Effect of oxygen deficiency on Charge Ordering in La0.5Ca0.5MnO3-δ

Published online by Cambridge University Press:  02 July 2020

J. Tao ,
N. Jiang  and
J.C.H. Spence
J. Tao
Affiliation:
Physics Department, Arizona State University, Tempe, AZ85287-1504
N. Jiang
Affiliation:
Physics Department, Arizona State University, Tempe, AZ85287-1504
J.C.H. Spence
Affiliation:
Physics Department, Arizona State University, Tempe, AZ85287-1504
Get access

Abstract

Elastically-filtered transmission electron diffraction patterns of La0.5Ca0.5MnO3-δ have been obtained between 105K to 288K using the Leo 912 Omega. On heating La0.5Ca0.5MnO3 undergoes a transition from antiferromagnetic insulator to ferromagnetic metal (TN ∼ 150K) and then to paramagnetic insulator (Tc ∼ 230K) . The q modulation wave vector along the b-axis direction arises from charge ordering of Mn3+ and Mn4+, and orbital ordering of dz22 orbitals associated with Jahn-Teller distortions in the Mn3+O6 octahedra at low temperature. Both the intensity and the position of superlattice peaks change as a function of temperature during heating. The large incommensurability we see between 105K to 260K differs from that seen previously and proposed model. Figure 1 a) shows the lattice constants a, b, c related to the simple perovskite lattice parameters ap (ap ∼ 3.9Å) by a≈b≈ap and c≈2ap, and indicates the octahedral coordination.

Type
Diffraction Techniques in TEM and SEM
Information
Microscopy and Microanalysis , Volume 7 , Issue S2: Proceedings: Microscopy & Microanalysis 2001, Microscopy Society of America 59th Annual Meeting, Microbeam Analysis Society 35th Annual Meeting, Long Beach, California August 5-9, 2001 , August 2001 , pp. 376 - 377
Copyright
Copyright © Microscopy Society of America 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Schiffer, P., et al. Phys. Rev. Lett. 75, 3336 (1995).CrossRefGoogle Scholar
2.Radaelli, P.G., et al. Phys. Rev. B 55, 3015 (1997).CrossRefGoogle Scholar
3. Chen, C.H. and Cheong, S-W., Phys. Rev. Lett. 76, 4042 (1996).CrossRefGoogle Scholar
4.Li, J.Q., et al. Phys. Rev. Lett. 82, 2386 (1999).CrossRefGoogle Scholar
5.Barnabe, A., et al. J. Appl. Phys. 84, 5506 (1998).CrossRefGoogle Scholar
6.Hyde, B. and Andersen, S. Inorganic Crystal Sructures Wiley.(1989)Google Scholar
7. Supported by NSF award DMR9973894.Google Scholar