Density- and Hardness-optimized Pressureless Sintered and Post-hot Isostatic Pressed B4C

Published online by Cambridge University Press:  01 August 2005

Namtae Cho ,
Zhihao Bao  and
Robert F. Speyer
Namtae Cho
Affiliation:
School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332
Zhihao Bao
Affiliation:
School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332
Robert F. Speyer*
Affiliation:
School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Pressureless sintered B4C relative densities as high as 96.7% were obtained by optimizing the soak temperature, and holding at that temperature for the minimum time required to reach terminal density. Although the relative densities of pressureless sintered specimens were lower than that of commercially produced hot-pressed B4C, their (Vickers) hardness values were comparable. For 4.45-cm-diameter, 1.35-cm-high disk-shaped specimens, pressureless sintered to at least 93.0% relative density, post-hot isostatic pressing resulted in vast increases in relative densities (e.g., 100.0%) and hardness values significantly greater than that of commercially produced hot-pressed B4C.

Keywords

DensificationHardnessSintering
Type
Articles
Information
Journal of Materials Research , Volume 20 , Issue 8 , August 2005 , pp. 2110 - 2116
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Thevenot, F.: Boron carbide—A comprehensive review. J. Eur. Ceram. Soc. 6, 205 (1990).CrossRefGoogle Scholar
2Beauvy, J.: System B-C, solid state phase equilibria. J. Less-Common Met. 90, 169 (1983).CrossRefGoogle Scholar
3Emin, D.: Structure and single-phase regime of boron carbide. Phys. Rev. B 31, 6041 (1988).CrossRefGoogle Scholar
4Wilkins, M.L. Progress Report on Light Armor Program, Lawrence Livermore National Laboratory, 1969.CrossRefGoogle Scholar
5Viechnicki, D.J., Savin, M.L. and Iliman, M.I.: Am. Ceram. Soc. Bull. 70, 1035 (1991).Google Scholar
6Skorokhod, V. Jr.Vlajic, M.D. and Krstic, V.D.: Mechanical properties of pressureless sintered boron carbide containing TiB2 phase. J. Mater. Sci. Lett. 15, 1337 (1996).CrossRefGoogle Scholar
7Lee, C.H. and Kim, C.H.: Pressureless sintering and related reaction phenomena of Al2O3-doped B4C. J. Mater. Sci. 27, 6335 (1992).CrossRefGoogle Scholar
8Kanno, Y., Kawase, K. and Nakano, K.: Additive effect on sintering of boron carbide. J. Ceram. Soc. Jpn. 95, 1137 (1987).Google Scholar
9Zakhariev, Z. and Radev, D.: Properties of polycrystalline boron carbide sintered in the presence of W2B5 without pressing. J. Mater. Sci. Lett. 7, 695 (1988).CrossRefGoogle Scholar
10Schwetz, K. and Vogt, G.: Process for the production of dense sintered articles of boron carbide, U.S. Patent No. 4 195 066 (1980).Google Scholar
11Lee, H. and Speyer, R.F.: Pressureless sintering of boron carbide. J. Am. Ceram. Soc. 86, 1468 (2003).CrossRefGoogle Scholar
12Lee, H., Hackenberger, W.S. and Speyer, R.F.: Sintering of boron carbide heat-treated with hydrogen. J. Am. Ceram. Soc. 85, 2131 (2002).CrossRefGoogle Scholar
13Dole, S.L., Prochazka, S. and Doremus, R.H.: Microstructural coarsening during sintering of boron carbide. J. Am. Ceram. Soc. 72, 958 (1989).CrossRefGoogle Scholar
14German, R.M.: Sintering Theory and Practice (John Wiley and Sons, New York, 1996).Google Scholar
15Kuzenkova, M.A., Kislyi, P.S., Grabchuk, B.L. and Bodnaruk, N.I.: The structure and properties of sintered boron carbide. J. Less-Common Met. 67, 217 (1979).CrossRefGoogle Scholar
16Lee, H. and Speyer, R.F.: Hardness and fracture toughness of pressureless-sintered B4C. J. Am. Ceram. Soc. 85, 1291 (2002).CrossRefGoogle Scholar