The crystal structure of nechelyustovite, ideally Na4Ba2Mn1.5☐2.5Ti5Nb(Si2O7)4O4(OH)3F(H2O)6, a 5.447(1) Å, b 7.157(1) Å, c 47.259(9) Å, α 95.759(4)°, β 92.136(4)°, γ 89.978(4)°, V 1831.7(4) Å3, space group P, Z = 2, Dcalc. 3.041 g cm–3, from Lovozero alkaline massif, Kola Peninsula, Russia, has been solved and refined to R1 = 13.9% on the basis of 1745 unique reflections (Fo > 15σF). Electron microprobe analysis yielded the empirical formula (H20)6.01, Z = 2, calculated on the basis of 42 (O + F) a.p.f.u., H2O and OH are calculated from structure refinement (H2O = 6 p.f.u.; F + OH = 4 p.f.u.). The crystal structure of nechelyustovite is a combination of a TS (titanium silicate) block and an I (intermediate) block. The TS block consists of HOH sheets (H-heteropolyhedral, O-octahedral). The TS block exhibits linkage and stereochemistry typical for Group III (Ti = 3 a.p.f.u.) of Ti-disilicate minerals: two H sheets connect to the O sheet such that two (Si2O7) groups link to the trans edges of a Ti octahedron of the O sheet. There are two distinct TS blocks of the same topology, TS1 and TS2, that differ in the cations of the O sheet, [(Na1.5Mn1☐0.5)Ti] and [(Na2Mn0.5☐0.5)Ti] (4 a.p.f.u.) respectively. The TS1 and TS2 blocks have two different H sheets, H1,2 and H3,4, where (Si2O7) groups link to [5]- and [6]-coordinated (Ti,Nb) polyhedra respectively. There are three peripheral sites, AP(1—3), occupied mainly by Ba (less Sr and K) at 96, 86 and 26% and one peripheral site AP(4) occupied by Na at 50%. There are two I blocks: the I1 block is a layer of Ba atoms; the I2 block consists of H2O groups and AP(3) atoms. TS blocks alternate with I blocks or link through hydrogen bonds (as in epistolite). There is a sequence of four TS blocks and three I blocks per the c cell parameter: TS2 — I1 — TS1 — I2 — TS1 — I1 — TS2.

The crystal structure of mosandrite, ideally Na2Ca4REETi(Si2O7)2OF3, a = 7.4184(8), b = 5.6789(6), c = 18.873(2) Å, β = 101.410(2)°, V = 779.35(5) Å3, space group P21/c, Z = 2, Dcalc = 3.363 g.cm-3, from the type locality, Låven (Skådön), Langesundsfjorden, Larvik, Vestfold, Norway, has been refined to Ri = 6.33% on the basis of 1113 unique reflections F°≥4σF. Electron microprobe analysis gave the empirical formula Na1.99(Ca3.93Sr0.02)Σ3.95(Ce0.41La0.16Nd0.13Pr0.04Sm0.02Dy0.01Y0.13)Σ0.90 (Ti0.864+Nb0.08Zr0.05)Σ0.99(Si207)2(F1.20O0.80)Σ2.00F2, Z = 2, calculated on the basis of 18 (O + F) a.p.f.u.. The crystal structure of mosandrite is a framework of TS (titanium silicate) blocks. The TS block consists of HOH sheets (H-heteropolyhedral, O-octahedral). The TS block in mosandrite exhibits linkage and stereochemistry typical for Group I (Ti = 1 a.p.f.u.) Ti-disilicate minerals: two H sheets connect to the O sheet such that two (Si2O7) groups link to the trans edges of a Na polyhedron of the O sheet. The O sheet cations give Na(NaCa)Ti (4 a.p.f.u.). The TS blocks link via common vertices of (Si2O7) groups and common vertices and edges of Ca-dominant MH and Ap polyhedra. Two adjacent TS blocks are related by the glide plane cy. Composition and topology of the TS block in mosandrite and rinkite are identical. The crystal structure of mosandrite from the type locality is topologically and chemically identical to that of rinkite from the type locality of Kangerdluarssuk, Greenland.

