Nanostructured Barium Titanate Prepared Through a Modified Reverse Micellar Route: Structural Distortion and Dielectric Properties

Published online by Cambridge University Press:  01 June 2005

Tokeer Ahmad ,
Gnanasundaram Kavitha ,
Chandrabhas Narayana  and
Ashok K. Ganguli
Tokeer Ahmad
Affiliation:
Department of Chemistry, Indian Institute of Technology, Hauz Khas, New Delhi 110016, India
Gnanasundaram Kavitha
Affiliation:
Chemistry and Physics of Materials Unit, Jawaharlal Nehru Centre for Advanced Scientific Research, Bangalore 560064, India
Chandrabhas Narayana
Affiliation:
Chemistry and Physics of Materials Unit, Jawaharlal Nehru Centre for Advanced Scientific Research, Bangalore 560064, India
Ashok K. Ganguli*
Affiliation:
Department of Chemistry, Indian Institute of Technology, Hauz Khas, New Delhi 110016, India
*
a) Address all correspondence to this author.e-mail: [email protected]
Get access

Abstract

A modified and convenient route using microemulsions (avoiding Ba-alkoxide) was evolved for the synthesis of uniform and monodisperse nanoparticles of BaTiO3 at low temperature (800 °C). X-ray line broadening and transmission electron microscopy studies show that the particle size varies in the range of 20–25 nm. Evidence for tetragonal distortion was found in these nano-sized (20–25 nm) particles of barium titanate from careful x-ray diffraction studies as well as from Raman spectroscopy. Our study showed that the critical size of the cubic to tetragonal transition in barium titanate may be much lower than suggested theoretically. The grain size showed an increase on sintering of 35 nm at 900 °C to 120 nm at 1100 °C, which was much lower than the grain size obtained at this temperature by the normal solid state route. The dielectric constant depends on sintering temperature and was found to increase from 210 (900 °C sintering) to 520 (1100 °C sintering) at 100 kHz. The dielectric constant was highly stable with temperature as well as frequency.

