Electron-beam-induced soft-X-ray emission spectroscopy (SXES) that uses a grating spectrometer has been introduced to a conventional scanning electron microscope (SEM) for characterizing desired specimen areas of bulk materials. The spectrometer was designed as a grazing incidence flat-field optics by using aberration corrected (varied line spacing) gratings and a multichannel plate detector combined with a charge-coupled device camera, which has already been applied to a transmission electron microscope. The best resolution was confirmed as 0.13 eV at Mg L-emission (50 eV), which is comparable with that of recent dedicated electron energy-loss spectroscopy instruments. This SXES-SEM instrument presents density of states of simple metals of bulk Mg and Li. Apparent band-structure effects have been observed in Si L-emission of Si wafer, P L-emission of GaP wafer, and Al L-emissions of intermetallic compounds of AlCo, AlPd, Al2Pt, and Al2Au.

Image pre-processing is highly significant in automated analysis of microscopy images. In this work, non-uniform illumination correction has been attempted using the surface fitting method (SFM), multiple regression method (MRM), and bidirectional empirical mode decomposition (BEMD) in digital microscopy images of tuberculosis (TB). The sputum smear positive and negative images recorded under a standard image acquisition protocol were subjected to illumination correction techniques and evaluated by error and statistical measures. Results show that SFM performs more efficiently than MRM or BEMD. The SFM produced sharp images of TB bacilli with better contrast. To further validate the results, multifractal analysis was performed that showed distinct variation before and after implementation of illumination correction by SFM. Results demonstrate that after illumination correction, there is a 26% increase in the number of bacilli, which aids in classification of the TB images into positive and negative, as TB positivity depends on the count of bacilli.

Transmission electron microscopy (TEM) is an important tool for studies in cell biology, and is essential to address research questions from bacteria to animals. Recent technological innovations have advanced the entire field of TEM, yet classical techniques still prevail for most present-day studies. Indeed, the majority of cell and developmental biology studies that use TEM do not require cutting-edge methodologies, but rather fast and efficient data generation. Although access to state-of-the-art equipment is frequently problematic, standard TEM microscopes are typically available, even in modest research facilities. However, a major unmet need in standard TEM is the ability to quickly prepare and orient a sample to identify a region of interest. Here, I provide a detailed step-by-step method for a positional correlative anatomy approach to flat-embedded samples. These modifications make the TEM preparation and analytic procedures faster and more straightforward, supporting a higher sampling rate. To illustrate the modified procedures, I provide numerous examples addressing research questions in Caenorhabditis elegans and Drosophila. This method can be equally applied to address questions of cell and developmental biology in other small multicellular model organisms.

Correlative electron tomography and atom probe tomography have been carried out successfully on the same region of a commercial 8090 aluminum alloy (Al-Li-Mg-Cu). The combination of the two techniques allows accurate geometric reconstruction of the atom probe tomography data verified by crystallographic information retrieved from the reconstruction. Quantitative analysis of the precipitate phase compositions and volume fractions of each phase have been obtained from the atom probe tomography and electron tomography at various scales, showing strong agreement between both techniques.

A solid solution of Nd1−xSrxCoO3−δ (with x=0, 1/3, 2/3, and 1) has been prepared and characterized by a combination of X-ray diffraction, electron microscopy, and electron energy-loss spectroscopy (EELS). The structural characterization indicates that Nd-doped materials present an orthorhombic symmetry with a=√2xap, b=√2xap, and c=2xap (ap refers to lattice parameter of simple cubic perovskite), while SrCoO2.5 has an orthorhombic symmetry with a=√2xap, b=4xap, and c=√2xap. EELS analysis revealed that Co are in 3+ oxidation states but in different spin configurations.

In this paper, the process of pushing rough cylindrical micro/nanoparticles on a surface with an atomic force microscope (AFM) probe is investigated. For this purpose, the mechanics of contact involving adhesion are studied first. Then, a method is presented for estimating the real area of contact between a rough cylindrical particle (whose surface roughness is described by the Rumpf and Rabinovich models) and a smooth surface. A dynamic model is then obtained for the pushing of rough cylindrical particles on a surface with an AFM probe. Afterwards, the process is simulated for different particle sizes and various roughness dimensions. Finally, by reducing the length of the cylindrical particle, the simulation condition is brought closer to the manipulation condition of a smooth spherical particle on a rough substrate, and the simulation results of the two cases are compared. Based on the simulation results, the critical force and time of manipulation diminish for rough particles relative to smooth ones. Reduction in the aspect ratio at a constant cross-section radius and the radius of asperities (height of asperities based on the Rabinovich model) results in an increase in critical force and time of manipulation.

The introduction of gases, such as water vapor, into an environmental scanning electron microscope is common practice to assist in the imaging of insulating or biological materials. However, this capability may also be exploited to introduce, or form, liquid phase precursors for electron-beam-induced deposition. In this work, the authors report the deposition of silver (Ag) and copper (Cu) structures using two different cell-less in situ deposition methods—the first involving the in situ hydration of solid precursors and the second involving the insertion of liquid droplets using a capillary style liquid injection system. Critically, the inclusion of surfactants is shown to drastically improve pattern replication without diminishing the purity of the metal deposits. Surfactants are estimated to reduce the droplet contact angle to below ~10°.

