In this study, the mechanism of ferrite grain refinement during warm compression deformation in the (γ + α) region of Cu–P–Cr–Ni–Mo weathering steel was analyzed by optical microscopy and electron backscatter diffraction. Results showed that fine equiaxed ferrite grains surrounded by high-angle boundaries (HABs) formed along the initial boundaries as the strain is increased. As the deformation temperature decreased, some low-angle boundaries shifted to HABs in intragranular ferrite, and ferrite grain refinement was promoted by continuous dynamic recrystallization. Microstructural observations also indicated that the fine ferrite grains of approximately 1.4–3 μm in size can be obtained by deformation at 750 °C with a strain over 0.69 because of ferrite dynamic recrystallization. Moreover, both strain and deformation temperature influenced the ferrite grain size and volume fraction. Thus, the predominant mechanism for ferrite grain refinement in the (γ + α) region was continuous dynamic recrystallization.

Les alliages ferritiques Fe-8 %Al possèdent des propriétés physiques et mécaniques prometteuses pour le développement et la conception de nouveaux types d’aciers allégés. Ces alliages présentent cependant des défauts de surface appelés « roping », apparaissant après l’étape d’emboutissage à froid. La formation de ces défauts est principalement attribuée à la distribution hétérogène des orientations des grains. Dans cette étude, les effets de la quantité de déformation, de la vitesse de déformation et de la température ont été examinés en utilisant la torsion à chaud. Les essais ont été réalisés à des températures comprises entre 900 °C et 1100 °C et des vitesses de déformation comprises entre 0,1 s-1 et 10 s-1. Il a été montré que deux types de recristallisation dynamique pouvaient intervenir durant la déformation à chaud : la recristallisation dynamique continue et la recristallisation dynamique discontinue.