Diffraction Effects from Irradiated Aluminum Single Crystals*

Published online by Cambridge University Press:  06 March 2019

H. E. Kissinger
H. E. Kissinger*
Affiliation:
General Electric Company Richland, Washington
Get access

Abstract

The effect of substructural perfection on the accumulation of irradiation damage in aluminum was examined. Large single crystals with extensive substructure and crystals essentially free of substructure, all with faces cut parallel to crystal planes, were subjected to neutron irradiation. Subsequent examination by X-ray diffraction revealed pronounced changes in integrated intensity and Debye-Waller temperature factor for the substructure-free crystals; these effects disappeared upon re-etching of the surface. Laue photographs showed that the normal single-crystal pattern was partially obscured by a polycrystalline effect which also disappeared upon etching. Crystals with extensive substructure showed no such effects.

This diffraction evidence supports the view that irradiation-induced defects in aluminum migrate to and collect at the crystal surface if no internal trapping sites exist.

Type
Research Article
Information
Advances in X-Ray Analysis , Volume 6: Eleventh Annual Conference on Applications of X-ray Analysis, August 8-10, 1962 , 1962 , pp. 164 - 171
Copyright
Copyright © International Centre for Diffraction Data 1962

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

*

Work peiformed by the General Electric Company for the Atomic Energy Commission under Contract No. AT(45-1)-1350.

References

1. Warren, B. E., USAEC Reports, NYO3732, 19S2; NYO-6511, 1954.Google Scholar
2. McReynolds, A. W., W. Augustyniak, M. McKeown, and Rosenblatt, D. B., Phys. Rev. 98: 418, 1955.Google Scholar
3. Eridgman, P. W., Proc. Nat. Acad. Sci. 60: 306, 1925.Google Scholar
4. Noggle, T. S., Rev. Sci. Instr. 24: 184, 1953.Google Scholar
5. Noggle, T. S. and Koehler, J. S., Acta Met. 3: 260, 1955.Google Scholar
6. Fumas, T. C., Single Crystal Orienter Manual, General Electric Co., Milwaukee, Wisc., 1956, p. 96.Google Scholar
7. Eond, W. L., Acta Cryst., 13: 814, 1960.Google Scholar
8. Huang, K., Proc. Roy. Soc. (London) A190: 102, 1947.Google Scholar