atomic force microscopy. Scr. Metall. Mater. 33(7), 1187 (1995).CrossRefGoogle Scholar
Motz, C., Schöberl, T., and Pippan, R.: Mechanical properties of micro-sized copper bending beams machined by the focused ion beam technique. Acta Mater. 53(15), 4269 (2005).Google Scholar
Demir, E., Raabe, D., and Roters, F.: The mechanical size effect as a mean-field breakdown phenomenon: Example of microscale single crystal beam bending. Acta Mater. 58(5), 1876 (2010).CrossRefGoogle Scholar
Kiener, D., Motz, C., Rester, M., Jenko, M., and Dehm, G.: FIB damage of Cu and possible consequences for miniaturized mechanical tests. Mater. Sci. Eng., A 459(1–2), 262 (2007).Google Scholar
D 5934-6002: Standard Test Method for Determination of Modulus of Elasticity for Rigid and Semi-Rigid Plastic Specimens by Controlled Rate of Loading Using Three-Point Bending (ASTM International, West Conshohocken, PA, 2002).Google Scholar