The crystal structure of mosandrite, ideally (Ca3REE)[(H2O)2Ca0.5☐0.5]Ti(Si2O7)2(OH)2(H2O)2, from the Saga mine, Morje, Porsgrunn, Norway, has been refined as two components related by the TWIN matrix ( 0 0, 0 0, 1 0 1): a 7.4222(3), b 5.6178(2), c 18.7232(7) Å, β 101.4226(6)°, V = 765.23(9) Å3, space group P21/c, Dcalc. = 3.361 g.cm–3, R1 = 3.69% using 1347 observed (Fo > 4σF) reflections. The empirical formula of mosandrite (EMPA) was calculated on the basis of 4 Si a.p.f.u., with H2O determined from structure refinement: [(Ca2.89Ba0.01)Σ2.90(Ce0.39La0.18Nd0.14Sm0.02Gd0.03Y0.16Th0.03)Σ1.01Zr0.09]Σ4 [(H2O)2.00Ca0.32Na0.17Al0.10Mn0.04Fe2+0.02☐0.35]Σ3(Ti0.87Nb0.09Zr0.04)Σ1(Si2O7)2[(OH)1.54F0.46]Σ2[(H2O)1.50F0.50]Σ2, Z = 2. The crystal structure of mosandrite is a framework of TS (titanium silicate) blocks; each TS block consists of HOH sheets (H-heteropolyhedral, O-octahedral). In the TS block, there are five fully occupied cation sites, two [4]-coordinated Si sites with <Si–O> 1.623 Å , [7]-coordinated MH and AP sites occupied by Ca and REE in the ratio ∼3:1, and one [6]-coordinated Ti-dominant MO(1) site. There are two H2O-dominant H2O-alkali-cation sites. The partly occupied MO(2) site has composition [(H2O)0.5☐0.33Na0.17], ideally [(H2O)0.5☐0.5] p.f.u. The MO(3) site has ideal composition [(H2O)1.5Ca0.5] p.f.u. In the O sheet, the XOM and XOA anion sites have compositions [(OH)1.54F0.46] (XOM) and [(H2O)1.50F0.50] (XOA), ideally (OH)2 and (H2O)2 p.f.u. The MH and AP polyhedra and Si2O7 groups constitute the H sheet that is completely ordered. In the O sheet, MO(1) octahedra are long-range ordered whereas H2O and OH groups and alkali cations Na and Ca are long-range disordered. Two SRO (short-range ordered) arrangements have been proposed for the O sheet: (1) Na [MO(2)], Ca2 [MO(3)] and F4[XOM and XOA anion sites]; (2) 2 H2O [MO(2)] and MO(3)] and (OH)2 and (H2O)2 [XOM and XOA]. Linkage of H and O sheets occurs mainly via common vertices of MH polyhedra and Si2O7 groups and MO(1) octahedra. Two adjacent TS blocks are related by the glide plane cy. Mosandrite is an H2O- and OH-bearing Na- and Ca-depleted analogue of rinkite, ideally (Ca3REE)Na(NaCa) Ti(Si2O7)2(OF)F2. Mosandrite and rinkite are related by the following substitution at the MO(2,3) and XO(M,A) sites in the O sheet: M[(H2O)2 + ☐0.5] + X[(OH)–2 + (H2O)2] ↔ M[Na+2 + Ca2+0.5] + X[(OF)3– + (F2)2–].

Rinkite, ideally Na2Ca4REETi(Si2O7)2OF3, is a common mineral in alkaline and peralkaline rocks. The crystal structures of five rinkite crystals from three alkaline massifs: Ilimaussaq, Greenland; Khibiny, Kola Peninsula, Russia and Mont Saint-Hilaire, Canada, have been refined as two components related by the TWIN matrix (–1 0 0, 0 –1 0, 1 0 1) (Mo-αa radiation). The crystals, a = 7.4132-7.4414, b = 5.6595-5.6816, c = 18.8181-18.9431 Å, β = 101.353-101.424(2)°, V= 776.1-786.7 Å3, space group P21lc, Z = 2, Dcalc = 3.376—3.502 g cm–3, were analysed using an electron microprobe subsequent to collection of the X-ray intensity data. Transmission electron microscopy confirmed the presence of pseudomerohedral twinning in rinkite crystals. The crystal structure of rinkite is a framework of TS (titanium silicate) blocks. The TS block consists of HOH sheets (H-heteropolyhedral, O-octahedral). The TS block in rinkite exhibits linkage and stereochemistry typical for Group I (Ti = 1 a.p.f.u.) of Ti disilicate minerals: two H sheets connect to the O sheet such that two (Si2O7) groups link to the trans edges of a Na polyhedron of the O sheet. The crystal chemistry of rinkite and nacareniobsite-(Ce) is discussed.

