Anisotropic Microstructure and Hydrogen Permeability of Nb-Ti-Ni Duplex Phase Alloy Prepared by Hot Forging-Rolling Technique

Published online by Cambridge University Press:  26 February 2011

Sho Tokui ,
Kazuhiro Ishikawa  and
Kiyoshi Aoki
Sho Tokui
Affiliation:
[email protected], Kitami Institute of Technology, Materials Science, Koen-cho 165, Kitami, 090-8507, Japan, +81-26-9449
Kazuhiro Ishikawa
Affiliation:
[email protected], Kitami Institute of Technology, Materials Science, Koen-cho 165, Kitami, 090-8507, Japan
Kiyoshi Aoki
Affiliation:
[email protected], Kitami Institute of Technology, Materials Science, Koen-cho 165, Kitami, 090-8507, Japan
Get access

Abstract

It has been demonstrated that the as-cast Nb40Ti30Ni30 duplex phase alloy, which consists of the primary (Nb, Ti) solid solution and the fine lamellar type eutectic {TiNi+(Nb, Ti)} phase, shows higher hydrogen permeability ¶ than that of pure Pd without the hydrogen embrittlement at 673K. In this alloy, the eutectic phase contributes to the suppression of the hydrogen embrittlement, while the primary one does mainly to the hydrogen permeation. It is important to note that even if the eutectic microstructure disappears and is replaced by the small spherical (Nb, Ti) phase embedded in the TiNi matrix by rolling and subsequent annealing, its high hydrogen permeability and large resistance to the hydrogen embrittlement are sustained. Furthermore, the present authors have observed that the primary (Nb, Ti) phase is largely elongated along the rolling direction. Consequently, it is expected that rolled and annealed Nb-Ti-Ni alloys show the large anisotropy of the microstructure and the hydrogen permeability. In the present work, the microstructure and hydrogen permeability ¶nof the Nb40Ti30Ni30 alloy after rolling and annealing treatments are examined in order to develop highly hydrogen permeable alloys utilizing the anisotropic microstructure.

The primary (Nb, Ti) phase and the very fine eutectic {TiNi+(Nb, Ti)} phase are observed in the as-cast Nb40Ti30Ni30 alloy by scanning electron microscopy (SEM). The X-ray diffractometry (XRD) indicates that this alloy consists of the B2-TiNi intermetallic compounds and the bcc- (Nb, Ti) solid solution. The primary (Nb, Ti) phase is largely elongated along the rolling direction by forging and subsequent rolling at 1173 K. On the other hand, the eutectic microstructure becomes unclear with increasing the rolling reduction. The composite alloys in which the (Nb, Ti) phase is elongated along to the rolling direction are obtained by 69 % rolling reduction. ¶n of this sample is four times higher than that of as-cast one. On the other hand, ¶ for the sample vertical to the rolling direction is reduced to about one third of that of as-cast one. Thus, the hydrogen permeability of the Nb40Ti30Ni30 alloy varies about ten times or more depending on the direction of the primary¡]Nb, Ti¡^ phase. We conclude that it is possible to produce highly hydrogen permeable Nb-Ti-Ni alloys using the anisotropy of the microstructure prepared by hot forging and rolling.

Keywords

purificationmicrostructurealloy
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 980: Symposium II – Advanced Intermetallic-Based Alloys , 2006 , 0980-II05-54
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Kikuchi, E., Catalysis Today 56, 97 (2000).Google Scholar
2. Nishimura, C., Komaki, M., Hwang, S., and Amano, M., J.Alloys and Compd. 330, 902 (2002).10.1016/S0925-8388(01)01648-6Google Scholar
3. Hara, S., Hatakeyama, N., Itoh, N., Kimura, H.-M. and Inoue, A., J. Membrane Sci. 211, 149 (2003).Google Scholar
4. Yamaura, S., Shimpo, Y., Okouchi, H., Nishida, M., Kajita, O., Kimura, H., Inoue, A., Mater. Trans. 44, 1885 (2003).Google Scholar
5. Hashi, K., Ishikawa, K., Matsuda, T. and Aoki, K., J.Alloys and Compd. 368, 215 (2004).Google Scholar
6. Hashi, K., Ishikawa, K., Matsuda, T. and Aoki, K., Mater. Trans. 46, 1026 (2005).Google Scholar
7. Hashi, K., Ishikawa, K., Matsuda, T. and Aoki, K., J.Alloys and Compd. 404, 273 (2005).10.1016/j.jallcom.2005.02.085Google Scholar
8. Luo, W., Ishikawa, K. and Aoki, K., J.Alloys and Comp. 406, 115 (2006).Google Scholar
9. Tokui, S., Ishikawa, K. and Aoki in, K.Defect Properties and Processing of The Hydrogen Cycle-Generation, Storage and Fuel Cells, edited by A., Dillon, C., Filiou and J., Ohi, (Mater. Res. Soc. Symp. Proc. 885, Pittsburgh, PA, 2006) pp. 245–250.Google Scholar