We combine two scanning electron microscopy techniques to investigate the influence of dislocations on the light emission from nitride semiconductors. Combining electron channeling contrast imaging and cathodoluminescence imaging enables both the structural and luminescence properties of a sample to be investigated without structural damage to the sample. The electron channeling contrast image is very sensitive to distortions of the crystal lattice, resulting in individual threading dislocations appearing as spots with black–white contrast. Dislocations giving rise to nonradiative recombination are observed as black spots in the cathodoluminescence image. Comparison of the images from exactly the same micron-scale region of a sample demonstrates a one-to-one correlation between the presence of single threading dislocations and resolved dark spots in the cathodoluminescence image. In addition, we have also obtained an atomic force microscopy image from the same region of the sample, which confirms that both pure edge dislocations and those with a screw component (i.e., screw and mixed dislocations) act as nonradiative recombination centers for the Si-doped c-plane GaN thin film investigated.

Complex, electrochemically driven transport processes form the basis of electrochemical energy storage devices. The direct imaging of electrochemical processes at high spatial resolution and within their native liquid electrolyte would significantly enhance our understanding of device functionality, but has remained elusive. In this work we use a recently developed liquid cell for in situ electrochemical transmission electron microscopy to obtain insight into the electrolyte decomposition mechanisms and kinetics in lithium-ion (Li-ion) batteries by characterizing the dynamics of solid electrolyte interphase (SEI) formation and evolution. Here we are able to visualize the detailed structure of the SEI that forms locally at the electrode/electrolyte interface during lithium intercalation into natural graphite from an organic Li-ion battery electrolyte. We quantify the SEI growth kinetics and observe the dynamic self-healing nature of the SEI with changes in cell potential.

Surface topography and work function maps were simultaneously obtained for carbon surfaces modified by a dendritic molecule: 3,5-Bis (3,5-dinitrobenzoylamino) benzoic acid. The dendrons were spontaneously assembled onto highly ordered pyrolytic graphite samples, exhibiting an increase in the surface potential. This fact is consistent with the incorporation of an electron-acceptor functional group that remains electroactive on the surface.

The impact of lubricants on pole-tip recession and surface morphology of hard disk drive heads in the precision lapping process was investigated with atomic force microscopy, scanning electron microscopy, and auger electron spectroscopy. In particular, the effects of deionized water, hydrocarbon oil, ethanediol, isopropanol, and ethanol lubricants were evaluated. The results reveal that proper selection of lubricant is critical for achieving optimal performance in the lapping process. A mixture of 68% hydrocarbon oil, 30% isopropanol, and 2% octadecenoic acid was found to yield the most favorable results, displaying a writer shield recession, first shield of reader recession, and surface roughness of 0.423, 0.581, and 0.242 nm, respectively.

The study uses microscopy to analyze damage caused to the ovaries of a fresh water fish, Cyprinus carpio L., owing to its exposure to municipal wastes in a polluted reservoir, Umiam in Meghalaya, India. Histological analysis of the ovary showed atretic oocytes, detached ovarian wall, detached follicular linings, and necrosis of nuclei. Scanning electron microscopy revealed deformed oocytes with a rough and distorted surface. Transmission electron microscopy showed a poorly developed chorion, presence of relatively less electron-dense materials as compared with control, multinucleation in some cells surrounding the oocytes, and distorted and condensed mitochondria. The importance of microscopy in its different forms in analyzing histological, surface microstructural and fine structural damage to fish ovaries in response to environmental pollution owing to municipal wastes and city garbage is discussed with the help of available literature.

Direct in situ visualization of nanoparticles in a liquid is an important challenge of modern electron microscopy. The increasing significance of bottom-up methods in nanotechnology requires a direct method to observe nanoparticle interactions in a liquid as the counterpart to the ex situ electron microscopy and indirect scattering and spectroscopy methods. Especially, the self-assembly of anisometric nanoparticles represents a difficult task, and the requirement to trace the route and orientation of an individual nanoparticle is of highest importance. In our approach we utilize scanning transmission electron microscopy under environmental conditions to visualize the mobility and self-assembly of cetyltrimethylammonium bromide (CTAB)-capped gold nanorods (AuNRs) in an aqueous colloidal solution. We directly observed the drying-mediated AuNR self-assembly in situ during rapid evaporation of a colloidal droplet at 4°C and pressure of about 900 Pa. Several types of final AuNR packing were documented including side-by-side oriented chains, tip-to-tip loosely arranged nanorods, and domains of vertically aligned AuNR arrays. The effect of local heating by electron beam is used to qualitatively asses the visco-elastic properties of the formed AuNR/CTAB/water membrane. Local heating induces the dehydration and contraction of a formed membrane indicated either by its rupture and/or by movement of the embedded AuNRs.