Crack initiation and early growth behavior of TC4 titanium alloy under high cycle fatigue and very high cycle fatigue

Published online by Cambridge University Press:  08 January 2018

Wei Li ,
Ning Gao ,
Hongqiao Zhao  and
Xinxin Xing
Wei Li*
Affiliation:
School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China
Ning Gao
Affiliation:
School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China
Hongqiao Zhao
Affiliation:
School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China
Xinxin Xing
Affiliation:
School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

The crack initiation and early growth behaviors of a TC4 titanium alloy under high cycle fatigue and very high cycle fatigue were experimentally investigated. The results show that it exhibits the duplex S–N curve characteristics associated with surface and interior failures at a stress ratio of 0.1, while it represents the similar S–N curve characteristics only related to surface failure at a stress ratio of −1. The interior failure is accompanied with the occurrence of facets, granular bright facets (GBFs), and fisheye. Slip-like patterns are observable on the facets easily formed under positive stress ratio. The interior failure process is characterized as (i) occurrence of slip lines on partial α grains under cyclic loading, (ii) initiation and growth of microcracks within some α grains, (iii) coalescence of microcracks and formation of GBF, (iv) stable long crack growth within fisheye, (v) unstable crack growth outside fisheye, and (vi) final momentary fracture.

Keywords

fatiguemicrostructurenucleation and growth
Type
Article
Information
Journal of Materials Research , Volume 33 , Issue 8 , 27 April 2018 , pp. 935 - 945
Copyright
Copyright © Materials Research Society 2018 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

