The capabilities of X-ray powder diffraction (XRD), infrared absorption (IR), solid-state magicangle-spinning nuclear magnetic resonance (MAS-NMR), and chemical dissolution methods were assessed for estimating the amount of noncrystalline material in a ground kaolinite. The Georgia kaolinite was ground in a mechanical mortar for various lengths of time to produce a set of ground samples containing different amounts of the resulting noncrystalline material. In the XRD method, the intensities of characteristic reflections at 7.2 and 4.47 Å did not respond proportionally to the amount of crystalline kaolinite. Although a transmission-type X-ray diffraction method using the hk reflection gave a slightly better estimate than the reflection-type X-ray diffraction method using the basal reflection, both methods gave overestimated values for the amount of noncrystalline material. This overestimation may have been caused by a masking effect due to coaggregation. Using the characteristic IR absorption band at 3700 cm-1 underestimated the amount of the noncrystalline material, if the proportion of this material <50%.

Extraction with NaOH gave estimations 15 to 20% greater than extraction with alkaline Tiron, except for the sample ground for 24 hr, for which both extractions indicated the presence of about 50% noncrystalline material. X-ray powder diffraction data of the residues after these extractions indicated that they consisted of crystalline kaolinite. 29Si NMR spectra of samples ground for ≥ 30 hr suggested that SiO4 tetrahedra were considerably distorted.27 Al NMR spectra showed a signal for tetrahedral A1 for the sample ground for 10 hr, which increased with an increase in grinding time. Plots of the Al(IV)/[Al(IV) + Al(VI)] ratios vs. time were similar to those of chemical extraction curves. Inasmuch as extraction with hot 0.5 M NaOH is a rather harsh treatment, the composition of the noncrystalline material must have been similar to that of the crystalline kaolinite. The chemical dissolution using alkaline Tiron appeared to be superior to other methods, such as XRD, IR, and NaOH extraction, for estimating the amount of noncrystalline material in kaolinite.

The structural damage produced by dry grinding and acid leaching of chrysotile was studied by transmission and scanning electron microscopy, infrared spectroscopy, X-ray powder diffraction, and thermogravimetric analysis. Severe dry grinding converted the chrysotile fibers into fragments having strong potential basic reaction sites. These sites were immediately neutralized by molecules present in the atmosphere (e.g., H2O, CO2). Acid leaching transformed the chrysotile fibers into very porous, non-crystalline silica, which was easily fractured into short fragments. The damage produced in the chrysotile structure by grinding or leaching was assessed by monitoring the intensity of various infrared absorption bands.

Alteration of the crystal structure of Mulhacén antigorite caused by dry, vibration grinding was investigated by X-ray diffraction (XRD), infrared spectroscopy (IR), thermal analyses (TG), grain-size distribution, and transmission and analytical electron microscopy (TEM, AEM). Grinding for 1 min reduces particles to a size ideal for IR and TG. With prolonged grinding, XRD and electron diffraction patterns showed that the crystal structure was affected mainly along the c axis, causing a partial loss of crystallinity. TG analyses revealed that vibration grinding modified mineral dehydration, accelerating the dehydroxylation process and transforming the structural OH to adsorbed water in the resulting matrix. IR spectra and AEM showed that grinding affected the tetrahedral sheet to a lesser extent than the octahedral sheet. Partial release of Mg by preferential destruction of the octahedral sheet after 10 min grinding produced an increase in the Si/Mg ratio in semi-crystalline particles, whereas the amorphous material product after 120 min showed the same composition as the initial antigorite. TEM and grain-size distribution results revealed that grinding led to a general decrease in particle size at the beginning of the experiment followed by the agglomeration of ultrafine particles as grinding proceeded.