This study evaluated the effect of fluoride solutions on surface roughness and morphology of composites in the short and long term. Specimens were randomly assigned to experimental groups (n=5) according to type of composite (nanofilled, microhybrid, microfilled) and immersion media (artificial saliva, 0.05% sodium fluoride solution, Fluordent Reach, Oral-B, and Fluorgard). Roughness was evaluated at time intervals: T0 after 24 h in artificial saliva (baseline); T60 after being in assigned immersion media for 1 min daily over 60 days; and Tfinal after artificial aging (20,000 thermal cycles, 1,200,000 mechanical loading cycles, and continuous immersion for 1,825 min). Surface morphology was qualitatively analyzed by scanning electron microscopy (SEM) at T60 and Tfinal. Roughness data were submitted to analysis of variance for mixed repeated measures, Sidak, and Tukey tests at α=0.05. Micro-filled resin showed the highest roughness values. Fluoride solutions had no influence on roughness. Higher roughness values were observed after artificial aging. In SEM observations after the artificial aging, the specimens showed surface degradation, irrespective of immersion medium or type of composite. Nano-filled resin showed higher loss of resin matrix and protrusion of filler particles. Roughness was not influenced by fluoride solutions; however, it is material dependent and increases over time.

This study evaluated the influence of fluoride mouth rinses and repolishing on the superficial morphology and color stability of nanofilled resin. About 150 specimens were prepared and polished using aluminum oxide discs for 15 s with a pressure of 2 kg. The experimental groups were divided according to the immersion medium (artificial saliva, 0.5% sodium fluoride, Fluordent Reach, Oral B, Fluorgard) and repolishing procedure (without and with). The specimens were continuously immersed for 1 week. Thereafter, half of each sample was repolished. A color reading was performed after 24 h of immersion in the artificial saliva baseline, after continuous immersion, and after repolishing. The superficial morphology was examined using scanning electron microscopy (SEM) in a qualitative way. Color change (∆E) data were submitted to a mixed analysis of variance using a Shapiro–Wilk test (p>0.05 for the different immersion media) and Sidak’s test (p<0.05 for the differences between groups). In the interaction between the repolishing and the immersion media, Fluorgard showed a statistical difference between the ∆E values with and without repolishing (p<0.0001). On the SEM observations, both Fluordent Reach and Fluorgard caused degradation of the superficial resinous matrix of the composite after continuous immersion. This matrix was removed after repolishing.

Our aim was to test the hypothesis that the use of mouthwashes, consumption of soft drinks, as well as the type of light curing unit (LCU), would change the surface roughness (Ra) and morphology of a nanofilled composite resin (Z350® 3M ESPE). Samples (80) were divided into eight groups: Halogen LCU, group 1, saliva (control); group 2, Pepsi Twist®; group 3, Listerine®; group 4, Colgate Plax®; LED LCU, group 5, saliva; group 6, Pepsi Twist®; group 7, Listerine®; group 8, Colgate Plax®. Ra values were measured at baseline, and after 7 and 14 days. One specimen of each group was prepared for scanning electron microscopy analysis after 14 days. The data were subjected to multifactor analysis of variance at a 95% confidence followed by Tukey's honestly significant difference post-hoc test. All the treatments resulted in morphological changes in composite resin surface, and the most significant change was in Pepsi Twist® groups. The samples of G6 had the greatest increase in Ra. The immersion of nanofilled resin in mouthwashes with alcohol and soft drink increases the surface roughness. Polymerization by halogen LCU (reduced light intensity) associated with alcohol contained mouthwash resulted in significant roughness on the composite.