A Devonian weathering profile was developed near the contact of Riphean dolostone containing disseminated carbonate-fluorapatite and intensively pyritized black shales. Samples from the profile were investigated by XRF, SEM, electron microprobe and ion microprobe. Rock-forming minerals are apatite, diaspore, chlorite and kaolinite, while accessory minerals are svanbergite, anatase, pyrite and zircon.

Primary marine carbonate-fluorapatite is represented by extremely weathered crystals concentrated near the footwall. Dissolution of apatite and pyrite provided an acidic environment that is expressed in the formation of S-rich apatite and svanbergite. The environment allowed Ti migration which formed anatase in weathered apatite grains. Coupled substitution Na+ + S6+ = Ca2+ + P5+ is suggested in S-rich apatite. A large volume of dissolved carbonate rocks was a source of Sr necessary for svanbergite formation. Apatite of the third generation formed at the final stage of weathering is represented by small (10—30 μm) very well shaped crystals.

A Th-rich mineral of the crandallite group has been investigated from the weathering profile of the Schugorsk bauxite deposit, Timan, Russia. It occurs within thin (up to 0.5 mm) organic-rich veinlets together with ‘leucoxene’ in the form of small shapeless grains which vary in size from 1—2 mm to 60—70 mm. Rare grains disseminated among boehmite crystals were also found. Microprobe analyses determined that the ThO2 content can be as high as 18 wt.%. The mineral composition is intermediate between crandallite CaAl3H(PO4)2(OH)6, goyazite SrAl3H(PO4)2(OH)6, Th-crandallite and svanbergite SrAl3PO4SO4(OH)6 in the beudantite group.

Comparatively high contents of Fe and Si and a very high positive Th and Fe content correlation (r = +0.98) suggest that the formula of the hypothetical Th-bearing end-member is ThFe3(PO4,SiO4)2(OH)6 with Th and Si substituting for REE and Prespectively (woodhouseite-type substitution). Another possible substitution is Th4+ + Ca2+ ⇋ 2REE3+ (florencite-type). A deficiency of cations in the X site can be explained by either the presence of carbon, undetectable by microprobe, in the crystal lattice or a lack of X-site cations due to radiation damage induced by Th. Some excess of cations in the B site (Al and Fe3+) can be explained by the presence of very small boehmite and hematite inclusions on the crandallite grain surfaces. Th-rich crandallite may be the result of alteration of an unidentified silicate mineral from the parent rock with a composition close to the simplified formula Fe2+ThSiO4(OH)2.