In recent years, tissue engineering has helped to reduce hospital stays and deaths caused by skin wounds. Scaffolds are one of the main factors that influence the success of any tissue graft. Collagen is one of the main components of the extracellular matrix, and there has been much interest in new sources for application as a biomaterial. In this work, a tissue engineering scaffold was developed using the electrospinning technique. The chicken skin was used as an alternative source to obtain collagen. The combination of this collagen with elastin was successfully electrospun, and a distribution of diameters was obtained, less than 100 nm. In vitro tests showed the adhesion and proliferation of the cells, as well as an absence of cytotoxicity from non–cross-linked scaffolds and scaffolds that were cross-linked with carbonyldiimidazole. The structure and composition of the developed scaffolding provide a favorable environment for cell growth and generating a skin substitute.

In recent years, biomaterial investigators have increasingly focused their research on hydrogels and their capability to be fabricated into tissue engineering scaffolds. Although several fabrication methods have been used to produce hydrogel scaffolds, those methods are unable to routinely produce three-dimensional submicron and nanoscale scaffolds with precise control of the geometry, a crucial factor necessitated by the recent developments in the field of tissue engineering. Femtosecond laser-induced two-photon polymerization is a promising technique that fulfills these requirements. In our work, we used a femtosecond laser to fabricate three-dimensional submicron-scale scaffolds with poly(ethylene glycol) (PEG). The modulus, dimensions, and shape of the scaffold can be readily adjusted by changing both the laser parameters and the molecular weight of the PEG prepolymer. With the femtosecond laser, we also fabricated two-dimensional topographical patterns, which have important applications in basic biological research. To improve the throughput of femtosecond laser fabrication, we integrated the femtosecond direct-write process with a nano-imprint process by which the femtosecond laser is used to produce nano-patterned molds. We then carried out nanoimprinting to transfer the nanofeatures in the mold to the hydrogel in a massively parallel fashion.

This paper reports the development of a biodegradable porous scaffold made from naturally derived chitosan and alginate polymers for bone tissue engineering. The scaffold has a 3-D interconnected porous structure and was fabricated through thermally induced phase separation. The mechanical test showed that the scaffold has compressive strength of 0.46 ± 0.02 MPa — about 4 times that of the pure chitosan scaffold. The cell-material interaction study indicated that osteoblast cells seeded on the chitosan-alginate scaffold attach and proliferate well. The mineral deposition occurred after 3 days of culture and formed large chunks after 7 days. The chitosan-alginate scaffold was also found to have desirable swelling property and was structurally stable in solutions of different pH. The chitosan-alginate scaffold can be prepared from solutions of neutral pH allowing growth factors to be incorporated homogeneously into the scaffold for sustained release. This research demonstrated a technique by which a polymer-based biodegradable scaffold can be made to have high porosity up to 92% and excellent mechanical and biological properties.