Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: Bilayer structures

Published online by Cambridge University Press:  03 March 2011

Sanjit Bhowmick ,
Yu Zhang  and
Brian R. Lawn
Sanjit Bhowmick
Affiliation:
Materials Science and Engineering Laboratory, National Institute of Standards and Technology, Gaithersburg, Maryland 20899-8500
Yu Zhang
Affiliation:
New York University College of Dentistry, New York, New York 10010
Brian R. Lawn*
Affiliation:
Materials Science and Engineering Laboratory, National Institute of Standards and Technology, Gaithersburg, Maryland 20899-8500
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

A preceding study of the competition between fracture modes in monolithic brittle materials in cyclic loading with curved indenters in liquid environments is here extended to brittle layers on compliant substrates. The fracture modes include outer and inner cone cracks and radial cracks that initiate from the near-contact zone and penetrate downward. Outer cone cracks are driven by stresses from superposed Hertzian and plate flexure fields; inner cone cracks also grow within these fields but are augmented by mechanical driving forces from hydraulic pumping into the crack fissures. Radial cracks are augmented by mechanical driving forces from developing quasiplasticity zones beneath the indenter. Basically, the crack-growth rates are governed by a crack velocity relation. However, the hydraulic and quasiplastic mechanical forces can cumulate in intensity with each cycle, strongly enhancing fatigue. Plate flexure generates compressive stresses at the top surface of the brittle layer, somewhat inhibiting the initiation, and tensile stresses at the lower surface, strongly enhancing the far-field propagation. The tensile stresses promote instability in the crack propagation, resulting in through-thickness penetration (failure). Experiments on a model bilayer system consisting of glass plates bonded to thick polycarbonate bases are presented as an illustrative case study. In situ observations of the crack evolution from initial growth to failure reveal that each fracture mode can dominate under certain test conditions, depending on plate thickness, maximum load, and sphere radius. Implications concerning the failure of practical layer systems, notably dental crowns, are discussed.

Type
Articles
Information
Journal of Materials Research , Volume 20 , Issue 10 , October 2005 , pp. 2792 - 2800
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Zhang, Y., Bhowmick, S. and Lawn, B.R.: Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: Monoliths. J. Mater. Res. 20, 2021 (2005).CrossRefGoogle Scholar
2Lawn, B.R., Deng, Y., Miranda, P., Pajares, A., Chai, H. and Kim, D.K.: Overview: Damage in brittle layer structures from concentrated loads. J. Mater. Res. 17, 3019 (2002).CrossRefGoogle Scholar
3Zhang, Y., Kwang, J-K. and Lawn, B.R.: Deep penetrating conical cracks in brittle layers from hydraulic cyclic contact. J. Biomed. Mater. Res. B 73B, 186 (2005).CrossRefGoogle Scholar
4Kim, D.K., Jung, Y-G., Peterson, I.M. and Lawn, B.R.: Cyclic fatigue of intrinsically brittle ceramics in contact with spheres. Acta Mater. 47, 4711 (1999).CrossRefGoogle Scholar
5Chai, H., Lawn, B.R. and Wuttiphan, S.: Fracture modes in brittle coatings with large interlayer modulus mismatch. J. Mater. Res. 14, 3805 (1999).CrossRefGoogle Scholar
6Rhee, Y-W., Kim, H-W., Deng, Y. and Lawn, B.R.: Contact-induced damage in ceramic coatings on compliant substrates: Fracture mechanics and design. J. Am. Ceram. Soc. 84, 1066 (2001).CrossRefGoogle Scholar
7Deng, Y., Lawn, B.R. and Lloyd, I.K.: Characterization of damage modes in dental ceramic bilayer structures. J. Biomed. Mater. Res. 63B, 137 (2002).CrossRefGoogle Scholar
8Lawn, B.R., Deng, Y. and Thompson, V.P.: Use of contact testing in the characterization and design of all-ceramic crown-like layer structures: A review. J. Prosthet. Dent. 86, 495 (2001).CrossRefGoogle Scholar
9Lawn, B.R., Lee, S.K., Peterson, I.M. and Wuttiphan, S.: Model of strength degradation from Hertzian contact damage in tough ceramics. J. Am. Ceram. Soc. 81, 1509 (1998).CrossRefGoogle Scholar
10Chai, H. and Lawn, B.R. Hydraulically pumped cone fractures in brittle solids. (in press).Google Scholar
11Lawn, B.R., Lee, K.S., Chai, H., Pajares, A., Kim, D.K., Wuttiphan, S., Peterson, I.M. and Hu, X.: Damage-resistant brittle coatings. Adv. Eng. Mater. 2, 745 (2000).3.0.CO;2-E>CrossRefGoogle Scholar
12Qasim, T., Bush, M.B., Hu, X. and Lawn, B.R.: Contact damage in brittle coating layers: Influence of surface curvature. J. Biomed. Mater. Res. 73B, 179 (2005).CrossRefGoogle Scholar
13Deng, Y., Miranda, P., Pajares, A. and Lawn, B.R.: Fracture of ceramic/ceramic/polymer trilayers for biomechanical applications. J. Biomed. Mater. Res. 67A, 828 (2003).CrossRefGoogle Scholar
14Timoshenko, S. and Woinowsky-Krieger, S.: Theory of Plates and Shells (McGraw-Hill, New York, 1959).Google Scholar
15Wiederhorn, S.M. and Bolz, L.H.: Stress corrosion and static fatigue of glass. J. Am. Ceram. Soc. 53, 543 (1970).CrossRefGoogle Scholar
16Wiederhorn, S.M.: A chemical interpretation of static fatigue. J. Am. Ceram. Soc. 55, 81 (1972).CrossRefGoogle Scholar