Phase Analysis on Dual-Phase Steel Using Band Slope of Electron Backscatter Diffraction Pattern

Published online by Cambridge University Press:  06 August 2013

Jun-Yun Kang ,
Seong-Jun Park  and
Man-Been Moon
Jun-Yun Kang*
Affiliation:
Ferrous Alloy Department, Korea Institute of Materials Science, 797 Changwon-daero, Changwon, Gyeongsangnam-do 641-831, Republic of Korea
Seong-Jun Park
Affiliation:
Automotive Steel R&D Team, Hyundai HYSCO Dangjin Works, 313 Donggok, Dangjin, Chungcheongnam-do 343-831, Republic of Korea
Man-Been Moon
Affiliation:
Automotive Steel R&D Team, Hyundai HYSCO Dangjin Works, 313 Donggok, Dangjin, Chungcheongnam-do 343-831, Republic of Korea
*
*Corresponding author. E-mail: [email protected]
Get access

Abstract

A quantitative and automated phase analysis of dual-phase (DP) steel using electron backscatter diffraction (EBSD) was attempted. A ferrite–martensite DP microstructure was produced by intercritical annealing and quenching. An EBSD map of the microstructure was obtained and post-processed for phase discrimination. Band slope (BS), which was a measure of pattern quality, exhibited much stronger phase contrast than another conventional one, band contrast. Owing to high sensitivity to lattice defect and little orientation dependence, BS provided handiness in finding a threshold for phase discrimination. Its grain average gave a superior result on the discrimination and volume fraction measurement of the constituent phases in the DP steel.

Keywords

phase analysiselectron backscatter diffractionpattern qualityband slopedual-phase steelmartensite
Type
Research Article
Information
Microscopy and Microanalysis , Volume 19 , Supplement S5: IUMAS , August 2013 , pp. 13 - 16
Copyright
Copyright © Microscopy Society of America 2013 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Han, H.N., Oh, C.S., Kim, G. & Kwon, O. (2009). Design method for TRIP-aided multiphase steel based on a microstructure-based modeling for transformation-induced plasticity and mechanically induced martensitic transformation. Mater Sci Eng A 499, 462–468.Google Scholar
Han, S.H., Ahn, Y.S., Chin, K.G. & Kim, I.B. (2008). The effect of Mo and Cr addition on the deep drawability of dual phase steel sheets. J Kor Ins Met Mater 46, 713–724.Google Scholar
Han, S.-H., Choi, S.-H., Choi, J.-K., Seong, H.-G. & Kim, I.-B. (2010). Effect of hot-rolling processing on texture and r-value of annealed dual-phase steels. Mater Sci Eng A 527, 1686–1694.10.1016/j.msea.2009.11.016Google Scholar
Kang, J.-Y., Kim, D.H., Baik, S.-I., Ahn, T.-H., Kim, Y.-W., Han, H.N., Oh, K.H., Lee, H.-C. & Han, S.H. (2011). Phase analysis of steels by grain-averaged EBSD functions. ISIJ Int 51, 130–136.Google Scholar
Llewellyn, D.T. & Hills, D.J. (1996). Dual phase steels. Ironmaking Steelmaking 23, 471–478.Google Scholar
Maitland, T. & Sitzman, S. (2007). Electron backscatter diffraction (EBSD) technique and materials characterization examples. In Scanning Microscopy for Nanotechnology: Techniques and Applications, Zhou, W. & Wang, Z.L. (Eds.), pp. 41–75. New York: Springer.Google Scholar
Matsuoka, T. & Yamamori, K. (1975). Metallurgical aspects in cold rolled high strength steel sheets. Metall Trans A 6, 1613–1622.Google Scholar
Nakaoka, K. (1982). Aging characteristics and formability of dual phase steel sheet. Tetsu-to-Hagané 68, 1159–1168.Google Scholar
Nakaoka, K. (1984). Microstructure design of dual-phase steel with proper quality balance. Skand J Metall 13, 289–297.Google Scholar
Nowell, M.M., Wright, S.I. & Carpenter, J.O. (2008). A practical investigation into identifying and differentiating phases in steel using electron backscatter diffraction. In Materials Processing and Texture, Rollett, A.D. (Ed.), pp. 285–292. Hoboken, NJ: John Wiley & Sons, Inc.Google Scholar
Randle, V. & Engler, O. (2000). Introduction to Texture Analysis. Amsterdam: Gordon and Breach Science Publishers.Google Scholar
Ryde, L. (2006). Application of EBSD to analysis of microstructures in commercial steels. Mater Sci Technol 22, 1297–1306.10.1179/174328406X130948Google Scholar
Schwartz, A.J., Kumar, M. & Adams, B. (2000). Electron Backscatter Diffraction in Materials Science. New York: Kluwer Academic/Plenum Publishers.10.1007/978-1-4757-3205-4Google Scholar
Wilson, A.W., Madison, J.D. & Spanos, G. (2001). Determining phase volume fraction in steels by electron backscattered diffraction. Scr Mater 45, 1335–1340.Google Scholar
WorldAutoSteel (2009). Advanced High Strength Steel (AHSS) Application Guidelines, Version 4.1. Brussels, Belgium: WorldAutoSteel.Google Scholar
Wright, S.I. & Nowell, M.M. (2006). EBSD image quality mapping. Microsc Microanal 12, 72–84.Google Scholar
Wu, J., Wray, P.J., Garcia, C.I., Hua, M. & DeArdo, A.J. (2005). Image quality analysis: A new method of characterizing microstructures. ISIJ Int 45, 254–262.Google Scholar