This paper reports an infrared spectroscopic study of a set of sodalite-group minerals. The specimens have been identified using a combination of X-ray diffraction and microchemical analysis. As expected, the Si/Al ratio is ~1; the extra framework cation content is characterized by a well-defined Na ⇌ (Ca+K) substitution. The lattice parameters of the studied samples range from sodalite (sample LM11) with a = 8.889(2) Å, to haüyne (sample HR3S) with a = 9.1265(2) Å. The specimens, having the SO2– group as a dominant anion, show a clear correlation between the a cell edge and the K content. Singlecrystal FTIR spectroscopy shows that haüyne and nosean typically contain enclathrated CO2 molecules, inadditionto H2O and minor carbonate, while sodalite is virtually CO2-free. Detailed microspectrometric mappings show a non-homogeneous distribution of volatile constituents across the crystals, which may be related to the presence of fractures in the crystals. Because of such zoning, a relatively wide variation is observed when calibrating extinction coefficients on the basis of a bulk analytical method such as CHN elemental analysis.

The crystal structures of two polytypes of innelite, ideally Ba4Ti2Na2M2+Ti(Si2O7)2[(SO4) (PO4)]O2[O(OH)] where M2+ = Mn, Fe2+, Mg, Ca: innelite-1T, a 5.4234(9), b 7.131(1), c 14.785(3) Å, α 98.442(4), β 94.579(3), γ 90.009(4)°, V 563.7(3) Å3, space group P1̄, Dcalc = 4.028 g/cm3, Z = 1; and innelite-2M, a 5.4206(8), b 7.125(1), c 29.314(4) Å, 0 94.698(3)°, V 1128.3(2) Å3, space group P2/c, Dcalc.= 4.024 g/cm3, Z = 2, from the Inagli massif, Yakutia, Russia, have been refined to R values of 8.99 and 7.60%, respectively. Electron-microprobe analysis gave the empirical formula for innelite as (Ba3.94Sr0.06)Σ4.00(Na2.16Mn0.382+Fe2+0.17Mg0.15Ca0.10☐0.04)Σ3(Ti2.97Nb0.02Al0.02)Σ3.01Si4.01 (S1.02P0.81☐0.17)Σ2H1.84O25.79F0.21 which is equivalent to (Ba3.94Sr0.06)Σ4.00(Ti1.97Nb0.02Al0.02)Σ2.01 [(OH0.99F0.21)Σ1.20O0.80], calculated on the basis of 26 (O + F) anions, with H2O calculated from structure refinement. The crystal structure of innelite is a combination of a TS (titanium silicate) block and an I (intermediate) block. The TS block consists of HOH sheets (H-heteropolyhedral, O-octahedral) and exhibits linkage and stereochemistry typical for Ti-disilicate minerals of Group III (Ti = 3 a.p.f.u.): two H sheets connect to the O sheet such that two (Si2O7) groups link to the trans edges of a Ti octahedron of the O sheet. The I block contains T sites, statistically occupied by S and P, and Ba atoms. In the structures of innelite-1T and innelite-2M, TS blocks are related by an inversion centre and a cy glide plane, respectively. HRTEM images show a coherent intergrowth of the two polytypes, together with an as-yet unidentified ∼10 Å phase.

