Xenotime-(Y), (Y,REE)PO4, and thortveitite, (Sc, Y)2Si2O7, in a miarolitic cavity in a niobium, yttrium, fluorine (NYF) granitic pegmatite at Baveno, Verbania, Southern Alps, Italy, were investigated by electron microprobe analysis and single-crystal X-ray diffraction. Fluorine has an important role as a complexing agent for Y and REEs in supercritical pegmatitic fluids; annitesiderophyllite and chamosite are the most likely sources of the Y and REEs. The thortveitite from Baveno contains up to 3.20 wt.% SnO2, an unusually high Sn content. Xenotime-(Y) is enriched in Gd in comparison to other Alpine xenotimes. Quantitative chemical data and measurements of the lattice parameters show that a higher scandium content results in a smaller unit-cell volume in thortveitite. The substitution of REEs for Y up to ∼20 mol.% has little effect on the unit cell of xenotime-(Y). The textures of xenotime-(Y) and thortveitite provide information about the dissolution and crystallization processes in the miarolitic cavity.

Pilawite-(Y), ideally Ca2(Y,Yb)2Al4(SiO4)4O2(OH)2, was discovered in a pegmatite near Piława Górna, Lower Silesia, Poland. The mineral occurs as white, translucent, brittle crystals up to 1.5 mm in size. It has a white streak, vitreous lustre and a hardness of 5 on Mohs scale. The calculated density is 4.007 g/cm3. Pilawite-(Y) is non-pleochroic, biaxial (+), with refractive indices α = 1.743(5), β = 1.754(5) and γ = 1.779(5), birefringence Δ = 0.03–0.04, 2Vmeas. = 65(2)° and 2Vcalc. = 68°. Pilawite-(Y) is monoclinic P21/c, with unit-cell parameters a = 8.558(3) Å, b = 7.260(3) Å, c = 11.182(6) Å, β = 90.61(4)o, V = 694.7(4) Å3. The crystal structure was refined to an R1 index of 2.76% and consists of chains of edge- and corner-sharing octahedra decorated by tetrahedra and having the stoichiometry [Al2(SiO4)4O(OH)] that link by sharing corners to form an octahedron–tetrahedron framework with large interstices that contain Ca2+ and (Y,Ln)3+. It is a graphical isomer of the Al–P framework in palermoite, Sr2Li4[Al2(PO4)2(OH)2]2. The pilawite-(Y)-bearing assemblage began crystallization at high Y + Ln activities and was modified progressively by a Ca-enriched fluid, resulting in the sequence: keiviite-(Y) → gadolinite-(Y) to hingganite-(Y) + hellandite-(Y) → pilawite-(Y) → allanite-(Y) → epidote/zoisite.

Żabińskiite, ideally Ca(Al0.5Ta0.5)(SiO4)O, was found in a Variscan granitic pegmatite at Piława Górna, Lower Silesia, SW Poland. The mineral occurs along with (Al,Ta,Nb)- and (Al,F)-bearing titanites, a pyrochlore-supergroupmineral and a K-mica in compositionally inhomogeneous aggregates, ∼120 μm × 70 μm in size, in a fractured crystal of zircon intergrown with polycrase-(Y) and euxenite-(Y). Żabińskiite is transparent, brittle, brownish, with a white streak, vitreous lustre and a Mohs hardness of ∼5. The calculated density for the refined crystal is equal to 3.897 g cm–3, but depends strongly on composition. The mineral is non-pleochroic, biaxial (–), with mean refractive indices ≥1.89. The (Al,Ta,Nb)-richest żabińskiite crystal,(Ca0.980Na0.015)∑=0.995(Al0.340Fe3+0.029Ti0.298V0.001Zr0.001Sn0.005Ta0.251Nb0.081)∑=1.005[(Si0.988Al0.012)O4.946F0.047(OH)0.007)∑=5.000];60.7 mol.% Ca[Al0.5(Ta,Nb)0.5](SiO4)O; is close in composition to previously described synthetic material. Żabińskiite is triclinic (space group symmetry A1) and has unit-cell parameters a = 7.031(2) Å, b = 8.692(2) Å,c = 6.561(2) Å, α = 89.712(11)°, β = 113.830(13)°, γ = 90.352(12)° and V = 366.77 (11) Å3. It is isostructural with triclinic titanite and bond-topologically identical with titanite and other minerals of the titanite group.Żabińskiite crystallized along with (Al,Ta,Nb)-bearing titanites at increasing Ti and Nb, and decreasing Ta activities, almost coevally with polycrase-(Y) and euxenite-(Y) from Ca-contaminated fluxed melts or early hydrothermal fluids.