Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Improved mechanical performance and wear resistance of Ti-coated cBN–WC–Ni composites

  • Changchun Lv, Xiaoyong Ren, Chengbiao Wang, Zhijian Peng
  • Journal:
    Journal of Materials Research / Volume 34 / Issue 22 / 28 November 2019
    Published online by Cambridge University Press:
    22 October 2019, pp. 3844-3852
    Print publication:
    28 November 2019

  • Composites of 0–20 vol% Ti-coated cBN (cBN@Ti) particles dispersed in WC–Ni were densified by spark plasma sintering under 50 MPa at 1300 °C. The cBN particles were distributed homogeneously with a Ti-rich interfacial layer between the cBN particles and WC–Ni matrix. Increasing cBN@Ti to 20 vol% decreased the sample densification, but all the composites were still >97.5% dense. The Vickers hardness and flexural strength initially increased and then decreased, reaching the maximum values of 1820 HV10 with 15 vol% cBN@Ti and 1500 MPa with 5 vol% cBN@Ti, respectively, whereas the fracture toughness KIC gradually increased from 8 to 13 MPa m1/2. For cutting rocks, the wear significantly decreased with 5–15 vol% cBN@Ti but increased with 20 vol% cBN@Ti because of cBN particles pull-out.