Observation of the Distinct X-Ray Intensity Reaks Due to a Stacking Fault Structure in Plastically Deformed a-Brass

Published online by Cambridge University Press:  06 March 2019

W. D. Sylwestrowicz
W. D. Sylwestrowicz*
Affiliation:
Bell Telephone Laboratories, Incorporated Murray Hill, New Jersey
Get access

Abstract

Distinct X-ray intensity peaks corresponding to a stacking fault structure have been observed in the plastically deformed ctbrass (30% Zn). TITO sets of intensity peaks were present simultaneously: one set corresponding to the f.c.c. structure of annealed a-brass, the second set was displaced with respect to the first set in accordance with the Paterson pattern for a stacking fault structure. With Increasing plastic deformation the height and width of the stacking fault peaks increased, while the height of f.c.c. peaks decreased. Finally, only the intensity peaks of the stacking fault structure were observed. The positions of the stacking fault peaks and the original structure peaks remained constant and were independent of the amount of plastic deformation.

Type
Research Article
Information
Advances in X-Ray Analysis , Volume 12: Seventeenth Annual Conference on Applications of X-ray Analysis, August 21-23, 1968 , 1968 , pp. 249 - 256
Copyright
Copyright © International Centre for Diffraction Data 1968

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Barrett, C. S. and Trantz, O. R., “Low Temperature Transformations in Lithium and Lithium-Magnesium Alloys” (Reply by Barrett to discussion p. 605). Trans. AIME 175:579–605 (1948).Google Scholar
2. Paterson, M. S., “X-Ray Diffraction by Face-Centered Cubic Crystals with Deformation Faults,” J. Appl. Phys. 23:805–811 (1952).Google Scholar
3. Warren, B. E., “X-Ray Studies of Deformed Metals,” Progress in Metal Physics, 8:147–201 (1959).Google Scholar
4. Guinier, A., “X-Ray Diffraction in Crystals, Imperfect Crystals, and Amorphous Bodies,” pp. 241–249, pub. W. H. Freeman and Co. (1963).Google Scholar
5. Warren, B. E. and Warekois, P. E., “Stacking Faults in Cold Worked Alpha-Brass,” Acta Met. 3 :473–479 (1955).Google Scholar