X-Ray Profile Analysis of 12% Chromium Stainless Steel

Published online by Cambridge University Press:  06 March 2019

Zenjxo Yajima ,
Ken-ichi Ishikawa ,
Toshihiko Sasaki  and
Yukio Hirose
Zenjxo Yajima
Affiliation:
Department of Mechanical Engineering Kanazawa Institute of Technology 7-1 Oogigaoka, Nonoichi, Kanazawa 921, Japan
Ken-ichi Ishikawa
Affiliation:
Department of Mechanical Engineering Kanazawa Institute of Technology 7-1 Oogigaoka, Nonoichi, Kanazawa 921, Japan
Toshihiko Sasaki
Affiliation:
Department of Materials Science, Kanazawa University Kakuma-machi, Kanazawa 920-11, Japan
Yukio Hirose
Affiliation:
Department of Materials Science, Kanazawa University Kakuma-machi, Kanazawa 920-11, Japan
Get access

Extract

X-ray line broadening is caused by variations in lattice strain and small particle size. When hydrogen is introduced into the steel by the electrolytica! method, structural changes are observed. X-ray line broadening is a suitable measurement in such cases. The Warren and Averbach Fourier analysis is a good method for line broadening studies. In this method, strain and particle size effects can be separated because broadening due to particle size is independent of order of the diffraction peaks, while broadening due to strain is not.

Type
Research Article
Information
Advances in X-Ray Analysis , Volume 37: Forty-Second Annual Conference on Applications of X-ray Analysis, August 2-6, 1993 , 1993 , pp. 351 - 358
Copyright
Copyright © International Centre for Diffraction Data 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Yajima, Z., Kibayashi, Y., Hirose, Y. and Mura, T.. ‘The Effect of Hydrogen on the Stress Corrosion Cracking Susceptibility (if AISI 4340 Steel”. Advanced Technology in Experimental Mechanics, p. 281 (1991).Google Scholar
2. Yajima, Z., Tsuda, M.. Hirose, Y. and Tanaka, K., “Load- History Effect on Initiation on Stress Corrosion Cracking in High- Strength Steel”, Residual Stresses in Science and Technology, 2: 721, (1987).Google Scholar
3. Warren, B.E., “X-Ray Studies of Deformed Metals”, Progress in Metal physics, 8: 147, (1959).Google Scholar
4. Stokes, A.R., “A Numerical Fourier- analysis Method for the Correction of Widths and shapes of Lines on X- Ray Powder Photographs”. Proceedings of the Physical Society. 61: 382(1948).Google Scholar
5. Garrod, R.J. and Auld, J.H., “X- Ray Line Broadening from Cold- Worked Iron”, Acta Metallurgica, 3: 190(1955).Google Scholar
6. Baneijee, B.R., Capenos, J. M. and Hauser, J.J., ‘Arrested Quenching of 12 % Chromium Steels”, Transactions of The American Society for Metals. 58: 54, (1965).Google Scholar
7. Yajima, Z., Hirose, Y. and Ogawa, H., “EiTecl of Some Heat Treatment on Environmental Embrittlement of 12 % chromium Stainless Steel”. Memoirs of K.J.T., A 10: 65, (1978).Google Scholar
8. Yajima, Z., Tsuda, M., Hirose, Y. and Tanaka, K.. “Residual Stresses Near SCC Fracture Surfaces of AISI 4340 Steel” Advances in X-Ray Analysis, 32: 451, (1989).Google Scholar