Keywords

NanoparticleTransmission electron microscopy (TEM)
Type
Articles
Information
Journal of Materials Research , Volume 20 , Issue 6 , June 2005 , pp. 1415 - 1421
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Phule, P.P. and Risbud, S.H.: Low-temperature synthesis and processing of electronic materials in the BaO–TiO2 system. J. Mater. Sci. 25, 1169 (1990).CrossRefGoogle Scholar
2Potdar, H.S., Deshpande, S.B. and Date, S.K.: Alternative route for synthesis of barium titanyl oxalate: Molecular precursor for microcrystalline barium titanate powders. J. Amer. Ceram. Soc. 79, 2795 (1996).CrossRefGoogle Scholar
3Sekhar, M.A., Dhanraj, G., Bhat, H.L. and Patil, K.C.: Synthesis of fine-particle titanates by the pyrolysis of oxalate precursors. J. Mater. Sci. Mater. Electron. 3, 237 (1992).CrossRefGoogle Scholar
4Phule, P.P. and Risbud, S.H.: Sol-gel synthesis of barium titanate powders using barium acetate and titanium(IV) isopropoxide. Adv. Ceram. Mater. 3, 183 (1988).CrossRefGoogle Scholar
5Salze, H., Odier, P. and Cales, B.: Elaboration of fine micropowders from organometallic polymeric precursors. J. Non-Cryst. Solids 82, 314 (1986).CrossRefGoogle Scholar
6Kakihana, M., Arima, M., Nakamura, Y., Yashima, M. and Yoshimura, M.: Spectroscopic characterization of precursors used in the pechini-type polymerizable complex processing of barium titanate. Chem. Mater. 11, 438 (1999).CrossRefGoogle Scholar
7Kutty, T.R.N. and Balachandran, R.: Direct precipitation of lead zirconate titanate by the hydrothermal method. Mater. Res. Bull. 19, 1479 (1984).CrossRefGoogle Scholar
8Kandori, K., Kon-No, K. and Kitahara, A.: Formation of ionic water/oil microemulsions and their application in the preparation of calcium carbonate particles. J. Colloid Interface Sci. 122, 78 (1988).CrossRefGoogle Scholar
9Pileni, M.P., Motte, L. and Petit, C.: Synthesis of cadmium sulfide in situ in reverse micelles: Influence of the preparation modes on size, polydispersity, and photochemical reactions. Chem. Mater. 4, 338 (1992).CrossRefGoogle Scholar
10Chhabra, V., Lal, M., Maitra, A.N. and Ayyub, P.: Preparation of ultrafine high density gamma ferric oxide using aerosol OT microemulsions and its characterization. Colloid Polym. Sci. 273, 939 (1995).CrossRefGoogle Scholar
11Beck, C., Haartl, W. and Hempelmann, R.: Size-controlled synthesis of nanocrystalline BaTiO3 by a sol-gel type hydrolysis in microemulsion provided nanoreactors. J. Mater. Res. 13, 3174 (1998).CrossRefGoogle Scholar
12Herrig, H. and Hempelmann, R.: A colloidal approach to nanometer-sized mixed oxide ceramic powders. Mater. Lett. 27, 287 (1996).CrossRefGoogle Scholar
13Wang, J., Fang, J., Ng, S.C., Gan, L.M., Chew, C.H., Wang, X. and Shen, Z.: Ultrafine barium titanate powders via microemulsion processing routes. J. Am. Ceram. Soc. 82, 873 (1999).CrossRefGoogle Scholar
14Frey, M.H. and Payne, D.A.: Synthesis and processing of barium titanate ceramics from alkoxide solutions and monolithic gels. Chem. Mater. 7, 123 (1995).CrossRefGoogle Scholar
15Campion, J.F., Payne, D.A., Chae, H.K. and Xu, Z.: Chemical processing of barium titanate powders and thin layer dielectrics. Ceram. Trans. 22, 477 (1991).Google Scholar
16Ahmad, T. and Ganguli, A.K.: Synthesis of nanometer-sized particles of barium orthotitanate prepared through a modified reverse micellar route: Structural characterization, phase stability and dielectric properties. J. Mater. Res. 19, 2905 (2004).CrossRefGoogle Scholar
17Arya, P.R., Jha, P. and Ganguli, A.K.: Synthesis, characterization and dielectric properties of nanometer-sized barium strontium titanates prepared by the polymeric citrate precursor method. J. Mater. Chem. 13, 415 (2003).CrossRefGoogle Scholar
18Sood, A.K., Chandrabhas, N., Muthu, D.V.S. and Jayaraman, A.: Phonon interference in BaTiO3: High-pressure Raman study. Phys. Rev. B: Condens. Mater. 51, 8892 (1995).CrossRefGoogle ScholarPubMed
19Chaves, A., Katiyar, R.S. and Porto, S.P.S.: Coupled modes with A1 symmetry in tetragonal barium titanate(IV). Phys. Rev. B: Solid State 10, 3522 (1974).CrossRefGoogle Scholar
20Noma, T., Wada, S., Yano, M. and Suzuki, T.: Analysis of lattice vibration in fine particles of barium titanate single crystal including lattice hydroxyl group. J. Appl. Phys. 80, 5223 (1996).CrossRefGoogle Scholar
21Hayashi, T., Oji, N. and Maiwa, H.: Film-thickness dependence of dielectric properties of barium titanate thin films prepared by sol-gel method. Jpn. J. Appl. Phys. 33, 5227 (1994).CrossRefGoogle Scholar
22Begg, B.D., Finnie, K.S. and Vance, E.R.: Raman study of the relationship between room-temperature tetragonality and the curie point of barium titanate. J. Am. Ceram. Soc. 79, 2666 (1996).CrossRefGoogle Scholar
23Asiaie, R., Zhu, W., Akbar, S.A. and Datta, P.K.: Characterization of submicron particles of tetragonal BaTiO3. Chem. Mater. 8, 226 (1996).CrossRefGoogle Scholar
24Cho, W-S.: Structural evolution and characterization of BaTiO3 nanoparticles synthesized from polymeric precursor. J. Phys. Chem. Solids 59, 659 (1998).CrossRefGoogle Scholar
25Frey, M.H. and Payne, D.A.: Grain-size effect on structure and phase transformations of barium titanate. Phys. Rev. B: Condens. Matter 54, 3158 (1996).CrossRefGoogle ScholarPubMed
26Perry, C.H. and Hall, D.B.: Temperature dependence of the Raman spectrum of BaTiO3. Phys. Rev. Lett. 15, 700 (1965).CrossRefGoogle Scholar
27Uchino, K., Sadanaga, E. and Hirose, T.: Dependence of the crystal structure on particle size in barium titanate. J. Am. Ceram. Soc. 72, 1555 (1989).CrossRefGoogle Scholar
28Yen, F.S., Hsiang, H.I. and Chang, Y.H.: Cubic to tetragonal phase transformation of ultrafine BaTiO3 crystallites at room temperature. Jpn. J. Appl. Phys. 34, 6149 (1995).CrossRefGoogle Scholar
29Wang, Y.G., Zhong, W.L. and Zhang, P.L.: Size driven phase transition in ferroelectric particles. Solid State Comm. 90, 329 (1994).CrossRefGoogle Scholar
30Binder, K.: Surface effects on phase transitions in ferroelectrics and antiferroelectrics. Ferroelectrics 35, 99 (1981).CrossRefGoogle Scholar
31Tybell, T., Ahn, C.H. and Triscone, J.M.: Ferroelectricity in thin perovskite films. Appl. Phys. Lett. 75, 856 (1999).CrossRefGoogle Scholar
32Junquera, J. and Ghosez, P.: Critical thickness for ferroelectricity in perovskite ultrathin films. Nature 422, 506 (2003).CrossRefGoogle ScholarPubMed
33Fong, D.D., Stephenson, G.B., Streiffer, S.K., Eastman, J.A., Auciello, O., Fuoss, P.H. and Thompson, C.: Ferroelectricity in ultrathin films. Science 304, 1650 (2004).CrossRefGoogle Scholar