Synthesis and structure of two phosphates belonging to the ternary Sb2O5-Fe2O3-P2O5 system are reported. Structures of both SbV1.50FeIII0.50(PO4)3 and (SbV0.50FeIIIe0.50)P2O7 phases, obtained by solid state reaction in air atmosphere at 950 °C and 900 °C, respectively, were determined at room temperature from X-ray powder diffraction using the Rietveld method. Sb1.50Fe0.50(PO4)3 phosphate belongs to the Nasicon-type structure with R32 space group. Hexagonal cell parameters are ahex.=8.305(1) Å and chex.=22.035(2) Å. Rietveld refinement results show a 2-2 ordered distribution, along the c-axis, of X(1) and X(2) sites (crystallographic formula [Sb0.88Fe0.12]X(1)[Fe0.38Sb0.62]X(2)(PO4)3) in the Nasicon framework. (Sb0.50Fe0.50)P2O7 is isotypic with β-SbP2O7 pyrophosphate [Pna21 space group; a=7.865(1) Å, b=15.699(2) Å, c=7.847(1) Å]. Its crystal structure is built up from corner-shared SbO6 or FeO6 octahedra and P2O7 groups (two group types). Each P2O7 group shares its six vertices with three SbO6 and three FeO6 octahedra, and each octahedra is connected to six P2O7 groups. A quasi 1-1 ordered distribution, along the b-axis, of Sb5+ and Fe3+ ions in the pyrophosphate framework are observed.

Synthesis and structure of two phosphates belonging to the ternary Sb2O5–In2O3–P2O5 system are realized. Structures of SbV1.50InIII0.50(PO4)3 and (SbV0.50InIII0.50)P2O7 phases, obtained by solid state reaction in air at 950 °C, were determined at room temperature from X-ray powder diffraction using the Rietveld method. SbV1.50InIII0.50(PO4)3 have a monoclinic (space group P21/n) distortion of the Sc2(WO4)3-type framework. Its structure is constituted by corner-shared SbO6 or InO6 octahedra and PO4 tetrahedra. Monoclinic unit cell parameters are a=11.801(2) Å, b=8.623(1) Å, c=8.372(1) Å, and β=90.93(1)°. (Sb0.50In0.50)P2O7 is isotypic with (Sb0.50Fe0.50)P2O7 and crystallizes in orthorhombic system (space group Pna21) with a=7.9389(1) Å, b=16.0664(2) Å, and c=7.9777(1) Å. Its structure is built up from corner-shared SbO6 or InO6 octahedra and P2O7 groups (two group-types). Each P2O7 group shares its six vertices with three SbO6 and three InO6 octahedra, and each octahedron is connected to six P2O7 groups.