Fatigue crack initiation at Nd-rich particles in an Nd containing high temperature titanium alloy

Published online by Cambridge University Press:  31 January 2011

J. F. Lei
Affiliation:
State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Academia Sinica, Shenyang 110015, People's Republic of China
Q. J. Wang
Affiliation:
State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Academia Sinica, Shenyang 110015, People's Republic of China
Y. Y. Liu
Affiliation:
State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Academia Sinica, Shenyang 110015, People's Republic of China
S. X. Guan
Affiliation:
State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Academia Sinica, Shenyang 110015, People's Republic of China
Z. G. Wang
Affiliation:
State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Academia Sinica, Shenyang 110015, People's Republic of China
D. Li
Affiliation:
State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Academia Sinica, Shenyang 110015, People's Republic of China
Z. Q. Hu
Affiliation:
State Key Laboratory for Fatigue and Fracture of Materials, Institute of Metal Research, Academia Sinica, Shenyang 110015, People's Republic of China
Get access

Abstract

Scanning electron microscopy (SEM) and surface replica method have been employed to study the micromechanism of fatigue crack initiation at Nd-rich phase particles in a high temperature titanium (Ti-55) alloy. It was found that the microcrack initiates near the equator of Nd-rich particles in the matrix. The microcrack grows first at an angle of about 45° with respect to the tensile axis, and then its growth direction becomes approximately normal to the tensile axis. The experimental results are analyzed in terms of the elastic stress distribution around soft particles imbedded in the matrix to account for the experimental findings of particle cracking and the associated surface microcrack initiation near the particle “equator.” A model of fatigue crack initiation at a soft surface particle is proposed.

Type
Articles
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Kung, C. Y. and Fine, M. E., Metall. Trans. 10A, 603 (1979).CrossRefGoogle Scholar
2.Lankford, J. and Kusenberger, F. N., Metall. Trans. 4A, 553 (1973).CrossRefGoogle Scholar
3.Lankford, J., Int. J. Fracture 12, 155 (1976).CrossRefGoogle Scholar
4.Morris, W. L., Buck, O., and Marcus, H. L., Metall. Trans. 7A, 1161 (1976).CrossRefGoogle Scholar
5.Chang, R., Morris, W. L., and Buck, O., Scripta Metall. 13, 191 (1979).CrossRefGoogle Scholar
6.Cummings, H. N., Stulen, F. B., and Schulte, W. C., ASTM Proceedings 58, 505 (1958).Google Scholar
7.Tanaka, K. and Mura, T., Metall. Trans. 13A, 117 (1982).CrossRefGoogle Scholar
8.Tanaka, K. and Mura, T., J. Appl. Mech. 48, 97 (1981).CrossRefGoogle Scholar
9.Li, D. and Liu, Y. Y., Titanium Science and Engineering, Proc. 6th Chinese Conference on Titanium (1987) (in Chinese), Vol. 2, p. 49.Google Scholar
10.Lei, J. F., Liu, Y. Y., Guan, S. X., Wang, Q. J., Wang, Z. G., Li, D., and Hu, Z. Q., unpublished.Google Scholar
11.Li, G. P., Ph.D. Dissertation, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, People's Republic of China (1995), p. 84.Google Scholar
12.Goodier, J. N., J. Appl. Mech. 1, 39 (1933).CrossRefGoogle Scholar
13.Melander, A., Int. J. Fatigue 12, 154 (1990).CrossRefGoogle Scholar