The aim of this study was to investigate if load cycling affects interfacial integrity of glass ionomer cements bonded to sound- or caries-affected dentin. A conventional glass ionomer, Ketac Bond, and a resin-modified glass ionomer (Vitrebond Plus), were applied to dentin. Half of the specimens were load cycled. The interfaces were submitted to dye-assisted confocal microscopy evaluation. The unloaded specimens of sound and carious dentin were deficiently hybridized when Ketac Bond was used. Ketac Bond samples showed an absorption layer and an adhesive layer that were scarcely affected by fluorescein penetration (nanoleakage), in sound dentin. Nevertheless, a higher degree of micropermeability was found in carious dentin. In Ketac Bond specimens, load cycling improves the sealing capability and remineralization at the cement–dentin interface as porosity and nanoleakage was reduced. In contrast, samples treated with Vitrebond Plus exhibited a Rhodamine B-labeled absorption layer with scarce nanoleakage in both sound and carious unloaded dentin. The adhesive layer was affected by dye sorption throughout the porous cement–dentin interface. Samples treated with Vitrebond Plus had significant increases in nanoleakage and cement–dye sorption after load cycling. Within the limitations of an in vitro study, it is expected that conventional glass ionomers will provide major clinical efficacy when applied to carious-affected or sound dentin.

The thermal and mechanical behavior, the water uptake (WU), and water diffusion coefficient of sulfonated poly(ether ether ketone) (SPEEK) membranes annealed at 180 °C for different times were explored by high-resolution thermogravimetric analysis, mechanical tensile tests, dynamic mechanical analysis, and WU measurements. The mechanical and thermal stability increased with the thermal treatment time, i.e., with the degree of crosslinking. The effect of residual casting solvent, dimethyl sulfoxide (DMSO), on the WU within SPEEK was probed. In presence of residual DMSO, crosslinked SPEEK exhibited higher water sorption at low and medium relative humidity (RH), and lower water sorption at high RH. These membranes have properties well adapted to fuel cell applications.