Contributing Editor: Jürgen Eckert

References

REFERENCES

Bathias, C.: There is no infinite fatigue life in metallic materials. Fatigue Fract. Eng. Mater. Struct. 22, 559 (1999).CrossRefGoogle Scholar
Berger, C., Schwerdt, D., and Pyttel, B.: Very high cycle fatigue—Is there a fatigue limit. Int. J. Fatigue 33, 49 (2011).Google Scholar
Bandara, C.S., Siriwardane, S.C., Dissanayake, U.I., and Dissanayake, R.: Fatigue failure predictions for steels in the very high cycle region—A review and recommendations. Eng. Failure Anal. 45, 421 (2014).CrossRefGoogle Scholar
McEvily, A.J., Nakamura, T., Oguma, H., Yamashita, K., Matsunaga, H., and Endo, M.: On the mechanism of very high cycle fatigue in Ti–6Al–4V. Scr. Mater. 59, 1207 (2008).CrossRefGoogle Scholar
Oguma, H. and Nakamura, T.: The effect of microstructure on very high cycle fatigue properties in Ti–6Al–4V. Scr. Mater. 63, 32 (2010).10.1016/j.scriptamat.2010.02.043CrossRefGoogle Scholar
Tschegg-Stanzl, S.E. and Mayer, H.: Fatigue and fatigue crack growth of aluminium alloys at very high numbers of cycles. Int. J. Fatigue 23, S231 (2001).10.1016/S0142-1123(01)00167-0CrossRefGoogle Scholar
Meischel, M., Tschegg-Stanzl, S.E., Arcari, A., Iyyer, N., Apetre, N., and Phan, N.: Constant and variable-amplitude loading of aluminum alloy 7075 in the VHCF regime. Procedia Eng. 101, 501 (2015).CrossRefGoogle Scholar
Mayer, H., Haydn, W., Schuller, R., Issler, S., Furtner, B., and Bacher-Hochst, B.: Very high cycle fatigue properties of bainitic high carbon–chromium steel. Int. J. Fatigue 31, 1300 (2009).CrossRefGoogle Scholar
Li, W., Sakai, T., Li, Q., and Wang, P.: Reliability evaluation on very high cycle fatigue property of GCr15 bearing steel. Int. J. Fatigue 32, 1096 (2010).CrossRefGoogle Scholar
Zhang, J.W., Song, Q.P., Zhang, N., Lu, L.T., Zhang, M.T., and Cui, G.D.: Very high cycle fatigue property of high-strength austempered ductile iron at conventional and ultrasonic frequency loading. Int. J. Fatigue 70, 235 (2015).CrossRefGoogle Scholar
Matsunaga, H., Sun, C., Hong, Y., and Murakami, Y.: Dominant factors for very-high-cycle fatigue of high-strength steels and a new design method for components. Fatigue Fract. Eng. Mater. Struct. 38, 1274 (2015).CrossRefGoogle Scholar
Bacher-Hoechst, M. and Issler, S.: Assessment of very high cycle fatigue effects in practical applications. Procedia Eng. 66, 26 (2013).CrossRefGoogle Scholar
Sakai, T., Takeda, M., Shiozawa, K., Ochi, Y., Nakajima, M., and Nakamura, T.: Experimental reconfirmation of characteristic S–N property for high carbon chromium bearing steel in wide life region in rotating bending. J. Soc. Mater. Sci., Jpn. 49, 779 (2000).CrossRefGoogle Scholar
Shiozawa, K., Lu, L., and Ishihara, S.: S–N curve characteristics and subsurface crack initiation behavior in ultra-long life fatigue of a high carbon-chromium bearing steel. Fatigue Fract. Eng. Mater. Struct. 24, 781 (2001).CrossRefGoogle Scholar
Makino, T.: The effect of inclusion geometry according to forging ratio and metal flow direction on very high-cycle fatigue properties of steel bars. Int. J. Fatigue 30, 1409 (2008).CrossRefGoogle Scholar
Pyttel, B., Brunner, I., Schwerdt, D., and Berger, C.: Influence of defects on fatigue strength and failure mechanisms in the VHCF-region for quenched and tempered steel and nodular cast iron. Int. J. Fatigue 41, 107 (2012).CrossRefGoogle Scholar
Bach, J., Höppel, H., Bitzek, B., and Göken, M.: Influence of specimen geometry on temperature increase during ultrasonic fatigue testing. Ultrasonics 53, 1412 (2013).CrossRefGoogle ScholarPubMed
Itoga, H., Tokaji, K., Nakajima, M., and Ko, H-N.: Effect of surface roughness on step-wise S–N characteristics in high strength steel. Int. J. Fatigue 25, 379 (2003).CrossRefGoogle Scholar
Li, W., Sakai, T., Li, Q., Lu, L.T., and Wang, P.: Effect of loading type on fatigue properties of high strength bearing steel in very high cycle regime. Mater. Sci. Eng., A 528, 5044 (2011).CrossRefGoogle Scholar
Pérez-Mora, R., Palin-Luc, T., Bathias, C., and Paris, P.C.: Very high cycle fatigue of a high strength steel under sea water corrosion: A strong corrosion and mechanical damage coupling. Int. J. Fatigue 74, 156 (2015).CrossRefGoogle Scholar
Shiozawa, K., Murai, M., Shimatani, Y., and Yoshimoto, T.: Transition of fatigue failure mode of Ni–Cr–Mo low-alloy steel in very high cycle regime. Int. J. Fatigue 32, 541 (2010).CrossRefGoogle Scholar
Yu, Y., Gu, J.L., Bai, B.Z., Liu, Y.B., and Li, S.X.: Very high cycle fatigue mechanism of carbide-free bainite/martensite steel micro-alloyed with Nb. Mater. Sci. Eng., A 527, 212 (2009).CrossRefGoogle Scholar
Xu, X.X., Yu, Y., Cui, W.L., Bai, B.Z., and Gu, J.L.: Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure. Int. J. Miner., Metall. Mater. 16, 285 (2009).CrossRefGoogle Scholar
Lutjering, G. and Gysler, A.: Titanium’ 84 Science and Technology, 1st ed. (Deutsche Gesellscheaft fur Metallkunde, Oberursel, Germany, 1984); p. 2065.Google Scholar
Nagai, K., Umezawa, O., Yuri, T., and Ishikawa, K.: Internal crack initiation in high cycle fatigue at cryogenic temperatures. Eng. Fract. Mech. 40, 957 (1991).CrossRefGoogle Scholar
Neal, D.F. and Blenkinsop, P.A.: Internal fatigue origin in α–β titanium alloys. Acta. Metall. 24, 59 (1976).CrossRefGoogle Scholar
Hack, J.E. and Leverant, G.R.: A model for hydrogen-assisted crack initiation on planar shear bands in near-alpha titanium alloys. Scr. Metall. 14, 437 (1980).CrossRefGoogle Scholar
Evans, W.J. and Bache, M.R.: The role of hydrogen in cyclic and dwell sensitive fatigue of a near alpha titanium alloy. In Seventh World Conference on Titanium, Froes, F.H. and Caplan, I., eds. (TMS, San Diego, California, 1993); p. 1693.Google Scholar
Bache, M.R.: A review of dwell sensitive fatigue in titanium alloys: The role of microstructure, texture and operating conditions. Int. J. Fatigue 25, 1079 (2003).CrossRefGoogle Scholar
Jha, S.K. and Chandran, S.R.: An unusual fatigue phenomenon: Duality of the S–N fatigue curve in the beta-titanium alloy Ti–10V–2Fe–3Al. Scr. Mater. 48, 1207 (2003).CrossRefGoogle Scholar
Steele, R.K. and McEvily, A.J.: High-cycle fatigue behavior of Ti–6Al–4V alloy. Eng. Fract. Mech. 8, 31 (1976).CrossRefGoogle Scholar
Ono, Y., Yuri, T., Sumiyoshi, H., Matsuoka, S., and Ogata, T.: Subsurface fracture in high-cycle fatigue at cryogenic temperatures in Ti–5% Al–2.5% Sn extra low interstitial alloy. Mater. Trans. 44, 1702 (2003).CrossRefGoogle Scholar
Bridier, F., Villechaise, P., and Mendez, J.: Slip and fatigue crack formation processes in an alpha/beta titanium alloy in relation to crystallographic texture on different scales. Acta Mater. 56, 3951 (2008).CrossRefGoogle Scholar
Peterson, R.E.: Stress Concentration Factors, 2nd ed. (John Wiley & Sons, New York, USA, 1974); p. 99.Google Scholar
Shiozawa, K., Lu, L.T., and Ishihara, S.: S–N curve characteristics and subsurface crack initiation behavior in ultra-long life fatigue of a high carbon-chromium bearing steel. Fatigue Fract. Eng. Mater. Struct. 24, 781 (2001).CrossRefGoogle Scholar
Pippan, R., Tabernig, B., Gach, E., and Riemelmoser, F.: Non-propagation conditions for fatigue cracks and fatigue in the very high-cycle regime. Fatigue Fract. Eng. Mater. Struct. 25, 805 (2002).CrossRefGoogle Scholar
Murakami, Y.: Metal Fatigue: Effects of Small Defects and Nonmetallic Inclusions, 1st ed. (Elsevier Science Ltd, Oxford, U.K., 2002); pp. 17, 22.Google Scholar