The crystal structures of lomonosovite, ideally Na10Ti4(Si2O7)2(PO4)2 O4, a = 5.4170(7) Å, b = 7.1190(9) Å, c = 14.487(2) Å, a = 99.957(3)°, β = 96.711(3)°, γ = 90.360(3)°, V= 546.28(4) Å3, Dcalc. = 3.175 g cm“3, and murmanite, ideally Na4Ti4(Si2O7)2O4(H2O)4, a = 5.3875(6) Å, b = 7.0579(7) Å, c = 12.176(1) Å, a = 93.511(2)°, 0 = 107.943(4)°, y = 90.093(2)°, V = 439.55(2) Å3, Dcalc. = 2.956 g.cm∼3, from the Lovozero alkaline massif, Kola Peninsula, Russia, have been refined in the space group P1̄ (Z = 1) to R values of 2.64 and 4.47%, respectively, using 4572 and 2222 observed |F°≥ 4σF| reflections collected with a single-crystal Bruker AXS SMART APEX diffractometer with a CCD detector and Mo-Kα. radiation. Electron microprobe analysis gave empirical formulae for lomonosovite (Na9.50Mn0.16Ca0.11)Σ9.77(Ti4+2.83Nb0.51Mn0.272+Zr0.11Mg0.11Fe2+0.10Fe3+0.06Ta0.01)Σ4.00(Si2.02O7)2(P0.98O4)2(O3.50F0.50)Σ4, Z = 1, calculated on the basis of 22(O+F) a.p.f.u., with H2O determined from structure refinement and Fe3+/(Fe2++Fe3+) ratios obtained by Mössbauer spectroscopy. The crystal structures of lomonosovite and murmanite are a combination of a titanium silicate (TS) block and an intermediate (I) block. The TS block consists of HOH sheets (H-heteropolyhedral, O-octahedral), and is characterized by a planar cell based on translation vectors, t1 and t2, with t1\ ∼5.5 and t2 ∼7 Å and ttA t2 close to 90°. The TS block exhibits linkage and stereochemistry typical for Group IV (Ti = 4 a.p.f.u.) of the Ti disilicate minerals: two H sheets connect to the O sheet such that two (Si2O7) groups link to Ti polyhedra of the O sheet adjacent along tx. In murmanite and lomonosovite, the invariant part of the TS block is of composition Na4Ti4(Si2O7)2O4. There is no evidence of vacancy-dominant cation sites or (OH) groups in the O sheet of lomonosovite or murmanite. In lomonosovite, the I block is a framework of Na polyhedra and P tetrahedra which gives 2[Na3 (PO)4] p.f.u. In murmanite, there are four (H2O) groups in the intermediate space between TS blocks. In lomonosovite, TS and I blocks alternate along c. In murmanite, TS blocks are connected via hydrogen bonding. The H atoms were located and details of the hydrogen bonding are discussed.

The crystal structure of bornemanite, ideally Na6☐BaTi2Nb(Si2O7)2(PO4)O2(OH)F, a = 5.4587(3), b = 7.1421(5), c = 24.528(2) Å, α = 96.790(1), β = 96.927(1), γ = 90.326(1)°, V = 942.4(2) Å3, space group (P1̄), Z = 2, Dcalc. = 3.342 g cm–3, from the Lovozero alkaline massif, Kola Peninsula, Russia, has been solved and refined to R1 = 6.36% on the basis of 4414 unique reflections (Fo >4sF). Electron microprobe analysis yielded the empirical formula (Na6.07Mn2+0.23Ca0.06☐0.64)Σ7.00 (Ba0.73K0.13Sr0.06☐0.08)Σ1.00(Ti2.05Nb0.80Zr0.02Ta5+0.01Fe3+0.03Al0.02Mn2+0.06Mg0.01)Σ3.00(Si2O7)2(P0.97O4)O2 [F1.27(OH)0.74]Σ2.01. The crystal structure of bornemanite is a combination of a TS (titanium silicate) block and an I (intermediate) block. The TS block consists of HOH sheets (H-heteropolyhedral, O-octahedral). The TS block exhibits linkage and stereochemistry typical for Group III (Ti = 3 a.p.f.u.) of Ti-disilicate minerals: two H sheets connect to the O sheet such that two (Si2O7) groups link to the trans edges of a Ti octahedron of the O sheet. The O sheet cations give Na3Ti (4 a.p.f.u.). The TS block has two different H sheets, H1 and H2, where (Si2O7) groups link to [5]Ti and [6]Nb polyhedra, and there are two peripheral sites which are occupied by Ba and Na, respectively. There are two I blocks: the I1 block is a layer of Ba atoms; the I2 block consists of Na polyhedra and (PO4) tetrahedra.

