In our previous work [1] we investigated the impact of cold-crystallization on the structure of nanocomposites of PVDF with Lucentite STN™ OMS and observed the crossover composition in which the crystallographic beta phase dominated over alpha phase. Here, melt crystallization of PVDF/OMS nanocomposites was studied in the range of 0 to 1.0 wt% of OMS. In crystallization from melt, a decrease in crystallinity index occurs as a result of an increase in OMS. While beta phase fraction increased with an increase of OMS content in the range of interest, the amount of alpha crystals was found to be dominant even at high OMS compositions. At 1.0 wt% of OMS, beta crystals had reached at most 30% of the total crystallinity. Polarizing optical microscopy (POM) studies showed smaller, less birefringent spherulites with higher melting temperature compared to alpha spherulites appeared with OMS addition. Growth rate of these weakly birefringent spherulites is smaller than that of the strongly birefringent alpha spherulites. The increase in size and amount of the weakly birefringent spherulites with an increase of OMS and their higher melting point suggests these spherulites may be in the beta crystallographic phase.