Influence of hydrogen on the tarnishing film-induced brittle cracking of brass

Published online by Cambridge University Press:  31 January 2011

Cheng Zhang ,
Yan Jing Su ,
Li jie Qiao  and
Wu yang Chu
Cheng Zhang
Affiliation:
Environment Fracture Lab of Education Ministry, Department of Materials Physics, University of Science and Technology Beijing, Beijing 100083, People’s Republic of China
Yan Jing Su*
Affiliation:
Environment Fracture Lab of Education Ministry, Department of Materials Physics, University of Science and Technology Beijing, Beijing 100083, People’s Republic of China
Li jie Qiao
Affiliation:
Environment Fracture Lab of Education Ministry, Department of Materials Physics, University of Science and Technology Beijing, Beijing 100083, People’s Republic of China
Wu yang Chu
Affiliation:
Environment Fracture Lab of Education Ministry, Department of Materials Physics, University of Science and Technology Beijing, Beijing 100083, People’s Republic of China
*
a) Address all correspondence to this author. e-mail:
Get access

Abstract

The effects of hydrogen-charging on tarnishing film-induced brittle cracking of brass were studied. The tarnishing film was generated on brass samples with various hydrogen concentrations in Mattsson’s solution, then removed from the solution, dried, and subjected to a slow loading rate (loading speed = 0.5 mm/min) in air. The results indicated that hydrogen caused the film-induced brittle cracking to be more difficult to occur and a considerably high concentration of hydrogen could inhibit completely the film-induced brittle cracking. Elastic modulus test results showed that elastic modulus of the brass substrate decreased and elastic modulus of the tarnishing film increased with increasing the hydrogen concentration. Hydrogen inhibiting the film-induced cracking can be ascribed to the fact that hydrogen changed the elastic modulus of substrate and film.

Keywords

FilmFractureH
Type
Articles
Information
Journal of Materials Research , Volume 24 , Issue 11 , November 2009 , pp. 3432 - 3438
Copyright
Copyright © Materials Research Society 2009

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Newman, R.C., Shahrabi, T., and Sieradzki, K.: Film-induced cleavage of alpha-brass. Scr. Metall. 23, 71 (1989).Google Scholar
2.Kelly, R.G., Frost, A.J., Shahrabi, J., and Newman, R.C.: Brittle fracture of an Au/Ag alloy induced by a surface film. Metall. Trans. A 22, 531 (1991).CrossRefGoogle Scholar
3.Chen, J.S., Salmeron, M., and Devine, T.M.: Intergranular vs transgranular stress-corrosion cracking of Cu 30-Au. Scr. Metall. Mater. 26, 739 (1992).CrossRefGoogle Scholar
4.Devasenapathi, A., Prasad, R.C., and Raja, V.S.: Change in fracture mode and selective dissolution of austenitic stainless steels. Scr. Metall. Mater. 33, 233 (1995).Google Scholar
5.Saito, M., Smith, G.S., and Newman, R.C.: Testing the filminduced cleavage model of stress-corrosion cracking. Corros. Sci. 35, 411 (1993).CrossRefGoogle Scholar
6.Cassagne, T.B., Flanagan, W.F., and Lichter, B.D.: On the failure mechanism of chemically embrittled Cu3Au single crystals. Metall. Trans. A 17, 703 (1986).CrossRefGoogle Scholar
7.Zhang, C., Su, Y.J., Qiao, L.J., and Chu, W.Y.: Tarnishing filminduced brittle cracking of brass. J. Mater. Res. 24, 2409 (2009).CrossRefGoogle Scholar
8.McLellan, R.B. and Xu, Z.R.: Hydrogen-induced vacancies in the iron lattice. Scr. Mater. 36, 1201 (1997).CrossRefGoogle Scholar
9.Delafosse, D. and Magnin, T.: Hydrogen induced plasticity in stress-corrosion cracking of engineering systems. Eng. Fract. Mech. 68, 693 (2001).CrossRefGoogle Scholar
10.Gao, K.W., Chu, W.Y., Li, H.L., Liu, Y.P., and Qiao, L.J.: Correspondence between hydrogen enhancing dezincification layerinduced stress and susceptibility to SCC of brass. Mater. Sci. Eng., A 371, 51 (2004).CrossRefGoogle Scholar
11.Oliver, W.C. and Pharr, G.M.: An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564 (1992).Google Scholar
12.Liu, M.Y., Shi, B., Guo, J.X., Cai, X., and Song, H.W.: Lattice constant dependence of elastic modulus for ultrafine grained mild steel. Scr. Metall. 49, 167 (2003).Google Scholar
13.Sieradzki, K. and Newman, R.C.: Stress-corrosion cracking. J. Phys. Chem. Solids 48, 1101 (1987).CrossRefGoogle Scholar
14.Sieradzki, K. and Newman, R.C.: Brittle behavior of ductile metals during stress-corrosion cracking. Philos. Mag. A 51, 95 (1985).CrossRefGoogle Scholar
15.Gavriljuk, V.G., Bugaev, V.N., Petrov, Yu.N., Tarasenko, A.V., and Yanchitski, B.Z.: Hydrogen-induced equilibrium vacancies in fcc iron-base alloys. Scr. Mater. 34, 903 (1996).CrossRefGoogle Scholar
16.Sakaki, K., Kawase, T., Hirato, M., Mizuno, M., Araki, H., Shiraia, Y., and Nagumob, M.: The effect of hydrogen on vacancy generation in iron by plastic deformation. Scr. Mater. 55, 1031 (2006).CrossRefGoogle Scholar
17.Zhang, T.Y., Chu, W.Y., and Hsiao, C.M.: Mechanism of hydrogen induced softening. Scr. Metall. 20, 225 (1986).CrossRefGoogle Scholar
18.Wang, Y.B., Chu, W.Y., and Hsiao, C.M.: Hydrogen induced dislocation multiplication in a Fe-3Si single crystal. Scr. Metall. 19, 1161 (1985).CrossRefGoogle Scholar