The crystal structure of vigrishinite, ideally NaZnTi4(Si2O7)2O3(OH)(H2O)4, a murmanite-group mineral of the seidozerite supergroup from the type locality, Mt. Malyi Punkaruaiv, Lovozero alkaline massif, Kola Peninsula, Russia, was refined in space group C$\bar 1$, a = 10.530(2), b = 13.833(3), c = 11.659(2) Å, α = 94.34(3), β = 98.30(3), γ = 89.80(3)°, V = 1675.5(2.1) Å3 and R1 = 12.52%. Based on electron-microprobe analysis, the empirical formula calculated on 22 (O + F), with two constraints derived from structure refinement, OH + F = 1.96 pfu and H2O = 3.44 pfu, is: (Na0.67Zn0.21Ca0.05□1.07)Σ2 (Zn0.86□1.14)Σ2(Zn0.14□0.36)Σ0.5(Ti2.60Nb0.62Mn0.30${\rm Fe}_{{\rm 0}{\rm. 23}}^{{\rm 2 +}} $Mg0.10Zr0.06Zn0.05Al0.03Ta0.01)Σ4(Si4.02O14) [O2.60(OH)1.21F0.19]Σ4[(H2O)3.44(OH)0.56]Σ4{Zn0.24P0.03K0.03Ba0.02} with Z = 4. It seems unlikely that constituents in the {} belong to vigrishinite itself. The crystal structure of vigrishinite is an array of TS blocks (Titanium Silicate) connected via hydrogen bonds. The TS block consists of HOH sheets (H = heteropolyhedral and O = octahedral) parallel to (001). In the O sheet, the Ti-dominant MO(1,2) sites, Na-dominant MO(3) and □-dominant MO(4) sites give ideally Na□Ti2 pfu. In the H sheet, the Ti-dominant MH(1,2) sites, Zn-dominant AP(1) and vacant AP(2) sites give ideally Zn□Ti2 pfu. The MH and AP(1) polyhedra and Si2O7 groups constitute the H sheet. The ideal structural formula of vigrishinite of the form ${\rm A}_{\rm 2}^{P} {\rm M}_{\rm 2}^{\rm H} {\rm M}_{\rm 4}^{\rm O} $(Si2O7)2(${\rm X}_{\rm M}^{\rm O} $)2(${\rm X}_{\rm A}^{\rm O} $)2(${\rm X}_{{\rm M,A}}^{P} $)4 is Zn□Ti2Na□Ti2(Si2O7)2O2O(OH)(H2O)4. Vigrishinite is a Zn-bearing, Na-poor and OH-rich analogue of murmanite, ideally Na2Ti2Na2Ti2(Si2O7)2O2O2(H2O)4. Murmanite and vigrishinite are related by the following substitution: H(${\rm Na}_{\rm 2}^{\rm +} $)mur + O(Na+)mur + O(O2–)mur ↔ H(Zn2+)vig + H(□)vig + O(□)vig + O[(OH)–]vig. The doubling of the t1 and t2 translations of vigrishinite compared to those of murmanite is due to the order of Zn and □ in the H sheet and Na and □ in the O sheet of vigrishinite.

The crystal structure and chemical formula of zvyaginite, ideally Na2ZnTiNb2(Si2O7)2O2(OH)2(H2O)4, a lamprophyllite-group mineral of the seidozerite supergroup from the type locality, Mt. Malyi Punkaruaiv, Lovozero alkaline massif, Kola Peninsula, Russia have been revised. The crystal structurewas refined with a new origin in space group C1, a = 10.769(2), b = 14.276(3), c = 12.101(2) Å, α = 105.45(3), β = 95.17(3), γ = 90.04(3)°, V = 1785.3(3.2) Å3, R1 = 9.23%. The electron-microprobe analysis gave the following empirical formula [calculated on 22 (O + F)]: (Na0.75Ca0.09K0.04□1.12)Σ2 (Na1.12Zn0.88Mn0.17Fe2+0.04□0.79)Σ3 (Nb1.68Ti1.25Al0.07)Σ3 (Si4.03O14)O2 [(OH)1.11F0.89]Σ2(H2O)4, Z = 4. Electron-diffraction patterns have prominent streaking along c* and HRTEM images show an intergrowth of crystalline zvyaginite with two distinct phases, both of which are partially amorphous. The crystal structure of zvyaginite is an array of TS (Titanium-Silicate) blocks connected via hydrogen bonds between H2O groups. The TS block consists of HOH sheets (H = heteropolyhedral, O = octahedral) parallel to (001). In the O sheet, the [6]MO(1,4,5) sites are occupied mainly by Ti, Zn and Na and the [6]MO(2,3) sites are occupied by Na at less than 50%. In the H sheet, the [6]MH(1,2) sites are occupied mainly by Nb and the [8]AP(1) and [8]AP(2) sites are occupied mainly by Na and □. The MH and AP polyhedra and Si2O7 groups constitute the H sheet. The ideal structural formula is Na□Nb2NaZn□Ti(Si2O7)2O2(OH)2(H2O)4. Zvyaginite is a Zn-bearing and Na-poor analogue of epistolite, ideally (Na□)Nb2Na3Ti(Si2O7)2O2(OH)2(H2O)4. Epistolite and zvyaginite are related by the following substitution in the O sheet of the TS-block: (Naþ 2 )epi↔Zn2+ zvy +□zvy. The doubling of the t1 and t2 translations of zvyaginite relative to those of epistolite is due to the order of Zn and Na along a (t1) and b (t2) in the O sheet of zvyaginite.