Surface modification treatments, such as the plasma nitriding improve the tribological properties of AISI 420 stainless steel; however, the corrosion resistance is deteriorated. The DLC (Diamond-Like Carbon) coatings were not only having a low friction coefficient but also good wear and corrosion resistance. In this work, both the corrosion behavior and the adhesion of the DLC hard coating, deposited on nitrided and non-nitrided AISI 420 stainless steel substrates, were studied. The coatings were characterized by means of EDS and Raman. In addition, nitrided layer microstructure and the coatings were analyzed by SEM-FIB and XRD. Corrosion behavior was evaluated by the salt spray fog test and cyclic potentiodynamic polarization tests in NaCl solution. The adhesion was assessed using Rockwell indentation and scratch tests. The a-C:H film and nitrided layer thicknesses were about 2.5 μm and 11 μm respectively. The nitrided layer improved adhesion in both tests. The coated AISI 420 stainless steel proved to have excellent atmospheric corrosion resistance and a passive behavior over 1 V (versus SCE) in the electrochemical tests. The adhesion and the corrosion performance were improved when the coating was deposited after the plasma nitriding treatment.

Austenitic 316L stainless steel can be used for orthopedic implants due to its biocompatibility and high corrosion resistance. Its range of applications in this field could be broadened by improving its wear and friction properties. Surface properties can be modified through surface hardening treatments. The effects of such treatments on the microstructure of the alloy were investigated here. Surface Mechanical Attrition Treatment (SMAT) is a surface treatment that enhances mechanical properties of the material surface by creating a thin nanocrystalline layer. After SMAT, some specimens underwent a plasma nitriding process to further enhance their surface properties. Using electron backscatter diffraction, transmission Kikuchi diffraction, energy dispersive spectroscopy, and transmission electron microscopy, the microstructural evolution of the stainless steel after these different surface treatments was characterized. Microstructural features investigated include thickness of the nanocrystalline layer, size of the grains within the nanocrystalline layer, and depth of diffusion of nitrogen atoms within the material.